Polymer Property : Compressive Yield Strength = 17000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Compressive Yield Strength	117 - 124 MPa	17000 - 18000 psi	Average value: 122 MPa Grade Count:6
Overview of materials for Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled". Specific grades with glass content between 25..
Compressive Yield Strength	117 - 269 MPa	17000 - 39000 psi	Average value: 151 MPa Grade Count:8
Overview of materials for Phenolic, Novolac, Mineral/Graphite Filled This property data is a summary of similar materials in the MatWeb database for the category "Phenolic, Novolac, Mineral/Graphite Filled". Each property range of values reported is minimum and maxim..
Compressive Yield Strength	117 - 295 MPa	17000 - 42800 psi	Average value: 235 MPa Grade Count:20
Overview of materials for Polyphenylene Sulfide (PPS), Mineral/Glass-Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS), Mineral/Glass-Fiber Filled". Each property range of values reported is mini..
Compressive Yield Strength	117 MPa @Strain 2.00 %	17000 psi @Strain 2.00 %
TriStar TriSteel AT Metal Backed PTFE Bearing System Ultraflon 601T (AT) POM bronze with PTFE, lined metal back bearing system, high PV, self lube, high speed. This liner will run with zero lubrication required. Most commonly used in clip bearings, li..
Compressive Yield Strength	117.2 MPa	17000 psi
Abatron AboCast/AboCure 8109-1 High melting point.Processing: 100/30 pbw; mix at 130-140°C (270 °F); cures in 16 h/120°C (250°F), 10 h/140°C (285°F), 8 h/160°C (320°F), 2 h/ 200°C (390°F).Applications: Heavy duty castin..
Compressive Yield Strength	117.2 MPa	17000 psi
Abatron AboCast/AboCure 8109-12 1-part, contains latent hardener activated by higher temperature. 4-6 month shelf life at 20-25°C (68-77°F). Other versions available with longer shelf lives and cure cycles.Processing: Potlife:..
Compressive Yield Strength	117 MPa	17000 psi	ASTM D695
Adell BT-14 Nylon 6, 20% Glass Reinforced; Impact Modified Data provided by Adell Plastics, Inc.
Compressive Yield Strength	117 MPa	17000 psi	ASTM D695
Adell BT-34 Nylon 6, 20% Glass Reinforced; Impact Modified Data provided by Adell Plastics, Inc.
Compressive Yield Strength	117 MPa	17000 psi	ASTM D695
PolyOne Lubri-Tech™ ES-20GF/15T Polyethersulfone - 20% Glass Fiber Reinforced - 15% PTFE Lubricated (disconti Data provided by PolyOne.
Compressive Yield Strength	117 - 124 MPa	17000 - 18000 psi	Average value: 119 MPa Grade Count:3
Overview of materials for Acrylic, Optical Sheet This property data is a summary of similar materials in the MatWeb database for the category "Acrylic, Optical Sheet". Each property range of values reported is minimum and maximum values of appropr..