SABIC Innovative Plastics GELOY XTPM405 ASA+PC
| Category | Polymer , Thermoplastic , ASA Polymer , Polycarbonate (PC) , Polycarbonate/ASA Alloy, Unreinforced |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | GELOY |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics GELOY XTPM405 ASA+PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High flow PC/ASA with improved impact at room and low temperatures. Improved release. Excellent weatherability for outdoor unpainted or clearcoated applications. Injection Moldable with large color gamut.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in³ | ISO 1183 |
| Viscosity | 120000 cP | 120000 cP | Melt Viscosity, 260°C, 1500 sec-1; ISO 11443 |
| Melt Flow | 14 g/10 min @Load 10.0 kg, Temperature 220 °C |
14 g/10 min @Load 22.0 lb, Temperature 428 °F |
ISO 1133 |
| 30 g/10 min @Load 5.00 kg, Temperature 260 °C |
30 g/10 min @Load 11.0 lb, Temperature 500 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 39.0 MPa | 5660 psi | 50 mm/min; ISO 527 |
| Tensile Strength, Yield | 47.0 MPa | 6820 psi | 50 mm/min; ISO 527 |
| 49.0 MPa | 7110 psi | ASTM D638 | |
| Elongation at Break | 55 % | 55 % | 50 mm/min; ISO 527 |
| 90 % | 90 % | ASTM D638 | |
| Elongation at Yield | 3.0 % | 3.0 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 2.40 GPa | 348 ksi | 5 mm/min; ASTM D638 |
| 2.40 GPa | 348 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 75.0 MPa | 10900 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.20 GPa | 319 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched | 14.14 J/cm | 26.49 ft-lb/in | ASTM D256 |
| 1.30 J/cm @Temperature -20.0 °C |
2.44 ft-lb/in @Temperature -4.00 °F |
ASTM D256 | |
| 1.36 J/cm @Temperature 0.000 °C |
2.55 ft-lb/in @Temperature 32.0 °F |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 65.0 kJ/m² | 30.9 ft-lb/in² | 80*10*4; ISO 180/1A |
| 10.0 kJ/m² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 6.50 J/cm² | 30.9 ft-lb/in² | ISO 179/2C |
| Dart Drop, Total Energy | 11.0 J @Temperature -30.0 °C |
8.11 ft-lb @Temperature -22.0 °F |
ASTM D3763 |
| 40.0 J @Temperature 23.0 °C |
29.5 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 88.0 °C | 190 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| Vicat Softening Point | 103 °C | 217 °F | Rate B/50; ISO 306 |