NOVA Chemicals Sclair® 10A Octene VLDPE Film Resin (discontinued **)

Category	Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Very Low Density Polyethylene (VLDPE)
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	NOVA Chemicals Sclair® 10A Octene VLDPE Film Resin (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Film Properties. Features: Low gel, excellent sealability, easy processability, excellent clarity.Applications: Blending resin for improved toughness.Data provided by the manufacturer.

Physical Properties	Metric	English	Comments
Density	0.911 g/cc	0.0329 lb/in³	ASTM D792
Melt Flow	1.7 g/10 min @Load 2.16 kg, Temperature 190 °C	1.7 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Yield, MD	6.00 MPa	870 psi	ASTM D882
Film Tensile Strength at Yield, TD	5.00 MPa	725 psi	ASTM D882
Film Elongation at Break, MD	400 %	400 %	ASTM D882
Film Elongation at Break, TD	940 %	940 %	ASTM D882
Secant Modulus, MD	0.0680 GPa	9.86 ksi	ASTM D882
Secant Modulus, TD	0.0800 GPa	11.6 ksi	ASTM D882
Coefficient of Friction	>= 1.0	>= 1.0	ASTM D1894
Elmendorf Tear Strength, MD	13.0 g/micron	330 g/mil	ASTM D1922
Elmendorf Tear Strength, TD	21.0 g/micron	533 g/mil	ASTM D1922
Dart Drop	6.00 g/micron	152 g/mil	F 50; ASTM D1709/A
Film Tensile Strength at Break, MD	34.0 MPa	4930 psi	ASTM D882
Film Tensile Strength at Break, TD	27.0 MPa	3920 psi	ASTM D882

Optical Properties	Metric	English	Comments
Haze	1.0 % @Thickness 0.0250 mm	1.0 % @Thickness 0.000984 in	ASTM D1003
Gloss	92 %	92 %	45°; 1 mil; ASTM D1894

Processing Properties	Metric	English	Comments
Melt Temperature	260 - 290 °C	500 - 554 °F