Plastcom PLASTAMID® 6HM PA6

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced
Manufacturer Plastcom spol. s r.o.
Trade Name PLASTAMID®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Plastcom PLASTAMID® 6HM PA6.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PA 6 for compounding, basic type, modified for general use, used in the automotive, electrical, engineering and consumer goods industry. Delivered in natural color - white (contains TiO2)Information Provided by Plastcom spol. s r.o.
Physical Properties Metric English Comments
Density 1.16 g/cc
0.0419 lb/in³
STN EN ISO 1183-1
Linear Mold Shrinkage 0.018 cm/cm
0.018 in/in
STN EN ISO 294-4
Linear Mold Shrinkage, Transverse 0.0183 cm/cm
0.0183 in/in
STN EN ISO 294-4
Melt Flow 6.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
6.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
STN EN ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 65.0 MPa
9430 psi
STN EN ISO 527-2
Elongation at Break 3.0 %
3.0 %
STN EN ISO 527-2
Tensile Modulus 2.40 GPa
348 ksi
STN EN ISO 527-2
Flexural Strength 85.0 MPa
12300 psi
STN EN ISO 178
Flexural Modulus 2.30 GPa
334 ksi
STN EN ISO 178
Charpy Impact Unnotched 7.00 J/cm²

@Temperature -20.0 °C
33.3 ft-lb/in²

@Temperature -4.00 °F
STN EN ISO 179
13.5 J/cm²

@Temperature 23.0 °C
64.2 ft-lb/in²

@Temperature 73.4 °F
STN EN ISO 179
Charpy Impact, Notched 0.250 J/cm²

@Temperature -20.0 °C
1.19 ft-lb/in²

@Temperature -4.00 °F
STN EN ISO 179
0.400 J/cm²

@Temperature 23.0 °C
1.90 ft-lb/in²

@Temperature 73.4 °F
STN EN ISO 179
Thermal Properties Metric English Comments
Melting Point 220 °C
428 °F
STN EN 11357-1
Deflection Temperature at 1.8 MPa (264 psi) 50.0 °C
122 °F
STN EN ISO 75-2 (A)
Vicat Softening Point 190 °C
374 °F
STN EN ISO 306
Processing Properties Metric English Comments
Melt Temperature 250 - 270 °C
482 - 518 °F
Mold Temperature 60.0 - 80.0 °C
140 - 176 °F
Drying Temperature 80.0 °C

@Time 14400 sec
176 °F

@Time 4.00 hour
Moisture Content 0.15 %
0.15 %
STN EN ISO 3344
Injection Pressure 70.0 - 120 MPa
10200 - 17400 psi