SABIC Innovative Plastics Cycolac® DL100LG ABS (Europe-Africa-Middle East)

Category	Polymer , Thermoplastic , ABS Polymer
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	Cycolac®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics Cycolac® DL100LG ABS (Europe-Africa-Middle East).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Cycolac DL100LG is a low gloss, high heat, high impact ABS/PC blend with low emission

Physical Properties	Metric	English	Comments
Density	1.08 g/cc	0.0390 lb/in³	ISO 1183
Linear Mold Shrinkage, Flow	0.0050 - 0.0070 cm/cm	0.0050 - 0.0070 in/in	on Tensile Bar; SABIC Method
Melt Flow	10 g/10 min @Load 10.0 kg, Temperature 220 °C	10 g/10 min @Load 22.0 lb, Temperature 428 °F	ASTM D1238
Melt Index of Compound	10 g/10 min @Load 10.0 kg, Temperature 220 °C	10 g/10 min @Load 22.0 lb, Temperature 428 °F	MVR [cm^3/10 min]; ISO 1133
	12 g/10 min @Load 5.00 kg, Temperature 260 °C	12 g/10 min @Load 11.0 lb, Temperature 500 °F	MVR [cm^3/10 min]; ISO 1133

Mechanical Properties	Metric	English	Comments
Hardness, H358/30	80.0 MPa	11600 psi	ISO 2039-1
Tensile Strength at Break	36.0 MPa	5220 psi	5 mm/min; ISO 527
	38.0 MPa	5510 psi	Type I, 50 mm/min; ASTM D638
	39.0 MPa	5660 psi	50 mm/min; ISO 527
	40.0 MPa	5800 psi	Type I, 5 mm/min; ASTM D638
Tensile Strength, Yield	47.0 MPa	6820 psi	5 mm/min; ISO 527
	47.0 MPa	6820 psi	Type I, 5 mm/min; ASTM D638
	51.0 MPa	7400 psi	Type I, 50 mm/min; ASTM D638
	51.0 MPa	7400 psi	50 mm/min; ISO 527
Elongation at Break	12 %	12 %	Type I, 50 mm/min; ASTM D638
	12 %	12 %	50 mm/min; ISO 527
	50 %	50 %	5 mm/min; ISO 527
	85 %	85 %	Type I, 5 mm/min; ASTM D638
Elongation at Yield	4.0 %	4.0 %	50 mm/min; ISO 527
	4.0 %	4.0 %	5 mm/min; ISO 527
	4.0 %	4.0 %	Type I, 5 mm/min; ASTM D638
	4.0 %	4.0 %	Type I, 50 mm/min; ASTM D638
Tensile Modulus	2.20 GPa	319 ksi	1 mm/min; ISO 527
	2.24 GPa	325 ksi	50 mm/min; ASTM D638
Flexural Yield Strength	74.0 MPa	10700 psi	2 mm/min; ISO 178
Flexural Modulus	2.20 GPa	319 ksi	2 mm/min; ISO 178
Izod Impact, Notched	3.80 J/cm	7.12 ft-lb/in	ASTM D256
	1.15 J/cm @Temperature -30.0 °C	2.15 ft-lb/in @Temperature -22.0 °F	ASTM D256
Izod Impact, Notched (ISO)	28.0 kJ/m²	13.3 ft-lb/in²	80104; ISO 180/1A
	45.0 kJ/m²	21.4 ft-lb/in²	80103; ISO 180/1A
	11.0 kJ/m² @Temperature -30.0 °C	5.23 ft-lb/in² @Temperature -22.0 °F	80104; ISO 180/1A
	19.0 kJ/m² @Temperature -30.0 °C	9.04 ft-lb/in² @Temperature -22.0 °F	80103; ISO 180/1A
Charpy Impact, Notched	2.20 J/cm²	10.5 ft-lb/in²	Edgew 80103 sp=62mm; ISO 179/1eA
	1.10 J/cm² @Temperature -30.0 °C	5.23 ft-lb/in² @Temperature -22.0 °F	Edgew 80103 sp=62mm; ISO 179/1eA

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	82.0 µm/m-°C @Temperature -40.0 - 40.0 °C	45.6 µin/in-°F @Temperature -40.0 - 104 °F	ISO 11359-2
CTE, linear, Transverse to Flow	83.0 µm/m-°C @Temperature -40.0 - 40.0 °C	46.1 µin/in-°F @Temperature -40.0 - 104 °F	ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi)	103 °C	217 °F	Flatw 80104 sp=64mm; ISO 75/Bf
Deflection Temperature at 1.8 MPa (264 psi)	84.0 °C	183 °F	Flatw 80104 sp=64mm; ISO 75/Af
	85.0 °C @Thickness 6.40 mm	185 °F @Thickness 0.252 in	unannealed; ASTM D648
Vicat Softening Point	105 °C	221 °F	Rate B/50; ISO 306
	107 °C	225 °F	Rate B/120; ISO 306
	118 °C	244 °F	Rate A/50; ISO 306
	120 °C	248 °F	Rate A/120; ISO 306