Clariant Renol PBT1100 Black Polybutylene Terephthalate, General Purpose

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer Clariant
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Clariant Renol PBT1100 Black Polybutylene Terephthalate, General Purpose.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Data provided by Clariant Masterbatches
Physical Properties Metric English Comments
Specific Gravity 1.31 g/cc
1.31 g/cc
ASTM D792
Water Absorption 0.080 %

@Time 86400 sec
0.080 %

@Time 24.0 hour
ASTM D570
Linear Mold Shrinkage 0.018 cm/cm
0.018 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength, Yield 58.6 MPa
8500 psi
ASTM D638
Elongation at Break 50 %
50 %
ASTM D638
Flexural Yield Strength 75.8 MPa
11000 psi
ASTM D790
Flexural Modulus 2.28 GPa
330 ksi
ASTM D790
Izod Impact, Notched 0.534 J/cm

@Temperature 22.8 °C
1.00 ft-lb/in

@Temperature 73.0 °F
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 154 °C
310 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 67.2 °C
153 °F
ASTM D648
Flammability, UL94 HB
HB
1/32 - 1/4 in
Processing Properties Metric English Comments
Rear Barrel Temperature 221 - 249 °C
430 - 480 °F
Middle Barrel Temperature 227 - 254 °C
440 - 490 °F
Front Barrel Temperature 232 - 260 °C
450 - 500 °F
Nozzle Temperature 238 - 266 °C
460 - 510 °F
Melt Temperature 232 - 246 °C
450 - 475 °F
Mold Temperature 65.6 - 82.2 °C
150 - 180 °F
Injection Pressure 4.96 - 8.27 MPa
720 - 1200 psi
Secondary
8.27 - 13.8 MPa
1200 - 2000 psi
Initial
Back Pressure 0.345 - 0.689 MPa
50.0 - 100 psi
Shot Size 30 - 80 %
30 - 80 %
Screw Speed 25 - 80 rpm
25 - 80 rpm