SABIC Innovative Plastics LNP LUBRICOMP DFL36G PC (Asia Pacific)

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP DFL36G PC (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Lubricomp* DFL36G is a compound based on Polycarbonate resin containing Glass Fiber, PTFE, Milled Glass. Added features of this material include: Internally Lubricated.
Physical Properties Metric English Comments
Density 1.54 g/cc
0.0556 lb/in³
ISO 1183
1.55 g/cc
0.0560 lb/in³
ASTM D792
Linear Mold Shrinkage, Flow 0.0010 - 0.0030 cm/cm

@Time 86400 sec
0.0010 - 0.0030 in/in

@Time 24.0 hour
ASTM D955
0.0024 cm/cm

@Time 86400 sec
0.0024 in/in

@Time 24.0 hour
ISO 294
Linear Mold Shrinkage, Transverse 0.0030 - 0.0050 cm/cm

@Time 86400 sec
0.0030 - 0.0050 in/in

@Time 24.0 hour
ASTM D955
0.0043 cm/cm

@Time 86400 sec
0.0043 in/in

@Time 24.0 hour
ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 86.0 MPa
12500 psi
ASTM D638
90.0 MPa
13100 psi
ISO 527
Tensile Strength, Yield 90.0 MPa
13100 psi
ISO 527
91.0 MPa
13200 psi
ASTM D638
Elongation at Break 2.3 %
2.3 %
ISO 527
2.4 %
2.4 %
ASTM D638
Elongation at Yield 2.3 %
2.3 %
ASTM D638
2.3 %
2.3 %
ISO 527
Tensile Modulus 7.28 GPa
1060 ksi
1 mm/min; ISO 527
7.58 GPa
1100 ksi
50 mm/min; ASTM D638
Flexural Strength 137 MPa
19900 psi
ASTM D790
Flexural Modulus 6.89 GPa
999 ksi
ASTM D790
7.00 GPa
1020 ksi
ISO 178
Izod Impact, Notched 5.66 J/cm
10.6 ft-lb/in
ASTM D256
Izod Impact, Unnotched 1.33 J/cm
2.49 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 12.0 kJ/m²
5.71 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 37.0 kJ/m²
17.6 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 18.0 J
13.3 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 5.00 J
3.69 ft-lb
Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic 0.49
0.49
ASTM D3702 Modified
Coefficient of Friction, Static 0.41
0.41
ASTM D3702 Modified
K (wear) Factor 82.6 x 10-8 mm³/N-M
41.0 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 57.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
32.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
58.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
32.2 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 28.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
15.6 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
28.8 µm/m-°C

@Temperature -40.0 - 40.0 °C
16.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 144 °C
291 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
143 °C

@Thickness 3.20 mm
289 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 140 °C
284 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
138 °C

@Thickness 3.20 mm
280 °F

@Thickness 0.126 in
unannealed; ASTM D648