Polymer Property : Compressive Yield Strength = 16000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Compressive Yield Strength	110 - 138 MPa	16000 - 20000 psi	Average value: 120 MPa Grade Count:7
Overview of materials for Polycarbonate, 30% Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, 30% Glass Filled". Specific grades with glass content between 25% and 34% are included. E..
Compressive Yield Strength	110 - 380 MPa	16000 - 55100 psi	Average value: 237 MPa Grade Count:63
Overview of materials for Phenolic, Novolac, Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "Phenolic, Novolac, Glass Filled". Each property range of values reported is minimum and maximum values o..
Compressive Yield Strength	110 MPa	16000 psi	10% Deflection; ASTM D-695
Aardvark Polymers AARTELÂ® 820UV Acetal Copolymer Rotational Molding Resin Aartel 820UV is a natural acetal copolymer with added UV stabilizers.Aartel 820UV is a low viscosity resin with excellent flow characteristics.Aartel 820UV is available in natural white and may be p..
Compressive Yield Strength	110 MPa	16000 psi
Cytec Thornel® Graphite Cloth Laminate with Mil R-9299 Resin Data provided by the manufacturer, Amoco Performance Products, Inc.Carbon and graphite cloths, consisting entirely of flexible filaments, are produced by pyrolysis of rayon cloth at high temperature..
Compressive Yield Strength	110 MPa @Strain 10.0 %, Temperature 23.0 °C	16000 psi @Strain 10.0 %, Temperature 73.4 °F	EN ISO 604
Ensinger TECASINT™ 2032 Polyimide, Black, 40% Graphite (PI) TECASINT™ 2000 series of polyimide stock shapes provide a superior combination of high temperature and bearing and wear, properties that make it an ideal choice for the most demanding applications...
Compressive Yield Strength	110 MPa	16000 psi	ASTM D695
Adell AJ-13 Nylon 66, 15% Glass Reinforced; High Impact Data provided by Adell Plastics, Inc.
Compressive Yield Strength	110 MPa	16000 psi	ASTM D695
Adell AJ-33 Nylon 66, 15% Glass Reinforced; High Impact Data provided by Adell Plastics, Inc.
Compressive Yield Strength	110 MPa	16000 psi	ASTM D695
Techmer ES Plaslube® J-50/30/TF/15 Polycarbonate, 30% Glass Reinforced, PTFE Lubricated 30% Glass Reinforced, PTFE Lubricated
Compressive Yield Strength	110 MPa	16000 psi	Average value: 110 MPa Grade Count:3
Overview of materials for Polyethersulfone (PES), 10% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyethersulfone (PES), 10% Glass Fiber Filled". Specific grades with glass content between 5% and 14% a..
Compressive Yield Strength	110 - 124 MPa	16000 - 18000 psi	Average value: 114 MPa Grade Count:4
Overview of materials for Acrylic, Cast This property data is a summary of similar materials in the MatWeb database for the category "Acrylic, Cast". Each property range of values reported is minimum and maximum values of appropriate MatW..