Polymer Property : Melt Flow = 4.0 g/10 min Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Physical Properties Metric English Comments
Melt Flow 1.0 - 4.0 g/10 min
1.0 - 4.0 g/10 min
(Condition L) ASTM D-1238
Multibase Multi-Flex® TPE A 6900 LC BLK
The burn rate is 1 in/min (25 mm/min) based on ASTM FM VSS 302. Multi-Flex TPE contains Kraton™ G.Data provided by Multibase.
Melt Flow 3.0 - 4.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
3.0 - 4.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ASTM D1238/L
NIZHNEKAMSKNEFTEKHIM PP 8300K (EPT30R) Propylene and Ethylene Block Polymer
Product obtained by copolymerization of propylene with ethylene in presence of complex metalorganic catalysts. It incorporates increased long-term thermal stability, thermal-oxidative degradation r..
Melt Flow 1.0 - 4.0 g/10 min

@Load 3.80 kg,
Temperature 300 °C
1.0 - 4.0 g/10 min

@Load 8.38 lb,
Temperature 572 °F
ASTM D1238
Polymer Resources PPX/NY G20 PPO/Nylon 66 Alloy , 20% Glass Reinforced
Polyphenylene Oxide/Nylon 66 Alloy , 20% Glass ReinforcedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Informa..
Melt Flow 0.10 - 4.0 g/10 min

@Load 11.6 kg,
Temperature 250 °C
0.10 - 4.0 g/10 min

@Load 25.6 lb,
Temperature 482 °F
ASTM D1238
Polymer Resources PPX-GP7 Modified-PPO, General Purpose
Modified-Polyphenylene Oxide, General Purpose, 300F HDTProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Informati..
Melt Flow 2.0 - 4.0 g/10 min

@Load 1.20 kg,
Temperature 300 °C
2.0 - 4.0 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ASTM D1238
Ravago Manufacturing Americas Hylex® P1010G40 HB Polycarbonate, 40% Fiberglass Reinforced
Information provided by Ravago.
Melt Flow 1.0 - 4.0 g/10 min
1.0 - 4.0 g/10 min
ASTM D1238
Polymer Resources PPX/NY G20 Modified PPO, 20% Glass Reinforced PPX/Nylon 6,6 Alloy  (Unverified Data**)&l
Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation.
Melt Flow 1.0 - 4.0 g/10 min
1.0 - 4.0 g/10 min
ASTM D1238
Polymer Resources PPX-FRG20 Modified PPO, UL 94 V-1, 20% Glass Reinforced  (Unverified Data**)
Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation.
Melt Flow 1.0 - 4.0 g/10 min
1.0 - 4.0 g/10 min
ASTM D1238
Polymer Resources PPX-FRG30 Modified PPO, UL 94 V-1, 30% Glass Reinforced  (Unverified Data**)
Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation.
Melt Flow 2.0 - 4.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
2.0 - 4.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
FKuR Kunststoff Bio-Flex® F 1110 Compostable PLA Blend
The BIO-FLEX® trade name indicates blends of co-polyester and PLA* with, depending on the particular grade, a very high content of natural resource material. BIO-FLEX® does not contain any sta..
Melt Flow 3.0 - 4.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
3.0 - 4.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
FKuR Kunststoff Terralene® WF 6534 Biobased Polyethylene
With the brand name Terralene® FKuR offers biobased polyethylene compounds made using Braskem's Green PE. When compared to conventional polyethylene (PE), the main difference is that the ethanol..
Melt Flow 1.0 - 4.0 g/10 min

@Load 1.20 kg,
Temperature 300 °C
1.0 - 4.0 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ASTM D1238
Iran Petrochemical (PCC) PC 0104 Polycarbonate
Suitable for extrusionInformation provided by Iran Petrochemical Commercial Co.
Melt Flow 3.0 - 4.0 g/10 min
3.0 - 4.0 g/10 min
ASTM D1238
Micropol Microlin ML20 Linear Polyethylene Rotational Molding Powder
Information provided by Micropol Limited
Melt Flow 3.0 - 4.0 g/10 min
3.0 - 4.0 g/10 min
ASTM D1238
Micropol Microlin ML25 Linear Polyethylene Rotational Molding Powder
Information provided by Micropol Limited
Melt Flow 2.0 - 4.0 g/10 min

@Load 5.00 kg,
Temperature 230 °C
2.0 - 4.0 g/10 min

@Load 11.0 lb,
Temperature 446 °F
ASTM D1238
Kureha KF Polymer 1100 PVDF Homopolymer
KF Polymer is a fire-resistant engineering plastic which maintains the excellent performance of a fluoropolymer. It shows well-balanced molding processability similar to general-purpose resins. KF p..
Melt Flow 2.1 - 4.0 g/10 min
2.1 - 4.0 g/10 min
Shandong Dongyue Shenzhou New Material Co DS601 Perfluorinated Ethylene-Propylene Copolymer
Conformable with: Q/DYS 003-2007Fluorinated Ethylene Propylene resin is the copolymer of the TFE and HFP, with good thermal stability, outstanding chemical inertness, good electrical insulation, and..
Melt Flow 1.0 - 4.0 g/10 min

@Load 10.0 kg,
Temperature 230 °C
1.0 - 4.0 g/10 min

@Load 22.0 lb,
Temperature 446 °F
ASTM D1238
Shanghai Ofluorine M-1 PVDF Molding Grade
Description: M-1 PVDF is a kind of granules homopolymer, which has high melt viscosity, M-1 is more suitable for compression molding process. M-1 PVDF pellets as raw materials, the finished products..
Melt Flow 3.0 - 4.0 g/10 min

@Load 5.00 kg,
Temperature 200 °C
3.0 - 4.0 g/10 min

@Load 11.0 lb,
Temperature 392 °F
Granulate; ISO 1133/H
SYNTHOS Krasten® 662E High Impact Polystyrene
High impact grade with properties suitable for thermoforming. Processed mainly by extrusion and thermoforming. Production of demanding visual appearance plates, technical parts, sheets and molded pa..
Melt Flow 2.0 - 4.0 g/10 min
2.0 - 4.0 g/10 min
ASTM D1238
A. Schulman PP 1188-01 Polypropylene Extra High-Impact Polypropylene
DescriptionPolypropylene PP 1188-01 is an extra high-impact polypropylene, copolymer type, with excellent low temperature properties. Information provided by A. Schulman.
Melt Flow 2.0 - 4.0 g/10 min
2.0 - 4.0 g/10 min
ASTM D1238
A. Schulman PP 1188-01 Polypropylene Extra High-Impact Polypropylene
DescriptionPolypropylene PP 1188-01 is an extra high-impact polypropylene, copolymer type, with excellent low temperature properties. Information provided by A. Schulman.
Melt Flow 2.0 - 4.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
2.0 - 4.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ASTM D 1238
RTP Company RTP 102 FR Polypropylene (PP), Glass Fiber - Flame Retardant
Melt Flow 2.0 - 4.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
2.0 - 4.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ASTM D 1238
RTP Company RTP 105 CC FR Polypropylene (PP), Glass Fiber - Chemically Coupled - Flame Retardant - UL94 V-0
Melt Flow 2.0 - 4.0 g/10 min
2.0 - 4.0 g/10 min
ASTM D1238
A. Schulman PP 1188-01 Polypropylene Extra High-Impact Polypropylene
DescriptionPolypropylene PP 1188-01 is an extra high-impact polypropylene, copolymer type, with excellent low temperature properties. Information provided by A. Schulman.
Melt Flow 1.0 - 4.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
1.0 - 4.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ASTM D 1238
Cossa Polimeri ESTAPROP H0260 MC/EC Conductive Polypropylene, Mineral Filled
Information provided by Cossa Polimeri S.r.l.
Melt Flow 2.0 - 4.0 g/10 min

@Load 5.00 kg,
Temperature 232 °C
2.0 - 4.0 g/10 min

@Load 11.0 lb,
Temperature 450 °F
ASTM D1238
Arkema Group KYNAR® 6000 HD Polyvinylidene Fluoride - Injection Molding
Characteristics: Natural resin - translucent, off-white hemispheres. High stability in harsh thermal, chemical and ultraviolet environments. High toughness and mechanical strength, low permeabili..
Melt Flow 2.5 - 4.0 g/10 min

@Load 10.0 kg,
Temperature 230 °C
2.5 - 4.0 g/10 min

@Load 22.0 lb,
Temperature 446 °F
ASTM D1238
Solvay Specialty Polymers Solef® 60512 Polyvinylidene Fluoride (PVDF)  (Unverified Data**)
Solef® 60512 PVDF copolymer has high viscosity of the melt and it is a grade for offshore piping.Information provided by Solvay Specialty Polymers.
Melt Flow 2.0 - 4.0 g/10 min
2.0 - 4.0 g/10 min
ASTM D1238
Polymer Resources AC-GP1 Acetal Copolymer, Low Flow, High Melt Strength  (Unverified Data**)
Process: Molding or ExtrusionNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation.
Melt Flow 1.0 - 4.0 g/10 min
1.0 - 4.0 g/10 min
ASTM D1238
Polymer Resources PPX/NY G30 Modified PPO, 30% Glass Reinforced PPX/Nylon 6,6 Alloy  (Unverified Data**)&l
Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation.
Melt Flow 1.0 - 4.0 g/10 min
1.0 - 4.0 g/10 min
ASTM D1238
Polymer Resources PPX-G20 Modified PPO, 20% Glass Reinforced  (Unverified Data**)
Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation.
Melt Flow 1.0 - 4.0 g/10 min
1.0 - 4.0 g/10 min
ASTM D1238
Polymer Resources PPX-G30 Modified PPO, 30% Glass Reinforced  (Unverified Data**)
Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation.
Melt Flow 3.0 - 4.0 g/10 min

@Load 5.00 kg,
Temperature 200 °C
3.0 - 4.0 g/10 min

@Load 11.0 lb,
Temperature 392 °F
Granulate; ISO 1133/H
SYNTHOS Krasten® 562E High Impact Polystyrene
High impact grade with properties suitable for thermoforming. Processed mainly by extrusion and thermoforming. Production of plates, sheets, technical parts and molded packaging (used in e.g. the fo..