Polymer Property : Tensile Strength, Ultimate = 2760 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	19.0 MPa	2760 psi	ASTM D638-95
Multibase Multi-Pro® 3012 Natural 30% Calcium Carbonate Polypropylene This material is an impact modified Calcium Carbonate filled polypropylene that has good impact resistance, good basic UV resistance, and is easily colored. UV additives can be used for extended UV..
Tensile Strength, Ultimate	19.0 MPa	2760 psi	ASTM D638
NCMT NanoPAC™ HS401 High Performance Polypropylene Nanocomposite Applications: Electrical AppliancesInformation provided by Nano Composite Materials Technology Limited
Tensile Strength, Ultimate	19.0 MPa	2760 psi	ASTM D638
NCMT NanoPAC™ S216 High Performance Polypropylene Nanocomposite Characteristics: High stiffness Supplementary of ABS Good impact resistant Less shrinkage Good thermal conductivity Applications: Toys Industry AutomobileInformation provided by Nano Composite Mater..
Tensile Strength, Ultimate	19.0 MPa	2760 psi	ASTM D638
Owens Corning Glass Fiber Reinforced Polyurethane, Milled Fibers (RRIM), 13 wt.% glass Polyurethane is normally used for its structural properties when molded. It is highly resistant to most organic solvents. It is not recommended for use with strong acids and alkalis, steam, fuels, a..
Tensile Strength, Ultimate	19.0 MPa	2760 psi
Pyrotek F-24 Dense Machinable Board F-24 is a high temperature resin material that is reinforced with fiberglass. Abrasion resistant, it is used for hot glass handling applications.ApplicationsDonut rollers for glass Guide rails Wear..
Tensile Strength, Ultimate	19.0 MPa	2760 psi	ASTM D638
Huntsman PE1651 EVA Film Extrusion (discontinued **) 6.5% Vinyl Acetate EVA copolymer and FDA compliantFeatures: Yields film with outstanding low temperature strength, excellent clarity, and good heat seal.Applications: Film extrusion: ice bags, liqui..
Tensile Strength, Ultimate	19.0 MPa	2760 psi	ASTM D638
LyondellBasell Astryn NXO-21001 Polypropylene Copolymer Key Features: high melt flow, medium modulus polypropylene copolymer, high flow, excellent processability, excellent colorabilityApplications: wire harnesses, housings, thin walled partsDescription:..
Tensile Strength, Ultimate	19.0 MPa	2760 psi	at max load; ISO 527
A. Schulman FORMION™ FI 396 Ionomer DescriptionFormion® FI 3936is a 3% glass fiber reinforced, injection molding grade Ionomer, which has been formulated for scratch resistance, and impact. Formion F1 396U is UV stabilized to exceed ..
Tensile Strength, Ultimate	19.0 MPa	2760 psi	at max load; ISO 527
A. Schulman FORMION™ FI 396 Ionomer DescriptionFormion® FI 3936is a 3% glass fiber reinforced, injection molding grade Ionomer, which has been formulated for scratch resistance, and impact. Formion F1 396U is UV stabilized to exceed ..
Tensile Strength, Ultimate	19.0 MPa	2760 psi	Type IV, crosshead speed 2 in/min; ASTM D638
DuPont Elvax® 460 Ethylene-Vinyl Acetate Copolymer Resin Elvax resins offer a unique combination of processing and performance characteristics. They provide outstanding toughness and resilience and maintain flexibility over a broad temperature range with..
Tensile Strength, Ultimate	19.0 MPa	2760 psi	at max load; ISO 527
A. Schulman FORMION™ FI 396 Ionomer DescriptionFormion® FI 3936is a 3% glass fiber reinforced, injection molding grade Ionomer, which has been formulated for scratch resistance, and impact. Formion F1 396U is UV stabilized to exceed ..
Tensile Strength, Ultimate	19.0 MPa	2760 psi	Type IV, crosshead speed 2 in/min; ASTM D638
DuPont Elvax® 560 Ethylene-Vinyl Acetate Copolymer Resin Elvax resins offer a unique combination of processing and performance characteristics. They provide outstanding toughness and resilience and maintain flexibility over a broad temperature range with..
Tensile Strength, Ultimate	19.0 MPa	2760 psi	at max load; ISO 527
A. Schulman FORMION™ FI 396 Ionomer DescriptionFormion® FI 3936is a 3% glass fiber reinforced, injection molding grade Ionomer, which has been formulated for scratch resistance, and impact. Formion F1 396U is UV stabilized to exceed ..
Tensile Strength, Ultimate	19.0 MPa	2760 psi	ASTM D638/D412
Covestro Baydur® 730 IBS Polyurethane Structural Foam RIM, Density 40 pcf, MDI-based 2-Component Liquid System 0.25 in. thickness. IBS = Interactive Blowing System RIM = Reaction Injection MoldingInformation provided by Bayer Corporation, Polyurethanes DivisionAs of 1 September 2015, Bayer MaterialScience ..
Tensile Strength, Ultimate	19.0 MPa	2760 psi	ASTM D638/D412
Covestro Bayflex® 110-50 Polyurethane Elastomeric RIM, 15% Milled Glass Reinforced, MDI-based 2-Component Liquid System 0.125 in. thickness. RIM = Reaction Injection MoldingInformation provided by Bayer Corporation, Polyurethanes DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and o..
Tensile Strength, Ultimate	19.0 MPa	2760 psi	ASTM D638
Devcon Underwater Repair Putty (UW) Epoxy Emergency Repair ProductsComments: High-performance technology for repairing, patching and rebuilding equipment in habitually wet environments, even under water. Eliminates the need for substrate t..
Tensile Strength, Ultimate	19.0 MPa	2760 psi	Die C (35 min / 145°C); ASTM D412
Dow SE SLR-4601 Solution polymerized Styrene Butadiene Rubber (S-SBR) SE SLR-4601 is manufactured by anionic solution polymerization using lithium initiator. It is a product with medium styrene and high vinyl content. The product is partially Sn-coupled and chemical..
Tensile Strength, Ultimate	19.0 MPa	2760 psi	Die C (35 min / 145°C); ASTM D412
Dow SE SLR-4610 Solution polymerized Styrene Butadiene Rubber (S-SBR) SE SLR-4610 is manufactured by anionic solution polymerization using lithium initiator and is extended with 37.5 parts of aromatic oil in relation to solid rubber. It is a product with medium styre..
Tensile Strength, Ultimate	19.0 MPa	2760 psi	ASTM D412
Colorite Polymers Weatherflex™ CS1525WX (NTL01B) Wire and Cable Vinyl Compound Description: Colorite specialty wire and cable compounds feature low smoke properties, excellent flame retardance, low temperature flexibility, and resistance to abrasion and chemicals. All are avai..
Tensile Strength, Ultimate	19.0 MPa	2760 psi	ASTM D638
A. Schulman ComAlloy Comtuf® 102 Polypropylene, Mineral Reinforced, Impact Modified Data provided by the manufacturer, ComAlloy International Company.20% Mineral Reinforced. Superior toughness and impact resistance characterize Comtuf® materialsThe ComAlloy product line has been i..
Tensile Strength, Ultimate	19.0 MPa	2760 psi	ASTM D638
A. Schulman ComAlloy Hiloy® 164 Polypropylene, Mineral Reinforced Data provided by the manufacturer, ComAlloy International Company.40% Mineral Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
Tensile Strength, Ultimate	19.0 MPa	2760 psi	ASTM D638
Solvay Specialty Polymers Algoflon® 25CAR PTFE; Petroleum Coke and Graphite (discontinued **) Data provided by the manufacturer.25 wt.% Petroleum Coke and Graphite. Suspension polymer powder grade recommended for compression molding. Pure PTFE possesses high inertness, excellent dielectric p..
Tensile Strength, Ultimate	19.0 MPa	2760 psi	ASTM D638
Huntsman PE1201 EVA Film Extrusion (discontinued **) 2% Vinyl Acetate EVA copolymer and FDA compliantFeatures: Good optical, medium impact strength, and good processability.Applications: Film extrusion: heavy duty packaging.FDA Notes: Conforms to FDA ..
Tensile Strength, Ultimate	19.0 MPa	2760 psi	ASTM D638
Huntsman PE1451 EVA Film Extrusion (discontinued **) 4.5% Vinyl Acetate EVA copolymer and FDA compliantFeatures: Excellent balance of optical and strength, toughness and flexibility at low temperatures, and good heat seal characteristic.Applications: ..
Tensile Strength, Ultimate	19.0 MPa	2760 psi	ASTM D412-80
DuPont Performance Polymers Hypalon® 40 Chlorosulfonated Polyethylene Rubber, Mineral Filled Compound (discon Mineral filled compound with 100 parts Hypalon; 80 parts hard clay; 4 parts magnesia; 30 parts aromatic process oil; 3 parts pentaerythritol; and 2 parts Tetrone® A rubber accelerator (from DuPont ..
Tensile Strength, Ultimate	19.0 MPa	2760 psi
3M Dyneon™ Aflas® FA-100H PTFE Fluoroelastomer (discontinued **) Data provided by the manufacturer, Dyneon LLC.Non-incorporated cure polymer, 57%F in polymer with 19% Medium Thermal Carbon Black (N990), 4% Triallyl Isocyanurate (TAIC), 1% Percadox™ 14, 1% Sodium..
Tensile Strength, Ultimate	19.0 MPa	2760 psi	ASTM D638
LyondellBasell Astryn 7523C Polypropylene Copolymer Key Features: conventional melt flow, medium modulus polypropylene copolymer, excellent impact and stiffness balance, excellent chemical resistance, versatile, good processabilityApplications: autom..
Tensile Strength, Ultimate	19.0 - 281 MPa	2760 - 40800 psi	Average value: 106 MPa Grade Count:13
Overview of materials for Polyimide, Thermoset Film This property data is a summary of similar materials in the MatWeb database for the category "Polyimide, Thermoset Film". Each property range of values reported is minimum and maximum values of appr..