Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Yield Strength | 55.0 MPa | 7980 psi | ASTM D790 |
Nylene® 402 Nylon 6 Injection molding grade. Dry as molded. Nylene 402 is a high monomer resin which offers outstanding toughness and flexibility. Nylene 402 exhibits excellent flow properties at temperature and press.. |
|||
Flexural Yield Strength | 55.0 MPa | 7980 psi | ASTM D790 |
Nylene® Naxel™ AX190 PPE (Polyphenylene Ether) General Purpose Grade. Properties for dry as molded samples.ALM, Nylene Canada, and Custom Resins are all operting companies of Polymeric Resources Corporation. |
|||
Flexural Yield Strength | 55.0 MPa | 7980 psi | ASTM D790 |
Nylene® NX5703 Nylon 6, Impact Extrusion Grade Dry as molded. Extrusion grade. Nylene NX5703 is a high residual monomer, medium viscosity resin designed for extrusion applications requiring good flexibility and high strength. NX5703 is ideally.. |
|||
Flexural Yield Strength | 55.0 MPa | 7980 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
Ovation Polymers Nima™ NH PA66UT Nylon 66 Polyamide 66 - Ultra Tough, Flame Retarded Non-Hal grade with excellent retention of mechanical properties. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humi.. |
|||
Flexural Yield Strength | 55.0 MPa | 7980 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
Ovation Polymers OPTRENE 10GF Polypropylene, 10% Glass Reinforced Properties of chemically coupled glass reinforced (10 %) polypropylene with high strength and HDT. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. All.. |
|||
Flexural Yield Strength | 55.0 - 216 MPa | 7980 - 31300 psi | Average value: 127 MPa Grade Count:121 |
Overview of materials for Polybutylene Terephthalate (PBT), Flame Retardant This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Flame Retardant". Each property range of values reported is minimum an.. |
|||
Flexural Yield Strength | 55.0 MPa | 7980 psi | ASTM D790 |
Ineos Nova 5800 High Impact Polystyrene
(discontinued **) Balance of toughness and rigidity, Good gloss, USP Class VIApplications: Thermoformed and molded packaging, Drink cups and lids, Structural foam, Custom sheetProperties were determined on injection .. |
|||
Flexural Yield Strength | 55.0 MPa @Temperature 23.0 °C |
7980 psi @Temperature 73.4 °F |
50 mm/min; ASTM D790 |
Solvay Specialty Polymers Solef® 460/461 Polyvinylidene Fluoride (PVDF)
(Unverified Data**) Solef® 460/461 PVDF homopolymer has high melt viscosity and is typically processed by extrusion.Information provided by Solvay Specialty Polymers. |
|||
Flexural Yield Strength | 55.0 - 240 MPa | 7980 - 34800 psi | Average value: 92.9 MPa Grade Count:32 |
Overview of materials for Phenolic, Novolac, Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Phenolic, Novolac, Mineral Filled". Each property range of values reported is minimum and maximum values.. |
|||
Flexural Yield Strength | 55.0 - 163 MPa | 7980 - 23600 psi | Average value: 76.3 MPa Grade Count:8 |
Overview of materials for Phenolic, Novolac, Mineral/Graphite Filled This property data is a summary of similar materials in the MatWeb database for the category "Phenolic, Novolac, Mineral/Graphite Filled". Each property range of values reported is minimum and maxim.. |
|||
Flexural Yield Strength | 55.0 - 135 MPa | 7980 - 19600 psi | Average value: 90.0 MPa Grade Count:25 |
Overview of materials for Phenolic, Novolac, Cellulose Filled This property data is a summary of similar materials in the MatWeb database for the category "Phenolic, Novolac, Cellulose Filled". Each property range of values reported is minimum and maximum valu.. |
|||
Flexural Yield Strength | 55.0 - 290 MPa | 7980 - 42100 psi | Average value: 170 MPa Grade Count:75 |
Overview of materials for Nylon 6, Glass Filled, Impact Grade This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Glass Filled, Impact Grade". Each property range of values reported is minimum and maximum valu.. |
|||
Flexural Yield Strength | 55.0 MPa | 7980 psi | ASTM Data |
BASF Capron® 8230G HS 6% Glass-Filled Nylon 6 (Conditioned)
(discontinued **) Capron 8230G HS is a heat stabilized, 6% nylon 6 molding compound offering improved stiffness and dimensional stability in thin sections. It exhibits a combination of strength, stiffness and perfor.. |
|||
Flexural Yield Strength | 55.0 MPa | 7980 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Noryl V180HF PPE+HIPS (Europe-Africa-Middle East) NORYL V180HF is an unfilled, flame retardant material. It has been fully optimized w.r.t. flow and is halogen free according to VDE/DIN 472 part 815.This data was supplied by SABIC-IP for the Europe.. |
|||
Flexural Yield Strength | 55.0 MPa | 7980 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Noryl V190 PPE+HIPS (Europe-Africa-Middle East) NORYL V190 is an unfilled flame retardant material with a Vicat B/120 of 90°C according ISO 306. NORYL V190 is V1 at 2.0 mm according UL94 and halogen free according VDE/DIN 472 part 815.This dat.. |
|||
Flexural Yield Strength | 55.0 MPa | 7980 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics ULTEM STM1600 PEI Copolymer Siltem 1600 is a flexible copolymer designed for wire and cable applications. It offers a halogen free (according VDE 0472) flame retardant solution that also offers low smoke emission and toxicity... |
|||
Flexural Yield Strength | 55.0 MPa | 7980 psi | 50 mm/min; ASTM D790 |
Solvay Specialty Polymers Solef® 460/461 Polyvinylidene Fluoride (PVDF) Solef® 460/461 PVDF homopolymer has high melt viscosity and is typically processed by extrusion.Features: High Viscosity; HomopolymerAdditional Properties: Crystallization Heat - ASTM D3418 46.0 .. |
|||
Flexural Yield Strength | 55.0 MPa | 7980 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
SABIC Innovative Plastics Noryl N190A PPE+PS (Asia Pacific) Low heat, flame retardant PPO/HIPS alloy. Internal flammability results only.Not a UL recognised material.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
Flexural Yield Strength | 55.0 MPa | 7980 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
SABIC Innovative Plastics NORYL PN235 PPE+PS Plating grade, primarily automotive applications. |
|||
Flexural Yield Strength | 55.0 MPa | 7980 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
SABIC Innovative Plastics NORYL PN235 PPE+PS (Asia Pacific) Plating grade, primarily automotive applications. |
|||
Flexural Yield Strength | 55.0 MPa | 7980 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics NORYL PX1180 PPE+HIPS (Europe-Africa-Middle East) Noryl* PX1180 PolyPhenylene Oxide (PPO*) + Polystyrene (PS) resin is an unfilled , injection moldable grade, with improved impact performances, an ISO 306 Vicat B/120 temperature of 120 deg C and a.. |
|||
Flexural Yield Strength | 55.0 MPa | 7980 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics NORYL PX1181 PPE+HIPS (Europe-Africa-Middle East) Noryl* PX1181 PolyPhenylene Oxide (PPO*) + Polystyrene (PS) resin is an unfilled , injection moldable grade, with improved impact performances, an ISO 306 Vicat B/120 temperature of 120 deg C and a .. |
|||
Flexural Yield Strength | 55.0 MPa | 7980 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
SABIC Innovative Plastics Noryl PX1701 PPE+PS This data was supplied by SABIC-IP for the Americas region. |
|||
Flexural Yield Strength | 55.0 MPa | 7980 psi | ASTM D790 |
Chem Polymer Chemlon 267 Nylon 6, Impact Modified An extrusion grade copolymer nylon 6, providing good melt strength, impact, elongation, and flexibility. This grade provides excellent properties in most convoluted tubing or wire coating applicati.. |
|||
Flexural Yield Strength | 55.0 MPa | 7980 psi | ASTM D790 |
Ineos Nova 5120 High Impact Polystyrene
(discontinued **) Good balance of toughness and rigidity, Superior gloss, USP Class VIApplications: Refrigeration, Appliances, High gloss applicationsProperties were determined on injection molded specimens at 23°C .. |
|||
Flexural Yield Strength | 55.0 MPa | 7980 psi | ASTM D790 |
Ineos Nova 5124 High Impact Polystyrene
(discontinued **) Good balance of toughness and rigidity, Superior gloss, USP Class VIApplications: Refrigeration, Appliances, High gloss applicationsProperties were determined on injection molded specimens at 23°C .. |
|||
Flexural Yield Strength | 55.0 - 179 MPa | 7980 - 26000 psi | Average value: 128 MPa Grade Count:37 |
Overview of materials for Acetal Copolymer + Glass/PTFE This property data is a summary of similar materials in the MatWeb database for the category "Acetal Copolymer + Glass/PTFE". Each property range of values reported is minimum and maximum values of .. |
|||
Flexural Yield Strength | 55.0 - 150 MPa | 7980 - 21800 psi | Average value: 92.6 MPa Grade Count:22 |
Overview of materials for Polyimide, Graphite Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyimide, Graphite Filled". Each property range of values reported is minimum and maximum values of app.. |
|||
Flexural Yield Strength | 55.0 - 300 MPa | 7980 - 43500 psi | Average value: 167 MPa Grade Count:233 |
Overview of materials for Nylon 6, 20% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 20% Glass Fiber Filled".Specific grades with glass content between 15% and 24% are included. Ea.. |