SABIC Innovative Plastics Valox® 815 PBT (Asia Pacific)

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Valox®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Valox® 815 PBT (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
15% GR PBTP, excellent surface finish. Typical applications are hot air gun housing assemblies, industrial glue guns, appliance housings and handles.
Physical Properties Metric English Comments
Specific Gravity 1.43 g/cc
1.43 g/cc
ASTM D792
Water Absorption 0.060 %

@Time 86400 sec
0.060 %

@Time 24.0 hour
ASTM D570
Linear Mold Shrinkage, Flow 0.0040 - 0.0060 cm/cm

@Thickness 1.50 - 3.20 mm
0.0040 - 0.0060 in/in

@Thickness 0.0591 - 0.126 in
SABIC Method
0.0060 - 0.0090 cm/cm

@Thickness 3.20 - 4.60 mm
0.0060 - 0.0090 in/in

@Thickness 0.126 - 0.181 in
SABIC Method
Linear Mold Shrinkage, Transverse 0.0050 - 0.0080 cm/cm

@Thickness 1.50 - 3.20 mm
0.0050 - 0.0080 in/in

@Thickness 0.0591 - 0.126 in
SABIC Method
0.0080 - 0.011 cm/cm

@Thickness 3.20 - 4.60 mm
0.0080 - 0.011 in/in

@Thickness 0.126 - 0.181 in
SABIC Method
Mechanical Properties Metric English Comments
Hardness, Rockwell R 119
119
ASTM D785
Tensile Strength at Break 89.0 MPa
12900 psi
Type I, 5 mm/min; ASTM D638
Flexural Strength 137 MPa
19900 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 4.48 GPa
650 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 0.370 J/cm
0.693 ft-lb/in
ASTM D256
Izod Impact, Unnotched 2.67 J/cm
5.00 ft-lb/in
ASTM D4812
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 45.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
25.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
54.0 µm/m-°C

@Temperature 60.0 - 138 °C
30.0 µin/in-°F

@Temperature 140 - 280 °F
ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 210 °C

@Thickness 6.40 mm
410 °F

@Thickness 0.252 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 160 °C

@Thickness 6.40 mm
320 °F

@Thickness 0.252 in
unannealed; ASTM D648
UL RTI, Electrical 125 °C
257 °F
UL 746B
UL RTI, Mechanical with Impact 110 °C
230 °F
UL 746B
UL RTI, Mechanical without Impact 125 °C
257 °F
UL 746B
Flammability, UL94 HB

@Thickness 1.47 mm
HB

@Thickness 0.0579 in
UL 94
Electrical Properties Metric English Comments
Volume Resistivity 5.60e+16 ohm-cm
5.60e+16 ohm-cm
ASTM D257
Dielectric Constant 3.5

@Frequency 1.00e+6 Hz
3.5

@Frequency 1.00e+6 Hz
ASTM D150
3.6

@Frequency 100 Hz
3.6

@Frequency 100 Hz
ASTM D150
Dielectric Strength 22.0 kV/mm

@Thickness 3.20 mm
559 kV/in

@Thickness 0.126 in
in air; ASTM D149
23.6 kV/mm

@Thickness 1.60 mm
599 kV/in

@Thickness 0.0630 in
in oil; ASTM D149
Dissipation Factor 0.0020

@Frequency 100 Hz
0.0020

@Frequency 100 Hz
ASTM D150
Arc Resistance 120 - 180 sec
120 - 180 sec
Tungsten; ASTM D495
Comparative Tracking Index 250 - 400 V
250 - 400 V
UL 746A
Hot Wire Ignition, HWI 30 - 60 sec
30 - 60 sec
UL 746A
High Amp Arc Ignition, HAI 30 - 60 arcs
30 - 60 arcs
UL 746A
High Voltage Arc-Tracking Rate, HVTR 10.0 - 25.4 mm/min
0.394 - 1.00 in/min
UL 746A
Descriptive Properties Value Comments
Specific Volume 0.7cm^3/g
ASTM D792