Wellman Wellamid® GB1430-N 33% Glass Bubble Filled, Low Density Nylon 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass Bead Filled |
| Manufacturer | Wellman Engineering Resins |
| Trade Name | Wellamid® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Wellman Wellamid® GB1430-N 33% Glass Bubble Filled, Low Density Nylon 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Glass Bubble Filled, Low Density Nylon 66Information provided by Wellman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.900 g/cc | 0.0325 lb/in³ | ISO 1183-87 |
| Filler Content | 33 % | 33 % | |
| Linear Mold Shrinkage, Flow | 0.0075 - 0.0105 cm/cm | 0.0075 - 0.0105 in/in | ISO DIS 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0075 - 0.0105 cm/cm | 0.0075 - 0.0105 in/in | ISO DIS 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 65.0 MPa | 9430 psi | ISO 527-93 |
| Elongation at Break | 4.5 % | 4.5 % | ISO 527-93 |
| Flexural Strength | 100 MPa | 14500 psi | ISO 178-93 |
| Flexural Modulus | 3.80 GPa | 551 ksi | ISO 178-93 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² | 1.43 ft-lb/in² | ISO 180-93 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 260 °C | 500 °F | ISO 3146 |
| Deflection Temperature at 1.8 MPa (264 psi) | 140 °C | 284 °F | ISO 75-93 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 282 - 310 °C | 540 - 590 °F | |
| Middle Barrel Temperature | 277 - 304 °C | 530 - 580 °F | |
| Front Barrel Temperature | 271 - 299 °C | 520 - 570 °F | |
| Nozzle Temperature | 271 - 304 °C | 520 - 580 °F | |
| Melt Temperature | 271 - 304 °C | 520 - 580 °F | |
| Mold Temperature | 71.1 - 93.3 °C | 160 - 200 °F | |
| Drying Temperature | 79.4 °C | 175 °F | Opened bags and gaylord boxes |
| Dry Time | 2 - 4 hour | 2 - 4 hour | Opened bags and gaylord boxes |
| Moisture Content | 0.050 - 0.20 % | 0.050 - 0.20 % | During molding to prevent hydrolytic degradation |
| <= 0.20 % | <= 0.20 % | In shipping bags, ready to mold | |
| Injection Pressure | 34.5 - 138 MPa | 5000 - 20000 psi | |
| Back Pressure | 0.345 MPa | 50.0 psi | |
| Screw Speed | 30 - 120 rpm | 30 - 120 rpm |
Users viewing this material also viewed the following:
- Hong Kun Group 2-Bromo-4-fluorobenzoic Acid Pharmaceutical Intermediate
- Michelman® Michem® Emulsion 62330 Anionic paraffin/polyethylene emulsion
- Isoflon Tisoflon® 14S Silicone Coated Glass Fabric
- Heraeus Cleviosâ„¢ P T2 Conductive Sulfonate Polymer for Antistatic Coatings
- SABIC Innovative Plastics LNP STAT-KON KD000 Acetal Copolymer (Asia Pacific)
- Techmer ES HiFill® PA6 GF60 HS L BK 60% Glass Filled
- ThyssenKrupp Ck60 Saw Steel, Four-High Mill Plate
- ThyssenKrupp PAS 355 Structural Steel for Cold Forming
- AK Steel ASTM A 715 Class 2 Formable, Grade 50F Hot Rolled Carbon Steel, Medium/High Strength Low Alloy (HSLA)
Copyright © lookpolymers.com All Rights Reserved