Polymer Property : Tensile Strength, Yield = 100000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	>= 689 MPa	>= 100000 psi
Niagara LaSalle StressProof® Cold Finished Steel Bar StressProof® is made by a patented process which consists of drawing the bar through a special die under heavy draft, then stress relieving it in a precisely controlled furnace. StressProof® offer..
Tensile Strength, Yield	689 MPa	100000 psi
Pacific Sintered Materials FN-253-S(HT) 4600 Powdered Metal High performance material with high strength and wear resistance after heat treatment.Equivalent MPIF Specification: FL-4605-100HTAll information provided by Pacific Sintered Metals.
Tensile Strength, Yield	689 MPa @Strain 0.200 %	100000 psi @Strain 0.200 %
Materion moldMAXÂ® XL Spinodally Hardened Copper-Nickel-Tin Alloy moldMAX XLÂ® is a unique spinodally hardened copper-nickel-tin alloy that combines high strength and high thermal conductivity. Available in large plate thickness up to 12â€ and in rounds up t..
Tensile Strength, Yield	>= 690 MPa	>= 100000 psi
Materion Nibryl Beryllium Nickel Alloy (Nibryl)-360 Rod and Bar; H925 (H925) Temper; All Sizes (UNS N03360) Tabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materials Inc. changed its name to Materion Corporation in March 2011.
Tensile Strength, Yield	>= 690 MPa	>= 100000 psi	1/2 t
Industeel SUPERELSOÂ® 690CR Quenched and Tempered High Strength Steel for Leg Components of Jack-up Rigs SuperelsoÂ® 690 CR (SE 690 CR) is a 690MPa (100ksi) yield strength quenched and tempered steel adapted for jack-up rig legs of offshore drilling platforms. SuperelsoÂ® 690 CR is manufactured via..
Tensile Strength, Yield	>= 690 MPa @Strain 0.200 %	>= 100000 psi @Strain 0.200 %
Industeel SUPRALSIMÂ® 690 HLE Steel for Welded and Weight-Saving Structures Description: SUPRALSIMÂ® 690 is general steel plate for structure enables to make weight savings thanks to a minimum yield strength of 690 N/mmÂ². Thanks to its exceptional purity rate (very low..
Tensile Strength, Yield	690 MPa	100000 psi
Latrobe NitralloyÂ® 135 Modified VAC-ARC, Up to 1.5 in Premium Nitriding Steel NITRALLOY 135 MODIFIED VAC-ARC steel is a low alloy nitriding grade with moderate hardenability. It has been designed to provide a high case hardness and to maintain its core strength during the nit..
Tensile Strength, Yield	>= 690 MPa	>= 100000 psi
MetalTek INÂ® 713 UNS N07713 Centri-Vac Nickel Cobalt Based Alloy Information provided by MetalTek
Tensile Strength, Yield	690 MPa @Strain 0.200 %	100000 psi @Strain 0.200 %
Haynes HastelloyÂ® B-3Â® alloy, 10% cold work The attributes of Corrosion-Resistant HASTELLOYÂ® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and ..
Tensile Strength, Yield	689 MPa	100000 psi	Hard
Special Metals MONELÂ® 404 Copper-Nickel Alloy Data provided by California Fine Wire and the manufacturer, Special Metals.
Tensile Strength, Yield	690 MPa @Strain 0.200 %, Temperature 550 Â°C	100000 psi @Strain 0.200 %, Temperature 1020 Â°F	Precipitation Hardened prior to test
Special Metals NIMONICÂ® Alloy 90 A precipitation-hardenable nickel-chromium-cobalt alloy having high stress-rupture strength and creep resistance at temperatures to about 1700Â°F (920Â°C). The alloy also has good resistance to..
Tensile Strength, Yield	>= 690 MPa	>= 100000 psi
SSAB Tunnplat DomexÂ® 690XP Extra High-strength Cold-forming Steel Extra High-strength Cold-forming Steel, HSLACharacteristics: DomexÂ® is the brand name of hot rolled products from SSAB Tunnplat. DomexÂ® cold-forming steels are modern structural steels. Gene..
Tensile Strength, Yield	690 MPa	100000 psi	ISO 527
Styrolution AbsolanÂ® 2300 Sparkle SAN Absolac 2300 Sparkle is a good flow gradeInformation provided by Styrolution
Tensile Strength, Yield	>= 689 MPa @Strain 0.200 %	>= 100000 psi @Strain 0.200 %
Universal Wire Works 901 (AMS 5660) Nickel Alloy Filler Metal Alloy 901 is a corrosion and heat resistant nickel-base alloy designed for gas tungsten arc and gas metal arc welding. Alloy 901 is used primarily for parts, such as turbine rotors, shafts and bucke..
Tensile Strength, Yield	>= 690 MPa	>= 100000 psi
TIMET TIMETAL® 3-2.5 Titanium Alloy (Ti-3Al-2.5V; ASTM Grade 9) Aged Cold Workable Medium Strength Alloy. UTS, TYS, and elongation data below are specific to aged material; other specific condition entries are also available in MatWeb.Features: Cold formable and we..
Tensile Strength, Yield	689 - 1240 MPa	100000 - 180000 psi	depending on condition of material after heat treatment
Universal Wire Works 17-4 (AMS 5825) Filler Metal Universal 630 (17Cr-4Ni) is a martensitic precipitation - age hardening stainless steel alloy. Alloy 630 can be welded with all welding processes without preheat; however, to obtain weld metal prope..
Tensile Strength, Yield	>= 689 MPa	>= 100000 psi	0.2% Offset
Eagle Brass 430 Ferritic Stainless Steel, Full Hardened Type 430 is one of the most widely used of the "non-hardenable" ferritic stainless steels. It combines good corrosion resistance and heat and oxidation with good mechanical properties. Typical pro..
Tensile Strength, Yield	689 - 793 MPa	100000 - 115000 psi	0.2% offset
Eagle Brass 519 Phosphor Bronzes 6%, Extra Spring Alloy C519 has 6% nominal tin producing higher mechanical strengths with a slight decrease in electrical conductivity when compared to C510 phosphor bronze. Often functionally interchangeable with C..
Tensile Strength, Yield	689 - 779 MPa	100000 - 113000 psi	0.2% offset
Eagle Brass 521 Phosphor Bronzes 8% C, Spring Alloy C521 is a high tin alloy of the phosphor bronze family. The additional tin relative to the more commonly used C510 results in higher mechanical properties with a modest reduction in electrical..
Tensile Strength, Yield	>= 689 MPa	>= 100000 psi	0.2% offset
Eagle Brass 70265 XP175, Hard Information provided by Eagle Brass Company
Tensile Strength, Yield	690 MPa	100000 psi
Elgiloy® Co-Cr-Ni Alloy, Strip, 10% Cold Reduction The strength, elongation, and hardness values are specific to this cold reduction treatment; other values below are typical of Elgiloy®.General Elgiloy® information: High strength, ductility, fati..
Tensile Strength, Yield	690 MPa	100000 psi
Elgiloy® Co-Cr-Ni Alloy, Wire, 10% Cold Reduction The strength, shear modulus, and hardness values are specific to this cold reduction treatment; other values below are typical of Elgiloy®.General Elgiloy® information: High strength, ductility, f..
Tensile Strength, Yield	689 MPa @Strain 0.200 %	100000 psi @Strain 0.200 %	Solution treated ~ 34 HRC
Bohler-Uddeholm UDDEHOLM CORRAX® Precipitation Hardening Stainless Mold Steel A precipitation hardening stainless steel which offers excellent high corrosion resistance, excellent dimensional stability during hardening and good wear resistance. It can be used at its as-suppli..
Tensile Strength, Yield	689 MPa	100000 psi	Hard
California Fine Wire Alloy 52 Nickel Iron Alloy All values may vary dependent on specific design and usageCapabilities: WireRibbonSquareInsulatedPlatedInformation provided by California Fine Wire.
Tensile Strength, Yield	689 MPa	100000 psi	Hard
California Fine Wire Dumet Nickel Iron Core Copper Clad Alloy All values may vary dependent on specific design and usage99.9% copper cladding over iron-nickel coreCapabilities: WireRibbonSquareInsulatedPlatedInformation provided by California Fine Wire.
Tensile Strength, Yield	>= 690 MPa @Diameter <=100 mm	>= 100000 psi @Diameter <=3.94 in	Re. , un-machined
Assab Steels 709M Machinery Steel ASSAB 709M is an alloyed machinery steel with high strength in small and medium sizes. As standard ASSAB 705M is supplied tough hardened requiring no further heat treatment. It can be oil hardened t..
Tensile Strength, Yield	690 MPa	100000 psi	R<sub>e</sub>. 700°C tempering temperature. Quenching in oil ø 120. Testpiece hardened by oil quenching from 850°C.
Assab Steels 705M Machinery Steel ASSAB 705M is an alloyed machinery steel with good hardenability also in heavier sizes. As standard ASSAB 705M is supplied tough hardened with no further heat treatment required. It can be oil harde..
Tensile Strength, Yield	690 MPa	100000 psi
ATI Allegheny Ludlum Stainless Steel Chromium-Nickel Type 304, 20% Cold Rolled (UNS S30400) This alloy is one of the most familiar and most frequently used alloy in the stainless steel family. It may be best used in applications where the following properties are important: resistance to ..
Tensile Strength, Yield	690 MPa	100000 psi
ATI Allegheny Ludlum Stainless Steel Chromium-Nickel Type 304L, 20% Cold Rolled (UNS S30403) This alloy is one of the most familiar and most frequently used alloy in the stainless steel family. It may be best used in applications where the following properties are important: resistance to ..
Tensile Strength, Yield	690 MPa @Treatment Temp. 760 °C, Time 2.88e+7 sec	100000 psi @Treatment Temp. 1400 °F, Time 8000 hour	0.2%. Room temp test after thermal exposure
Haynes 282® Nickel Alloy Plate, Solution Annealed and Age-Hardened, after long term high temperature exposure Excellent High Temperature Strength HAYNES® 282® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and land-b..