Polymer Resources PC-IM4 Polycarbonate, Impact Modified, Easy Flow

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Impact Modified
Manufacturer Polymer Resources, LTD
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polymer Resources PC-IM4 Polycarbonate, Impact Modified, Easy Flow.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polycarbonate, Impact Modified, Easy FlowProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation.
Physical Properties Metric English Comments
Specific Gravity 1.19 g/cc
1.19 g/cc
ASTM D792
Linear Mold Shrinkage 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
ASTM D955
Melt Flow 20 - 30 g/10 min

@Load 1.20 kg,
Temperature 300 °C
20 - 30 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 53.1 MPa
7700 psi
ASTM D638
Tensile Strength, Yield 51.7 MPa
7500 psi
ASTM D638
Elongation at Break 100 %
100 %
ASTM D638
Elongation at Yield 6.0 %
6.0 %
ASTM D638
Flexural Strength 68.9 MPa
10000 psi
ASTM D790
Flexural Modulus 2.00 GPa
290 ksi
ASTM D790
Izod Impact, Notched 5.34 J/cm

@Temperature -17.8 °C
10.0 ft-lb/in

@Temperature 0.000 °F
ASTM D256
6.41 J/cm

@Temperature 22.8 °C
12.0 ft-lb/in

@Temperature 73.0 °F
ASTM D256
Gardner Impact 36.2 J
26.7 ft-lb
ASTM D3029
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 124 °C
255 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 118 °C
245 °F
ASTM D648
Vicat Softening Point 141 °C
285 °F
120°C/h, 50 N; ASTM D1525
Flammability, UL94 HB

@Thickness 1.59 mm
HB

@Thickness 0.0626 in
HB

@Thickness 3.17 mm
HB

@Thickness 0.125 in
Processing Properties Metric English Comments
Rear Barrel Temperature 254 - 277 °C
490 - 530 °F
Middle Barrel Temperature 266 - 288 °C
510 - 550 °F
Front Barrel Temperature 277 - 299 °C
530 - 570 °F
Melt Temperature 274 - 302 °C
525 - 575 °F
Mold Temperature 71.1 - 93.3 °C
160 - 200 °F
Drying Temperature 118 - 124 °C
245 - 255 °F
Dry Time 3.00 - 4.00 hour
3.00 - 4.00 hour
Descriptive Properties Value Comments
Vent 0.0005