- Polyvinylidinefluoride (PVDF), Molded/Extruded
- Solvay Specialty Polymers Solef® 6020 Polyvinylidene Fluoride (PVDF) (Unverified Data**)
Solvay Specialty Polymers Solef® 6020 Polyvinylidene Fluoride (PVDF) (Unverified Data**)
| Category | Polymer , Thermoplastic , Fluoropolymer , PVDF , Polyvinylidinefluoride (PVDF), Molded/Extruded |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Specialty Polymers Solef® 6020 Polyvinylidene Fluoride (PVDF)
(Unverified Data**).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Solef® 6020 PVDF homopolymer has very high viscosity for membranes and lithium batteries. It is available exclusively as powder.Information provided by Solvay Specialty Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.75 - 1.80 g/cc | 1.75 - 1.80 g/cc | ASTM D792 |
| Water Absorption | <= 0.040 % @Temperature 23.0 °C, Time 86400 sec |
<= 0.040 % @Temperature 73.4 °F, Time 24.0 hour |
ASTM D570 |
| Melt Flow | <= 0.20 g/10 min @Load 21.6 kg, Temperature 230 °C |
<= 0.20 g/10 min @Load 47.6 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 25.0 - 50.0 MPa @Thickness 2.00 mm, Temperature 23.0 °C |
3630 - 7250 psi @Thickness 0.0787 in, Temperature 73.4 °F |
Type IV, 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 53.0 - 57.0 MPa @Thickness 2.00 mm, Temperature 23.0 °C |
7690 - 8270 psi @Thickness 0.0787 in, Temperature 73.4 °F |
Type IV, 50 mm/min; ASTM D638 |
| Elongation at Break | 15 - 50 % @Thickness 2.00 mm, Temperature 23.0 °C |
15 - 50 % @Thickness 0.0787 in, Temperature 73.4 °F |
Type IV, 50 mm/min; ASTM D638 |
| Elongation at Yield | 5.0 - 10 % @Thickness 2.00 mm, Temperature 23.0 °C |
5.0 - 10 % @Thickness 0.0787 in, Temperature 73.4 °F |
Type IV, 50 mm/min; ASTM D638 |
| Tensile Modulus | 1.60 - 1.70 GPa @Thickness 2.00 mm, Temperature 23.0 °C |
232 - 247 ksi @Thickness 0.0787 in, Temperature 73.4 °F |
Type IV, 1.0 mm/min; ASTM D638 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Heat of Fusion | 47.0 - 52.0 J/g | 20.2 - 22.4 BTU/lb | Crystallization Heat; ASTM D3417 |
| 57.0 - 66.0 J/g | 24.5 - 28.4 BTU/lb | ASTM D3417 | |
| Melting Point | 171 - 175 °C | 340 - 347 °F | ASTM D3418 |
| Crystallization Temperature | 133 - 138 °C | 271 - 280 °F | Peak, DSC; ASTM D3418 |
| Glass Transition Temp, Tg | -40.0 °C | -40.0 °F | ASTM D4065 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+14 ohm-cm | >= 1.00e+14 ohm-cm | ASTM D257 |
| Surface Resistance | >= 1.00e+14 ohm | >= 1.00e+14 ohm | ASTM D257 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| Features | Homopolymer | |
| Very high Viscosity | ||
| Forms | Powder | |
| Generic | PVDF | |
| Uses | Batteries | |
| Membranes |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycoloy® CY9650 PC+ABS
- SABIC Innovative Plastics Lexan® EX7631T PC
- SABIC Innovative Plastics LNP FARADEX MS002 PP (Asia Pacific)
- SABIC Innovative Plastics Lexan® FL410 PC
- ICO Polymers ICORENEâ„¢ 115-1649 LMDPE Rotational Molding Resin
- Mateck Zinc Sulphide, ZnS
- Michelman® Michem® Lube 135 Anionic paraffin/polyethylene wax emulsion
- MRC Polymers NAXALOYâ„¢ 793A7 PC + Polyester Blend
- Amity Thermosets ATG 112 Phenolic Molding Organic Filler, Compression Molded
- Solvay Specialty Polymers Veradel® A-301 Polyethersulfone (PESU) (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved