Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Compressive Yield Strength | 117 - 124 MPa | 17000 - 18000 psi | Average value: 122 MPa Grade Count:6 |
Overview of materials for Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled". Specific grades with glass content between 25.. |
|||
Compressive Yield Strength | 96.5 - 124 MPa | 14000 - 18000 psi | Average value: 114 MPa Grade Count:8 |
Overview of materials for Polycarbonate, 20% Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, 20% Glass Filled". Specific grades with glass content between 15% and 24% are included. E.. |
|||
Compressive Yield Strength | 110 - 124 MPa | 16000 - 18000 psi | Average value: 114 MPa Grade Count:4 |
Overview of materials for Acrylic, Cast This property data is a summary of similar materials in the MatWeb database for the category "Acrylic, Cast". Each property range of values reported is minimum and maximum values of appropriate MatW.. |
|||
Compressive Yield Strength | 117 - 124 MPa | 17000 - 18000 psi | Average value: 119 MPa Grade Count:3 |
Overview of materials for Acrylic, Optical Sheet This property data is a summary of similar materials in the MatWeb database for the category "Acrylic, Optical Sheet". Each property range of values reported is minimum and maximum values of appropr.. |
|||
Compressive Yield Strength | 53.8 - 124 MPa | 7800 - 18000 psi | Average value: 77.7 MPa Grade Count:3 |
Overview of materials for Polybutylene Terephthalate (PBT), Glass + Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Glass + Mineral Filled". Each property range of values reported is min.. |