Polymer Property : Melt Flow = 11 g/10 min Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Physical Properties Metric English Comments
Melt Flow 7.0 - 11 g/10 min

@Load 5.00 kg,
Temperature 200 °C
7.0 - 11 g/10 min

@Load 11.0 lb,
Temperature 392 °F
ASTM D1238
NIZHNEKAMSKNEFTEKHIM 524B General Purpose Polystyrene
Polystyrene intended to produce glossy coating by co-extrusion. A specialty recipe provides for drastic reduction of buildup in a die plate and of streaks on an article in molding.Information provi..
Melt Flow 7.0 - 11 g/10 min

@Load 5.00 kg,
Temperature 200 °C
7.0 - 11 g/10 min

@Load 11.0 lb,
Temperature 392 °F
ASTM D1238
NIZHNEKAMSKNEFTEKHIM 525 General Purpose Polystyrene
Grade 525 is a crystal polystyrene for both injection molding and cap layer co-extrusion. Injection molding applications such as medical and laboratory parts, tumblers, and jewel boxes demonstrate t..
Melt Flow 4.0 - 11 g/10 min

@Load 1.20 kg,
Temperature 300 °C
4.0 - 11 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ASTM D1238
Polymer Resources PC-G5-IM Polycarbonate, 5% Glass Reinforced, Impact Modified, Foamable
Polycarbonate, 5% Glass Reinforced, Impact Modified, FoamableProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Inf..
Melt Flow 9.0 - 11 g/10 min

@Load 5.00 kg,
Temperature 190 °C
9.0 - 11 g/10 min

@Load 11.0 lb,
Temperature 374 °F
ISO 1133
FKuR Kunststoff Fibrolon® F 8530 Biodegradable Wood-Plastic Compound, Fiber Reinforced
FIBROLON® are fiber reinforced compounds. Depending on specific customer requirements either a biodegradable polymer or a polyolefin can be used as the polymeric matrix. With the brand name of F..
Melt Flow 8.0 - 11 g/10 min
8.0 - 11 g/10 min
ASTM D1238
Kolon KOCETAL® EL306 Toughened Grade Acetal Resin
Flexible grade. Applications: Flexible products. Information provided by API-Kolon.
Melt Flow 8.5 - 11 g/10 min
8.5 - 11 g/10 min
ASTM D1238
Kolon KOCETAL® GF705 G/F Reinforced Acetal Resin
Glass fiber reinforced, improved stiffnessApplications: Products for high stiffness, improved fatigue properties. Information provided by API-Kolon.
Melt Flow 8.5 - 11 g/10 min
8.5 - 11 g/10 min
ASTM D1238
Kolon KOCETAL® MS301 Wear Modified Acetal Resin
Molybdenum disulfide added, improved wear property. Applications: Products for low noise and friction against metal. Information provided by API-Kolon.
Melt Flow 9.0 - 11 g/10 min
9.0 - 11 g/10 min
230/2.16 (typical); ASTM D1238
Fiberfil® J-68/25/E/SD Polypropylene Copolymer, 25% Glass Fiber Reinforced, Chemically coupled, with static dissipation
Information provided by FIBERFIL Engineered Plastics
Melt Flow 5.0 - 11 g/10 min
5.0 - 11 g/10 min
ASTM D1238 - ISO 1133
DuPont Elvaloy® 4170 Reactive Ethylene Terpolymer (RET)
A reactive ethylene terpolymer (RET) that can be used to modify the properties of asphalt binder used in paving.Elvoy® 4170 is the most chemically reactive of the terpolymers manufactured by DuPont..
Melt Flow 3.0 - 11 g/10 min

@Load 2.16 kg,
Temperature 230 °C
3.0 - 11 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ASTM D1238
A. Schulman POLYFLAM™ E-15937B High Strength Impact Modified Polypropylene
DescriptionPolyfort® E-15937B is a high strength impact modified polypropylene.Information provided by A. Schulman.
Melt Flow 3.0 - 11 g/10 min

@Load 2.16 kg,
Temperature 230 °C
3.0 - 11 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ASTM D1238
A. Schulman POLYFLAM™ E-15937B High Strength Impact Modified Polypropylene
DescriptionPolyfort® E-15937B is a high strength impact modified polypropylene.Information provided by A. Schulman.
Melt Flow 3.0 - 11 g/10 min

@Load 2.16 kg,
Temperature 230 °C
3.0 - 11 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ASTM D1238
A. Schulman POLYFLAM™ E-15937B High Strength Impact Modified Polypropylene
DescriptionPolyfort® E-15937B is a high strength impact modified polypropylene.Information provided by A. Schulman.
Melt Flow 3.0 - 11 g/10 min

@Load 2.16 kg,
Temperature 230 °C
3.0 - 11 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ASTM D1238
A. Schulman POLYFLAM™ E-15937B High Strength Impact Modified Polypropylene
DescriptionPolyfort® E-15937B is a high strength impact modified polypropylene.Information provided by A. Schulman.
Melt Flow 3.0 - 11 g/10 min

@Load 2.16 kg,
Temperature 230 °C
3.0 - 11 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ASTM D1238
A. Schulman POLYFLAM™ E-15937B High Strength Impact Modified Polypropylene
DescriptionPolyfort® E-15937B is a high strength impact modified polypropylene.Information provided by A. Schulman.
Melt Flow 9.0 - 11 g/10 min

@Load 1.20 kg,
Temperature 300 °C
9.0 - 11 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ASTM D1238
Adell DS-10 General Purpose Polycarbonate
Melt Flow 8.0 - 11 g/10 min
8.0 - 11 g/10 min
Ashley Polymers Ashlene® RH190H2-B Acetal
General purpose, reprocessed homopolymer, excellent toughness, strength, stiffness and lubricity. UV stabilized with carbon black for outstanding weatherability.Data provided by the manufacturer
Melt Flow 8.0 - 11 g/10 min
8.0 - 11 g/10 min
Ashley Polymers Ashlene® RH190 Acetal
General purpose, reprocessed homopolymer, excellent toughness, strength, stiffness and lubricity. Available in Natural and Black. Natural: Designated RH190N-3; Black: Designated RH190B.Data provid..
Melt Flow 3.0 - 11 g/10 min

@Load 2.16 kg,
Temperature 230 °C
3.0 - 11 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ASTM D1238
A. Schulman POLYFLAM™ E-15937B High Strength Impact Modified Polypropylene
DescriptionPolyfort® E-15937B is a high strength impact modified polypropylene.Information provided by A. Schulman.
Melt Flow 7.0 - 11 g/10 min
7.0 - 11 g/10 min
ASTM D1238
Buckeye Polymers BP RPP 1509 GK BLK Polypropylene, 15% Glass Filled
Product Information: 15% glass reinforced polypropyleneProduct Features:Offers improved flex modulus while maintaining a low specific gravity propertyChemically coupled for improvved physical proper..