Polymer Resources PPX-GP6 Modified PPO, General Purpose with HDT of 290 F  (Unverified Data**)

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether, Molded
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polymer Resources PPX-GP6 Modified PPO, General Purpose with HDT of 290 F  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation.
Physical Properties Metric English Comments
Density 1.06 g/cc
0.0383 lb/in³
ASTM D792
Linear Mold Shrinkage 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
ASTM D955
Melt Flow 0.10 - 4.0 g/10 min
0.10 - 4.0 g/10 min
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 61.4 MPa
8900 psi
ASTM D638
Tensile Strength, Yield 58.6 MPa
8500 psi
ASTM D638
Flexural Strength 84.8 MPa
12300 psi
ASTM D790
Flexural Modulus 2.21 GPa
320 ksi
ASTM D790
Izod Impact, Notched 2.67 J/cm
5.00 ft-lb/in
ASTM D256
Gardner Impact >= 22.6 J
>= 16.7 ft-lb
ASTM D3029
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 143 °C
290 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 138 °C
280 °F
ASTM D648
Flammability, UL94 HB
HB
1/16 in
HB
HB
1/8 in
Processing Properties Metric English Comments
Rear Barrel Temperature 260 - 304 °C
500 - 580 °F
Middle Barrel Temperature 271 - 310 °C
520 - 590 °F
Front Barrel Temperature 282 - 316 °C
540 - 600 °F
Melt Temperature 293 - 316 °C
560 - 600 °F
Mold Temperature 76.7 - 98.9 °C
170 - 210 °F
Drying Temperature 104 - 110 °C
220 - 230 °F
Dry Time 3 - 4 hour
3 - 4 hour