Physical Properties | Metric | English | Comments |
---|---|---|---|
Melt Flow | 1.7 g/10 min | 1.7 g/10 min | (Condition L) ASTM D-1238 |
Multibase Multi-Flex® TPE A 7699 BLK Multi-Flex® A 7699 is an acoustic barrier compound for medium density applications . Multi-Flex® TPE compounds are based on Shell Kraton G polymers licensed to Multibase. Multi-Flex TPE contains.. |
|||
Melt Flow | 1.7 g/10 min | 1.7 g/10 min | ASTM D1238 |
Plaskolite West Optix® CA-945 Clear Impact Modified Acrylic Resin Impact modified acrylic resin, extrusion and injection moldingApplications: An impact-modified acrylic resin for extrusion and injection molding. This resin offers impact strengths up to six times .. |
|||
Melt Flow | 1.7 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.7 g/10 min @Load 4.76 lb, Temperature 374 °F |
Compression Molded; ASTM D1238 |
NOVA Chemicals Surpass® RMs244-UG Octene sHDPE Rotational Molding Film Features: Octene copolymerExceptional low temperature propertiesOutstanding stiffnessBroad processing windowSuperior whiteness for improved part appearanceEasy mold releaseNSF listed for Standards 1.. |
|||
Melt Flow | 1.7 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.7 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
DuPont Bynel® 41E532 Anhydride-Modified LLDPE Adhesive Resin
(discontinued **) Bynel® Series 4100 resins are anhydride-modified, linear low-density polyethylene (LLDPE) resins. All 4100 Series resins are available in pellet form for use in conventional extrusion and coextrusi.. |
|||
Melt Flow | 1.7 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.7 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
Eastman D4027-P Voridian Polyethylene
(discontinued **) VORIDIAN low density polyethylene D4027-P is a formulation suggested for extrusion coating applications that require clarity, high gloss and superior hot tack properties. Applications/UsesFood Packa.. |
|||
Melt Flow | 1.7 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.7 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
Eastman 1830A Polyethylene
(discontinued **) Polyethylene 1830A is a low density formulation. It is suggested for injection molding applications requiring good stiffness or gloss properties . It us used in applications such as closures.Polyet.. |
|||
Melt Flow | 1.7 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.7 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
Eastman E6838-899F Polyethylene
(discontinued **) E6838-899F is a low density formulation with no slip or antiblock. It is suggested for film applications requiring high clarity, good tear and impact strength, a wide heat-sealing range, and good pr.. |
|||
Melt Flow | 1.7 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.7 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
Eastman E6838-862A Polyethylene
(discontinued **) E6838-862A is a low density formulation suggested for injection molding applications, such as closuresInformation supplied by the manufacturer.Information from manufacturer data sheet.Eastman Chemic.. |
|||
Melt Flow | 1.7 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.7 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
NOVA Chemicals Sclair® 10A Octene VLDPE Film Resin
(discontinued **) Film Properties. Features: Low gel, excellent sealability, easy processability, excellent clarity.Applications: Blending resin for improved toughness.Data provided by the manufacturer. |
|||
Melt Flow | 1.7 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.7 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 - ISO 1133 |
DuPont Bexloy® AXW507NC010 Modified Ionomer Resin
(discontinued **) A modified ionomer resin engineered for injection molded exterior automotive applications.Availability: North AmericaInformation provided by DuPont. |
|||
Melt Flow | 1.7 - 2.3 g/10 min | 1.7 - 2.3 g/10 min | |
Kazanorgsintez 108-14C Low Density Polyethylene Composite Production Method: Produced from 10803-020 grade low density polyethylene, carbon black, and sliding aid. Application: Designed for production of light-proof polyethylene bags with sliding effe.. |
|||
Melt Flow | 1.7 - 2.3 g/10 min | 1.7 - 2.3 g/10 min | ±12% |
Kazanorgsintez 108-225 Film Grade Composition of High Density Polyethylene Production Method: Based on polyethylene grades 10803-20, 15803-20, 15813-020,17504-006. Application: Designed for packing manufacture for milk and milk products.Information Provided by Kazanorg.. |
|||
Melt Flow | 1.7 g/10 min | 1.7 g/10 min | ASTM D1238 |
LyondellBasell Plexar® PX3227 Extrudable Tie-Layer Resin - Anhydride Modified LLDPE General DescriptionPLEXAR tie-layers are chemically modified resins used to bond unlike materials, primarily in packaging and industrial applications. Common adherents include polyethylene resins a.. |
|||
Melt Flow | 1.7 g/10 min | 1.7 g/10 min | ASTM D1238 |
Hyosung Topilene J340 PP J340 Injection Impact CopolymerApplications:CrateContainerBatter caseCharacteristics:High ImpactInformation provided by Hyosung Corporation |
|||
Melt Flow | 1.7 g/10 min @Load 5.00 kg, Temperature 200 °C |
1.7 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
IRPC Polimaxx Polene GP110 Polystyrene APPLICATIONS: EXTRUSION SHEET, HOUSEHOLD PRODUCTS VACUUM SHEET , FOOD PACKAGING, TOY, SANITARY WARE, etc. |
|||
Melt Flow | 1.7 g/10 min | 1.7 g/10 min | ISO 1133 |
Lucite International Diakon® CLH952L Acrylic Polymer Information provided by Lucite International |
|||
Melt Flow | 1.7 g/10 min | 1.7 g/10 min | ISO 1133 |
Lucite International Diakon® CLH952LX Acrylic Polymer Information provided by Lucite International |
|||
Melt Flow | 1.7 g/10 min | 1.7 g/10 min | ASTM D1238G |
Hannam Chemical Hanalac HU-600 ABS |
|||
Melt Flow | 1.7 g/10 min @Load 2.16 kg, Temperature 230 °C |
1.7 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
Ineos R01A-01 Polypropylene Copolymer, Antistatic An antistated polypropylene random copolymer produced by Ineos utilizing unique catalyst technology. It is designed for blowmolding and extrusion applications and exhibits good stiffness and improv.. |
|||
Melt Flow | 1.7 g/10 min @Load 5.00 kg, Temperature 200 °C |
1.7 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
Samsung Cheil Industries Starex® SD-0150U ABS, Unreinforced Information provided by Samsung Cheil Industries. |
|||
Melt Flow | 1.7 g/10 min @Load 5.00 kg, Temperature 200 °C |
1.7 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
Samsung Cheil Industries Starex® SD-0170 F ABS, Unreinforced Information provided by Samsung Cheil Industries. |
|||
Melt Flow | 1.7 g/10 min @Load 5.00 kg, Temperature 200 °C |
1.7 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
Samsung Cheil Industries Starex® SD-0170 F ABS, Unreinforced Information provided by Samsung Cheil Industries. |
|||
Melt Flow | 1.7 g/10 min | 1.7 g/10 min | ASTM D1238/E |
Borealis Borstar® HE6067 Black Bimodal HD Polyethylene Compound for Jacketing of Communication and Power Cables Borstar HE6067 is a black, bimodal, co-polymer high density polyethylene (HDPE) compound produced according to the bimodal Borstar process. It is characterized by its balanced properties important .. |
|||
Melt Flow | 1.7 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.7 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
Westlake EM800AA Low Density Polyethylene WESTLAKE low-density polyethylene EM800 is a general-purpose low-density formulation used for injection molding applications that require good stress-crack resistance.Application/UsesCosmetics/perso.. |
|||
Melt Flow | 1.7 g/10 min @Load 2.16 kg, Temperature 230 °C |
1.7 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
Total PPH 3060 Polypropylene, Homopolymer ATOFINA Polypropylene PPH 3060 is homopolymer.ApplicationATOFINA Polypropylene PPH 3060 is characterized by a low fluidity for continuous extrusion of strapping, rope fibers and high tenacity tapes .. |
|||
Melt Flow | 1.7 g/10 min @Load 5.00 kg, Temperature 235 °C |
1.7 g/10 min @Load 11.0 lb, Temperature 455 °F |
after drying; ISO 1133 |
Arkema Group Orgalloy® LT 4060 Polyamide Alloy Polyamide Alloy, Flexible gradeTubes / Mandrels / Profiles / CablesInformation provided by Arkema Group |
|||
Melt Flow | 1.7 g/10 min @Load 2.16 kg, Temperature 230 °C |
1.7 g/10 min @Load 4.76 lb, Temperature 446 °F |
|
BASF Novolen® 1102 G Polypropylene Data was collected by ISO methods and provided by BASF. |
|||
Melt Flow | 1.7 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.7 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
ExxonMobil Escorene™ FL 00218 Ethylene Vinyl Acetate Copolymer (European Grade) Product Description: FL 00218 is a copolymer of ethylene and vinyl acetate. Processing Conditions: Processing temperatures above 240°C (464°F) may cause resin degradation. Machines should always b.. |
|||
Melt Flow | 1.7 g/10 min @Load 3.80 kg, Temperature 230 °C |
1.7 g/10 min @Load 8.38 lb, Temperature 446 °F |
|
Arkema Group Oroglas® MI-7T Acrylic
(discontinued **) OROGLAS MI-7T is a medium impact grade combining excellent thermal resistance with good impact performance.Key features : impact resistance: up to 7 times more impact-resistant than standard acr.. |