Ineos Nova 5120 High Impact Polystyrene  (discontinued **)

Category Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Impact Modified
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Ineos Nova 5120 High Impact Polystyrene  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Good balance of toughness and rigidity, Superior gloss, USP Class VIApplications: Refrigeration, Appliances, High gloss applicationsProperties were determined on injection molded specimens at 23°C and 50% R.H. unless otherwise specified.Information provided by NOVA Chemicals.INEOS NOVA began October 1 2007 as an expansion of the 50:50 joint venture between NOVA Chemicals and INEOS to include North American assets. 
Physical Properties Metric English Comments
Density 1.04 g/cc
0.0376 lb/in³
ASTM D792
Linear Mold Shrinkage 0.0040 - 0.0070 cm/cm
0.0040 - 0.0070 in/in
ASTM D955
Melt Flow 4.3 g/10 min
4.3 g/10 min
Condition G
Mechanical Properties Metric English Comments
Hardness, Rockwell M 42
42
Tensile Strength, Yield 22.0 MPa
3190 psi
ASTM D638
Elongation at Break 50 %
50 %
ASTM D638
Modulus of Elasticity 2.138 GPa
310.1 ksi
ASTM D638
Flexural Yield Strength 55.0 MPa
7980 psi
ASTM D790
Flexural Modulus 2.207 GPa
320.1 ksi
ASTM D790
Izod Impact, Notched 1.44 J/cm

@Diameter 3.17 mm
2.70 ft-lb/in

@Diameter 0.125 in
bar, 0.010" notch radius; ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 85.0 °C
185 °F
ASTM D648
Vicat Softening Point 98.0 °C
208 °F
ASTM D1525
Flammability, UL94 HB
HB
Electrical Properties Metric English Comments
Dielectric Constant 2.51

@Frequency 1e+6 Hz
2.51

@Frequency 1e+6 Hz
Dielectric Strength 15.7 kV/mm

@Thickness 3.17 mm
400 kV/in

@Thickness 0.125 in
Processing Properties Metric English Comments
Melt Temperature 190 - 274 °C
374 - 525 °F
Mold Temperature 38.0 - 82.0 °C
100 - 180 °F