Aclo Accutech Polypropylene Homopolymer HP0334M10CL Mica Reinforced Coupled
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 10% Mica Filler |
| Manufacturer | Aclo Compounders |
| Trade Name | Accutech |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accutech Polypropylene Homopolymer HP0334M10CL Mica Reinforced Coupled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.960 g/cc | 0.0347 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.010 cm/cm | 0.010 in/in | MD; ASTM D955 |
| Melt Flow | 3.0 g/10 min | 3.0 g/10 min | ASTM D1238 |
| Ash | 10 % | 10 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 84 | 84 | ASTM D785 |
| Tensile Strength at Break | 25.0 MPa | 3630 psi | ASTM D638 |
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | ASTM D638 |
| Elongation at Break | 21 % | 21 % | ASTM D638 |
| Elongation at Yield | 8.0 % | 8.0 % | ASTM D638 |
| Tensile Modulus | 1.80 GPa | 261 ksi | ASTM D638 |
| Flexural Strength | 41.0 MPa | 5950 psi | ASTM D790 |
| Flexural Modulus | 1.80 GPa | 261 ksi | ASTM D790 |
| Izod Impact, Notched | 0.502 J/cm | 0.940 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 112 °C | 234 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 58.9 °C | 138 °F |
Users viewing this material also viewed the following:
- Polymax® Maxelast® N8955 TPE, Nylon Overmold
- DuPont™ Sclairfilm® LX-1 LLDPE Film, Laminating, 50.8 µm Thickness (discontinued **)
- Mitsui AURUM® JCN6230 Thermoplastic Polyimide Resin, Crystalline (discontinued **)
- Lehmann & Voss LUVOCOM® 65-8452-1 PP-copolymer, with aramid reinforcement, lubricant modified
- IBC Advanced Alloys FA230 Beryllium Nickel Casting Alloy
- Covestro Desmopan® DP 9395AU Polyurethane
- ExxonMobil Exxtral™ H1725W Performance Polyolefin
- ChevronTexaco SAE 10W Transmission and Drive Train TO-4 Oil
- Cosmic Plastics 6160 Mineral Filled Ortho Diallyl Phthalate Molding Compound
Copyright © lookpolymers.com All Rights Reserved