- Polyvinylidinefluoride (PVDF), Molded/Extruded
- Solvay Specialty Polymers Solef® 460/461 Polyvinylidene Fluoride (PVDF)
Solvay Specialty Polymers Solef® 460/461 Polyvinylidene Fluoride (PVDF)
| Category | Polymer , Thermoplastic , Fluoropolymer , PVDF , Polyvinylidinefluoride (PVDF), Molded/Extruded |
| Manufacturer | Solvay Specialty Polymers |
| Trade Name | Solef® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Specialty Polymers Solef® 460/461 Polyvinylidene Fluoride (PVDF).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Solef® 460/461 PVDF homopolymer has high melt viscosity and is typically processed by extrusion.Features: High Viscosity; HomopolymerAdditional Properties: Crystallization Heat - ASTM D3418 46.0 J/g; Heat of Fusion - ASTM D3418 46.0 J/gInformation provided by Solvay Specialty Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.76 g/cc | 0.0636 lb/in³ | ASTM D792 |
| Water Absorption | 0.020 % @Time 86400 sec |
0.020 % @Time 24.0 hour |
ISO 62 |
| Viscosity | 2.60e+6 cP @Shear Rate 100 1/s, Temperature 232 °C |
2.60e+6 cP @Shear Rate 100 1/s, Temperature 450 °F |
Melt Viscosity; ASTM D3835 |
| Melt Flow | 10 g/10 min @Load 21.6 kg, Temperature 230 °C |
10 g/10 min @Load 47.6 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 75 | 75 | ASTM D2240 |
| Tensile Strength at Break | 41.0 MPa | 5950 psi | 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 48.0 MPa | 6960 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 100 % | 100 % | 50 mm/min; ASTM D638 |
| Elongation at Yield | 10 % | 10 % | 50 mm/min; ASTM D638 |
| Tensile Modulus | 1.31 GPa | 190 ksi | 50 mm/min; ASTM D638 |
| Flexural Yield Strength | 55.0 MPa | 7980 psi | 50 mm/min; ASTM D790 |
| Flexural Modulus | 1.52 GPa | 220 ksi | 50 mm/min; ASTM D790 |
| Izod Impact, Notched | 1.10 J/cm | 2.06 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 11.0 J/cm | 20.6 ft-lb/in | ASTM D256 |
| Coefficient of Friction, Dynamic | 0.20 | 0.20 | vs. Itself; ASTM D1894 |
| Coefficient of Friction, Static | 0.30 | 0.30 | vs. Itself; ASTM D1894 |
| Taber Abrasion, mg/1000 Cycles | 8.0 | 8.0 | CS-17 Wheel, 1000 g; ASTM D1044 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 130 µm/m-°C | 72.2 µin/in-°F | |
| Specific Heat Capacity | 1.34 J/g-°C | 0.320 BTU/lb-°F | ASTM C351 |
| Thermal Conductivity | 0.200 W/m-K | 1.39 BTU-in/hr-ft²-°F | ASTM C177 |
| Melting Point | 160 °C | 320 °F | DSC |
| Crystallization Temperature | 132 °C | 270 °F | Peak; ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 127 °C | 261 °F | Annealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 88.0 °C | 190 °F | Annealed; ASTM D648 |
| Glass Transition Temp, Tg | -39.0 °C | -38.2 °F | ASTM E1356 |
| Flammability, UL94 | V-0 | V-0 | |
| Oxygen Index | 44 % | 44 % | ASTM D2863 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Refractive Index | 1.42 | 1.42 | ASTM D542 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Dielectric Constant | 6.0 @Frequency 1.00e+6 Hz |
6.0 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Dielectric Strength | 10.0 kV/mm @Thickness 3.18 mm |
254 kV/in @Thickness 0.125 in |
ASTM D149 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| Latin America | ||
| North America | ||
| Processing Technique | Extrusion |