Aardvark Polymers AARTEL® 820UV Acetal Copolymer Rotational Molding Resin
| Category | Polymer , Thermoplastic , Acetal (POM) |
| Manufacturer | Gehrig & Associates |
| Trade Name | AARTEL® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aardvark Polymers AARTEL® 820UV Acetal Copolymer Rotational Molding Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Aartel 820UV is a natural acetal copolymer with added UV stabilizers.Aartel 820UV is a low viscosity resin with excellent flow characteristics.Aartel 820UV is available in natural white and may be painted, printed, or plated.Aartel 820UV may be compounded and dry colored.Aartel 820UV offers exceptional resistance to aggressive chemicals and fuels.Aartel 820UV has a fuel permeation rate of 1.2 gr-mm/m2-day.Aartel 820UV is formulated for interior and exterior applications
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | |
| Water Absorption | 0.22 % | 0.22 % | |
| Moisture Absorption at Equilibrium | 0.80 % | 0.80 % | |
| Linear Mold Shrinkage | 0.021 cm/cm | 0.021 in/in | |
| Linear Mold Shrinkage, Transverse | 0.017 cm/cm | 0.017 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 80 | 80 | |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | |
| Elongation at Break | 40 % | 40 % | |
| Flexural Yield Strength | 89.0 MPa | 12900 psi | |
| Flexural Modulus | 2.60 GPa | 377 ksi | |
| Compressive Yield Strength | 110 MPa | 16000 psi | 10% Deflection; ASTM D-695 |
| Fatigue Strength | 21.0 MPa @# of Cycles 1.00e+7 |
3050 psi @# of Cycles 1.00e+7 |
ASTM D-671 |
| Shear Strength | 53.0 MPa | 7690 psi | |
| Izod Impact, Notched | 0.530 J/cm | 0.993 ft-lb/in | ASTM D-256 |
| 0.430 J/cm @Temperature -29.0 °C |
0.806 ft-lb/in @Temperature -20.2 °F |
ASTM D-256 | |
| Tensile Impact Strength | 128 kJ/m² | 60.9 ft-lb/in² |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 158 °C | 316 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | |
| Flammability, UL94 | HB | HB |