- Polymer Property : Melt Flow = 1.7 g/10 min
Polymer Property : Melt Flow = 1.7 g/10 min Product List
Physical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Flow | 1.7 g/10 min | 1.7 g/10 min | ASTM D1238 |
| Plaskolite Optix® CA-945 Clear Impact Modified Acrylic Resin Impact modified acrylic resin, extrusion and injection moldingApplications: An impact-modified acrylic resin for extrusion and injection molding. This resin offers impact strengths up to six times .. |
|||
| Melt Flow | 1.7 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.7 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| DuPont Bynel® 41E532 Anhydride-Modified LLDPE Adhesive Resin
(discontinued **) Bynel® Series 4100 resins are anhydride-modified, linear low-density polyethylene (LLDPE) resins. All 4100 Series resins are available in pellet form for use in conventional extrusion and coextrusi.. |
|||
| Melt Flow | 1.7 g/10 min @Load 5.00 kg, Temperature 190 °C |
1.7 g/10 min @Load 11.0 lb, Temperature 374 °F |
ISO 1133 |
| Premix Thermoplastics PRE-ELEC® PE 1308
(discontinued **) PRE-ELEC PE 1308 is a conductive thermoplastic compound based on a blend of PE-LD/PE-LLD. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivi.. |
|||
| Melt Flow | 1.7 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.7 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Eastman 800E Polyethylene
(discontinued **) Polyethylene 800E is used in general-purpose extrusion applications that also require good stress resistance. This formula complies with FDA regulations at 21 CFR177.1520 (c)(2.2) for use in articl.. |
|||
| Melt Flow | 1.7 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.7 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Eastman Voridian 800P Polyethylene
(discontinued **) General purpose low density formulation used for extrusion coating applications that require good stress resistance. This formula complies with FDA regulations at 21 CFR 177.1520(c)(2.1) for use i.. |
|||
| Melt Flow | 1.7 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.7 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Eastman E6838-862A Polyethylene
(discontinued **) E6838-862A is a low density formulation suggested for injection molding applications, such as closuresInformation supplied by the manufacturer.Information from manufacturer data sheet.Eastman Chemic.. |
|||
| Melt Flow | 1.7 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.7 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| NOVA Chemicals Sclair® 10A Octene VLDPE Film Resin
(discontinued **) Film Properties. Features: Low gel, excellent sealability, easy processability, excellent clarity.Applications: Blending resin for improved toughness.Data provided by the manufacturer. |
|||
| Melt Flow | 1.7 g/10 min | 1.7 g/10 min | ASTM D1238 |
| LyondellBasell Plexar® PX3227 Extrudable Tie-Layer Resin - Anhydride Modified LLDPE General DescriptionPLEXAR tie-layers are chemically modified resins used to bond unlike materials, primarily in packaging and industrial applications. Common adherents include polyethylene resins a.. |
|||
| Melt Flow | 1.7 g/10 min @Load 3.80 kg, Temperature 230 °C |
1.7 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
| M. Holland Company AB105 ABS Features: Medium Flow, High Impact Resistance, Good StiffnessUses: Household Goods, Packaging Processing Method: Injection MoldingInformation provided by M. Holland. |
|||
| Melt Flow | 1.7 g/10 min | 1.7 g/10 min | ASTM D1238 |
| Hyosung Topilene J301CP PP J301CP Injection Special Purpose GradeApplications: Cap of pressure bottleCharacteristics:High stiffnessSlip propertyInformation provided by Hyosung Corporation |
|||
| Melt Flow | 1.7 g/10 min @Load 2.16 kg, Temperature 230 °C |
1.7 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Ineos H01H-00 Polypropylene Homopolymer This is a low flow rate homopolymer designed for extrusion or injection molding. This material meets the requirements of the U.S. Food and Drug Administration as specified in 21 CFR 177.1520.Applic.. |
|||
| Melt Flow | 1.7 - 2.5 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.7 - 2.5 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238-00 |
| Ipiranga Petrochem LB 0216 LLDP IPQ produces Linear Low Density Polyethylene (LLDPE) for use by plastics molding industry segments that employ extrusion processes in the manufacturing of films destined for producing bobbins and ba.. |
|||
| Melt Flow | 1.7 g/10 min @Load 5.00 kg, Temperature 200 °C |
1.7 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Iran Petrochemical (PCC) SD-0150 Acrylonitrile Butadiene Styrene General Purpose ABS, SD 0150 grade, is a rigid thermoplastic with good processing characteristics. It is a high flow injection molding grade with considerable impact strength and medium heat deflec.. |
|||
| Melt Flow | 1.7 g/10 min | 1.7 g/10 min | ISO 1133 |
| Lucite International Diakon® CLH952LX Acrylic Polymer Information provided by Lucite International |
|||
| Melt Flow | 1.7 g/10 min @Load 2.16 kg, Temperature 230 °C |
1.7 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Ineos R01A-01 Polypropylene Copolymer, Antistatic An antistated polypropylene random copolymer produced by Ineos utilizing unique catalyst technology. It is designed for blowmolding and extrusion applications and exhibits good stiffness and improv.. |
|||
| Melt Flow | 1.7 g/10 min @Load 5.00 kg, Temperature 200 °C |
1.7 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Samsung Cheil Industries Starex® SD-0170 F ABS, Unreinforced Information provided by Samsung Cheil Industries. |
|||
| Melt Flow | 1.7 g/10 min @Load 5.00 kg, Temperature 200 °C |
1.7 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Samsung Cheil Industries Starex® SD-0150U ABS, Unreinforced Information provided by Samsung Cheil Industries. |
|||
| Melt Flow | 1.7 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.7 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Borealis Borstar® HE 6068 Natural Bimodal HDPE with very low shrinkage for Submarine and Fiber Optical Cables Borstar® HE6068 is a natural, UV-stabilized, colorable, bimodal high density (HD) jacketing compound, which is produced with the Borealis proprietary Borstar® bimodal process technology. Borstar®.. |
|||
| Melt Flow | 1.7 g/10 min | 1.7 g/10 min | ASTM D1238/E |
| Borealis Borstar® HE6067 Black Bimodal HD Polyethylene Compound for Jacketing of Communication and Power Cables Borstar HE6067 is a black, bimodal, co-polymer high density polyethylene (HDPE) compound produced according to the bimodal Borstar process. It is characterized by its balanced properties important .. |
|||
| Melt Flow | 1.7 g/10 min @Load 3.80 kg, Temperature 230 °C |
1.7 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
| PlastxWorld CEVIAN®-V 420 ABS Heat Resistant ABSThese are typical values and are not intended for specification purposes. UL approved file No. is E47773. Information provided by PlastxWorld Inc. |
|||
| Melt Flow | 1.7 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.7 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Westlake EN1817AA Low Density Polyethylene Westlake Polyethylene EN1817 is a low density formulation suggested for film applications requiring high clarity, good tear and impact strength, good printability and a wide heat-sealing range.Appli.. |
|||
| Melt Flow | 1.7 g/10 min @Temperature 230 °C |
1.7 g/10 min @Temperature 446 °F |
I<sub>2</sub>; ASTM D1238 |
| Formosa Plastics Formolene® 2302E Impact Copolymer Polypropylene Impact Copolymer for Extrusion Applications Formolene® 2302E is a low flow, medium impact polypropylene copolymer designed for extrusion applications. It is a barefoot resin with a basic stabilizat.. |
|||
| Melt Flow | 1.7 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.7 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Polyram RamTal PMH2017 Polyacetal Homopolymer for Injection Molding General purpose polyacetal homopolymer for injection molding applications, MFI 1.7.Information provided by Polyram. |
|||
| Melt Flow | 1.7 g/10 min @Load 5.00 kg, Temperature 235 °C |
1.7 g/10 min @Load 11.0 lb, Temperature 455 °F |
after drying; ISO 1133 |
| Arkema Group Orgalloy® LT 4060 Polyamide Alloy Polyamide Alloy, Flexible gradeTubes / Mandrels / Profiles / CablesInformation provided by Arkema Group |
|||
| Melt Flow | 1.7 g/10 min | 1.7 g/10 min | |
| Ashley Polymers Ashlene® ABS Resin F-214 General purpose, medium impact resin.Data provided by the manufacturer |
|||
| Melt Flow | 1.7 g/10 min | 1.7 g/10 min | ISO 1133 D |
| Asahi Kasei Tenac® SH210 Homopolymer Acetal Resin Super high-impact grade; highest molecular weight category.Information provided by Asahi Kasei Corporation. |
|||
| Melt Flow | 1.7 g/10 min @Load 5.00 kg, Temperature 200 °C |
1.7 g/10 min @Load 11.0 lb, Temperature 392 °F |
ISO 1133 |
| Ineos Nova 201 Crystal Polystyrene High Heat Extrusion Grade
(discontinued **) Excellent heat resistance, Superior melt strengthApplications: Foam insulation, Oriented polystyrene sheet (OPS), XPS food packaging, Sheet and profile extrusionProperties were determined on injecti.. |
|||
| Melt Flow | 1.7 - 2.3 g/10 min | 1.7 - 2.3 g/10 min | ±12% |
| Kazanorgsintez 108-76 Film Grade Composition of High Density Polyethylene Production Method: Based on polyethylene grades 10803-20, 15803-20, 15813-020,17504-006. Application: Designed for packing manufacture for milk and milk products.Information Provided by Kazanorg.. |
|||
| Melt Flow | 1.7 g/10 min @Load 2.16 kg, Temperature 230 °C |
1.7 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Multibase Multi-Flex® A 6502 MR Natural TPE Thermoplastic Elastomer Forms: PelletsInformation provided by Multibase |
|||