Polymer Property : Tensile Strength at Break = 50.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	48.0 - 50.0 MPa	6960 - 7250 psi	ASTM D638
Proto3000 Accura® 50 Plastic Stereolithography (SLA) Prototyping Polymer Simulate the properties and appearance of molded ABS with this durable, accurate and versatile plastic.Features:Durable and stiffOutstanding accuracy w/out shrinkage related distortionChoice of grey..
Tensile Strength at Break	45.0 - 50.0 MPa	6530 - 7250 psi	ASTM D638-03
Proto3000 Objet Digital Materials™ DM_7230 Transparent Prototyping Polymer Primary material: FullCure720Secondary material: TangoBlackDigital Materials are made up of two Objet materials. The two materials are combined in specific concentrations and structures, to provide ..
Tensile Strength at Break	35.0 - 50.0 MPa @Thickness 2.00 mm, Temperature 23.0 °C	5080 - 7250 psi @Thickness 0.0787 in, Temperature 73.4 °F	Type IV, 50 mm/min; ASTM D638
Solvay Specialty Polymers Solef® 1015 Polyvinylidene Fluoride (PVDF) (Unverified Data**) Solef® 1015 PVDF homopolymer has very high viscosity, suitable for membrane manufacturing. It is available exclusively as powder.Information provided by Solvay Specialty Polymers.
Tensile Strength at Break	30.0 - 50.0 MPa	4350 - 7250 psi	ISO 527
Manifattura Cattaneo PVDF Manifattura Cattaneo products are available in semi-finished forms such as bars, profiles, sheets and plates.Information provided by Manifattura Cattaneo s.p.a.
Tensile Strength at Break	30.0 - 50.0 MPa	4350 - 7250 psi
GrafTech GRAFCELLÂ® FFP-200 SERIES Flow Field Plate Graphite Manufactured from expanded natural graphite, GRAFCELLÂ® Flow Field Plate (FFP) components retain a continuous graphitic phase. This phase continuity, combined with a low contact resistance, provid..
Tensile Strength at Break	30.0 - 50.0 MPa @Thickness 2.00 mm	4350 - 7250 psi @Thickness 0.0787 in	50 mm/min; ASTM D638
Solvay Specialty Polymers SolefÂ® 1006 Polyvinylidene Fluoride (PVDF) SolefÂ® 1006 PVDF is a very low viscosity homopolymer resin mainly used in injection molding or in multifilament extrusion.Features: Homopolymer; Low ViscosityUses: General PurposeAdditional Prope..
Tensile Strength at Break	35.0 - 50.0 MPa @Thickness 2.00 mm	5080 - 7250 psi @Thickness 0.0787 in	50 mm/min; ASTM D638
Solvay Specialty Polymers SolefÂ® 1015 Polyvinylidene Fluoride (PVDF) SolefÂ® 1015 PVDF homopolymer has very high viscosity, suitable for membrane manufacturing. It is available exclusively as powder.Features: Homopolymer; Ultra High ViscosityUses: MembranesAddition..
Tensile Strength at Break	30.0 - 50.0 MPa @Thickness 2.00 mm	4350 - 7250 psi @Thickness 0.0787 in	50 mm/min; ASTM D638
Solvay Specialty Polymers SolefÂ® 6010 Polyvinylidene Fluoride (PVDF) SolefÂ® 6010 PVDF homopolymer has medium viscosity and is typically processed by extrusion.Features: Homopolymer; Medium ViscosityAdditional Properties: Crystallization Heat - ASTM D3417 54.0 to 6..
Tensile Strength at Break	30.0 - 50.0 MPa @Thickness 2.00 mm	4350 - 7250 psi @Thickness 0.0787 in	50 mm/min; ASTM D638
Solvay Specialty Polymers SolefÂ® 6012 Polyvinylidene Fluoride (PVDF) SolefÂ® 6012 PVDF homopolymer is a high-viscosity PVDF resin and is typically processed by extrusion or compression molding.Features: High Viscosity; HomopolymerAdditional Properties: Crystallizat..
Tensile Strength at Break	25.0 - 50.0 MPa @Thickness 2.00 mm	3630 - 7250 psi @Thickness 0.0787 in	50 mm/min; ASTM D638
Solvay Specialty Polymers SolefÂ® 6020 Polyvinylidene Fluoride (PVDF) SolefÂ® 6020 PVDF homopolymer has very high viscosity for membranes and lithium batteries. It is available exclusively as powder.Features: Homopolymer; Ultra High ViscosityUses: Batteries; Membran..
Tensile Strength at Break	30.0 - 50.0 MPa @Thickness 2.00 mm	4350 - 7250 psi @Thickness 0.0787 in	50 mm/min; ASTM D638
Solvay Specialty Polymers SolefÂ® 9007 Polyvinylidene Fluoride (PVDF) SolefÂ® 9007 PVDF homopolymer has low viscosity and is used in film extrusion and injection molding.Features: Homopolymer; Low ViscosityAdditional Properties: Crystallization Heat - ASTM D3418 53...
Tensile Strength at Break	40.0 - 50.0 MPa	5800 - 7250 psi	ISO 527
Vyncolit 2923 W Novolac Phenolic Mineral filled phenolic molding compound with excellent heat resistance and dimensional stability.Information provided by Vyncolit, a Sumitomo Bak Group
Tensile Strength at Break	30.0 - 50.0 MPa	4350 - 7250 psi	ISO 527
Vyncolit 3640 CG Novolac Phenolic Graphite filled phenolic molding compound with excellent dimensional stability. Self-lubricating and has a low coefficient of friction. Not suitable for electrical applications.USES: Gas meter par..
Tensile Strength at Break	40.0 - 50.0 MPa	5800 - 7250 psi	ISO 527
Vyncolit 2530 W Novolac Phenolic Mineral and organic filled phenolic molding compound with excellent thermal properties.USES: Lamp sockets, special lamp holders, pan handles and knobs.Information provided by Vyncolit, a Sumitomo Ba..
Tensile Strength at Break	40.0 - 50.0 MPa	5800 - 7250 psi	ISO 527
Vyncolit 2723 W Novolac Phenolic Mineral and organic filled phenolic molding compound with excellent mechanical, thermal and dielectric properties. I2/FO classified under NF F 16-101 (Fire & Smoke classification).USES: Circuit bre..
Tensile Strength at Break	40.0 - 50.0 MPa	5800 - 7250 psi	ISO 527
Vyncolit 2920 W Novolac Phenolic Mineral and organic filled molding compound with good dimensional stability and heat resistance.USES: Carburettor and intake manifold thermal insulator.Information provided by Vyncolit, a Sumitomo B..
Tensile Strength at Break	40.0 - 50.0 MPa	5800 - 7250 psi	ASTM D638
Daikin NEOFLON EP-521 ETFE Pellets Due to its excellent melt flow properties, NEOFLON ETFE can be processed in the same was as other thermoplastic resins. NEOFLON ETFE is also highly suited to such secondary processes as welding, fl..
Tensile Strength at Break	40.0 - 50.0 MPa	5800 - 7250 psi	ASTM D638
Daikin NEOFLON EP-610 ETFE Pellets Due to its excellent melt flow properties, NEOFLON ETFE can be processed in the same was as other thermoplastic resins. NEOFLON ETFE is also highly suited to such secondary processes as welding, fl..
Tensile Strength at Break	40.0 - 50.0 MPa	5800 - 7250 psi	ASTM D638
Daikin NEOFLON EP-610AS ETFE Pellets Due to its excellent melt flow properties, NEOFLON ETFE can be processed in the same was as other thermoplastic resins. NEOFLON ETFE is also highly suited to such secondary processes as welding, fl..
Tensile Strength at Break	40.0 - 50.0 MPa	5800 - 7250 psi	ASTM D638
Daikin NEOFLON RP-4020 EFEP Pellets NEOFLON EFEP is an ETFE based fluoropolymer combining the excellent physical properties derived from ETFE together with a low processing temperature that is more compatible with conventional thermop..
Tensile Strength at Break	40.0 - 50.0 MPa	5800 - 7250 psi	ASTM D638
Daikin NEOFLON RP-5000 EFEP Pellets NEOFLON EFEP is an ETFE based fluoropolymer combining the excellent physical properties derived from ETFE together with a low processing temperature that is more compatible with conventional thermop..
Tensile Strength at Break	40.0 - 50.0 MPa	5800 - 7250 psi	ASTM D638
Daikin NEOFLON RP-5000AS EFEP Pellets NEOFLON EFEP is an ETFE based fluoropolymer combining the excellent physical properties derived from ETFE together with a low processing temperature that is more compatible with conventional thermop..
Tensile Strength at Break	40.0 - 50.0 MPa	5800 - 7250 psi	ASTM D638
Daikin NEOFLON EP-620 ETFE Pellets Due to its excellent melt flow properties, NEOFLON ETFE can be processed in the same was as other thermoplastic resins. NEOFLON ETFE is also highly suited to such secondary processes as welding, fl..
Tensile Strength at Break	40.0 - 50.0 MPa	5800 - 7250 psi	5 mm/min.; IS 867-1963
Amity Thermosets ATI 172 Phenolic Molding Organic and inorganic Filler, Injection Molded Characteristics:Heat resistant ( asbestos free )Good electric insulationLow shrinkageLow water absorptionMedium mechanical strengthNot suitable for high mechanical tensionColor-blackVery soft flow ..
Tensile Strength at Break	40.0 - 50.0 MPa	5800 - 7250 psi	5 mm/min.; IS 867-1963
Amity Thermosets ATS 131 Phenolic Molding Organic and graphite Filler, Compression Molded Characteristics:Self lubricating ( graphite modified )Good glide propertiesGood sealing propertiesMedium or low mechanical strengthUnsuitable for electrical applicationGlossy surfaceThermal conducti..
Tensile Strength at Break	40.0 - 50.0 MPa	5800 - 7250 psi	ASTM D638
Daikin NEOFLON EP-541 ETFE Pellets Due to its excellent melt flow properties, NEOFLON ETFE can be processed in the same was as other thermoplastic resins. NEOFLON ETFE is also highly suited to such secondary processes as welding, fl..
Tensile Strength at Break	25.0 - 50.0 MPa @Thickness 2.00 mm, Temperature 23.0 °C	3630 - 7250 psi @Thickness 0.0787 in, Temperature 73.4 °F	Type IV, 50 mm/min; ASTM D638
Solvay Specialty Polymers Solef® 6020 Polyvinylidene Fluoride (PVDF) (Unverified Data**) Solef® 6020 PVDF homopolymer has very high viscosity for membranes and lithium batteries. It is available exclusively as powder.Information provided by Solvay Specialty Polymers.
Tensile Strength at Break	30.0 - 50.0 MPa @Thickness 2.00 mm, Temperature 23.0 °C	4350 - 7250 psi @Thickness 0.0787 in, Temperature 73.4 °F	Type IV, 50 mm/min; ASTM D638
Solvay Specialty Polymers Solef® 9007 Polyvinylidene Fluoride (PVDF) (Unverified Data**) Solef® 9007 PVDF homopolymer has low viscosity and is used in film extrusion and injection molding.Information provided by Solvay Specialty Polymers.
Tensile Strength at Break	30.0 - 50.0 MPa @Thickness 2.00 mm, Temperature 23.0 °C	4350 - 7250 psi @Thickness 0.0787 in, Temperature 73.4 °F	Type IV, 50 mm/min; ASTM D638
Solvay Specialty Polymers Solef® 9009 Polyvinylidene Fluoride (PVDF) (discontinued **) Solef® 9009 PVDF homopolymer has low/medium viscosity and is used in film extrusion and injection molding.Information provided by Solvay Specialty Polymers.
Tensile Strength at Break	30.0 - 50.0 MPa	4350 - 7250 psi	ISO 527
Vyncolit 3520 CG Novolac Phenolic Graphite filled phenolic molding compound with excellent dimensional stability. Self-lubricating and has a low coefficient of friction. Not suitable for electrical applications.USES: Gas meter par..