- SABIC Innovative Plastics Cycolac® MG37EPX ABS (Europe-Africa-Middle East)
SABIC Innovative Plastics Cycolac® MG37EPX ABS (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Cycolac® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Cycolac® MG37EPX ABS (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
ABS plating grade optimized for a broad processing window for both painted and plated applications.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0060 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 20.6 g/10 min @Load 10.0 kg, Temperature 220 °C |
20.6 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 39.0 MPa | 5660 psi | 5 mm/min; ISO 527 |
| Tensile Strength, Yield | 48.0 MPa | 6960 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 15.8 % | 15.8 % | 5 mm/min; ISO 527 |
| Elongation at Yield | 2.0 % | 2.0 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 2.76 GPa | 400 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 73.0 MPa | 10600 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.47 GPa | 358 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 23.0 kJ/m² | 10.9 ft-lb/in² | 80*10*4; ISO 180/1A |
| 6.00 kJ/m² @Temperature -40.0 °C |
2.86 ft-lb/in² @Temperature -40.0 °F |
80*10*4; ISO 180/1A | |
| 8.00 kJ/m² @Temperature -30.0 °C |
3.81 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 60.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
33.3 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 60.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
33.3 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 81.0 °C | 178 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| Vicat Softening Point | 98.0 °C | 208 °F | Rate B/50; ISO 306 |
Users viewing this material also viewed the following:
- Plastcom PLASTALEN® TPU N 85 LTS TPU
- Polimeri Europa SINKRAL B260 ABS, Heat Stabilized (discontinued **)
- Teknor Apex Telcar® TL-2596C Thermoplastic Elastomer
- Ter Hell Plastic Terez® PA 6 7500 GF 30 Polyamide 6, 30% Glass Fiber Reinforced
- The NanoSteel® Company SHS 9700 PTAW Steel Alloy, Atomized Powder
- Clinton Aluminum Alumold 1-500 Forged
- Eurotec® Tecotek® PC43 GR003 TD70 PC, unfilled, flame retardant - halogen (RoHS compliant), impact modified, light grey
- ACC QLE 1100 QSI Quantum Silicones 43 Durometer Clear, Addition Cure, 1-part Elastomer for Coating
- 3M Dyneon™ FEP 6303Z Fluorinated Ethylene Propylene Fluorothermoplastic Granules
Copyright © lookpolymers.com All Rights Reserved