Plastcom SLOVAMID 66 HI Polyamide 66, Impact Grade

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Impact Grade
Manufacturer Plastcom spol. s r.o.
Trade Name SLOVAMID
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Plastcom SLOVAMID 66 HI Polyamide 66, Impact Grade.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
FeaturesModified with thermoplastic reactive elastomer, determined for mouldings with high toughness also at low temperatures. Eligible application for ski-shoes, helmets for sport and other safety use /hockey, building/, protection frames of car doors. Withstands high dynamic stress up to -40°C. Delivered in natural and in the full RAL color scale.Application: Injection MouldingInformation Provided by Plastcom spol. s r.o.
Physical Properties Metric English Comments
Density 1.09 g/cc
0.0394 lb/in³
STN 64 0111
Linear Mold Shrinkage 0.018 cm/cm
0.018 in/in
STN 64 0808
Linear Mold Shrinkage, Transverse 0.0183 cm/cm
0.0183 in/in
STN 64 0808
Melt Flow 2.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
2.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
STN EN ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 40.0 MPa
5800 psi
STN EN ISO 527-2
Elongation at Break 50 %
50 %
STN EN ISO 527-2
Tensile Modulus 1.80 GPa
261 ksi
STN EN ISO 527-2
Flexural Strength 60.0 MPa
8700 psi
STN EN ISO 178
Flexural Modulus 1.50 GPa
218 ksi
STN EN ISO 178
Charpy Impact Unnotched NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
STN EN ISO 179
NB

@Temperature -20.0 °C
NB

@Temperature -4.00 °F
STN EN ISO 179
Charpy Impact, Notched 1.00 J/cm²

@Temperature -20.0 °C
4.76 ft-lb/in²

@Temperature -4.00 °F
STN EN ISO 179
1.20 J/cm²

@Temperature 23.0 °C
5.71 ft-lb/in²

@Temperature 73.4 °F
STN EN ISO 179
Thermal Properties Metric English Comments
Melting Point 260 °C
500 °F
DSC; STN EN ISO 3146
Deflection Temperature at 1.8 MPa (264 psi) 59.0 °C
138 °F
STN EN ISO 75/A
Vicat Softening Point 190 °C
374 °F
B; STN EN ISO 306
Processing Properties Metric English Comments
Melt Temperature 280 - 300 °C
536 - 572 °F
Mold Temperature 60.0 - 80.0 °C
140 - 176 °F
Drying Temperature 80.0 °C
176 °F
Dry Time 4 hour
4 hour
Moisture Content 0.15 %
0.15 %
STN EN ISO 960
Injection Pressure 70.0 - 120 MPa
10200 - 17400 psi