Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Compressive Yield Strength | 117 - 124 MPa | 17000 - 18000 psi | Average value: 122 MPa Grade Count:6 |
Overview of materials for Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled". Specific grades with glass content between 25.. |
|||
Compressive Yield Strength | 117 - 269 MPa | 17000 - 39000 psi | Average value: 151 MPa Grade Count:8 |
Overview of materials for Phenolic, Novolac, Mineral/Graphite Filled This property data is a summary of similar materials in the MatWeb database for the category "Phenolic, Novolac, Mineral/Graphite Filled". Each property range of values reported is minimum and maxim.. |
|||
Compressive Yield Strength | 117 - 295 MPa | 17000 - 42800 psi | Average value: 235 MPa Grade Count:20 |
Overview of materials for Polyphenylene Sulfide (PPS), Mineral/Glass-Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS), Mineral/Glass-Fiber Filled". Each property range of values reported is mini.. |
|||
Compressive Yield Strength | 117 MPa @Strain 2.00 % |
17000 psi @Strain 2.00 % |
|
TriStar TriSteel AT Metal Backed PTFE Bearing System Ultraflon 601T (AT) POM bronze with PTFE, lined metal back bearing system, high PV, self lube, high speed. This liner will run with zero lubrication required. Most commonly used in clip bearings, li.. |
|||
Compressive Yield Strength | 117 MPa | 17000 psi | ASTM D695 |
Adell BT-14 Nylon 6, 20% Glass Reinforced; Impact Modified Data provided by Adell Plastics, Inc. |
|||
Compressive Yield Strength | 117 MPa | 17000 psi | ASTM D695 |
Adell BT-34 Nylon 6, 20% Glass Reinforced; Impact Modified Data provided by Adell Plastics, Inc. |
|||
Compressive Yield Strength | 117 MPa | 17000 psi | ASTM D695 |
PolyOne Lubri-Tech™ ES-20GF/15T Polyethersulfone - 20% Glass Fiber Reinforced - 15% PTFE Lubricated
(disconti Data provided by PolyOne. |
|||
Compressive Yield Strength | 117 - 124 MPa | 17000 - 18000 psi | Average value: 119 MPa Grade Count:3 |
Overview of materials for Acrylic, Optical Sheet This property data is a summary of similar materials in the MatWeb database for the category "Acrylic, Optical Sheet". Each property range of values reported is minimum and maximum values of appropr.. |