Polyram RamTal PMH2017 Polyacetal Homopolymer for Injection Molding
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Homopolymer, Unreinforced |
| Manufacturer | Polyram |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram RamTal PMH2017 Polyacetal Homopolymer for Injection Molding.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
General purpose polyacetal homopolymer for injection molding applications, MFI 1.7.Information provided by Polyram.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.42 g/cc | 0.0513 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.018 - 0.022 cm/cm | 0.018 - 0.022 in/in | ISO 2577 |
| Melt Flow | 1.7 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.7 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 72.0 MPa | 10400 psi | ISO 527 |
| Elongation at Break | 40 % | 40 % | ISO 527 |
| Tensile Modulus | 3.00 GPa | 435 ksi | ISO 527 |
| Charpy Impact, Notched | 0.900 J/cm² | 4.28 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 165 °C | 329 °F | ISO 11357 |
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | ISO 75 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
Users viewing this material also viewed the following:
- Plastcom PLASTAMID® 6 GF 30 002 TS PA6 reinforced with glass fiber, heat stabilized
- PolyMirae Moplen HP740T Injection Molding (Thin Wall) Grade Polypropylene
- Ineos H20Z-01 Polypropylene Homopolymer (discontinued **)
- Karina 700D40/356-AT Green PVC Compound
- Gromax CFG45-PN11N1 Nylon 6 46% Glass Filled (Dry)
- Westlake Plastics Kynar® PVDF CN-F Polyvinylidene Fluoride (conductive)
- A. Schulman POLYBATCH™ Blue 4300 Concentrate Based In Polyethylene
- UBE UBESTA® 3030U Nylon 12 (After Toluene for 1000 hours)
- Formosa Plastics Formolene® HP4401 Pipe HDPE
- ExxonMobil LD 144.50 Packaging Film Resin
Copyright © lookpolymers.com All Rights Reserved