| Category | Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Pipe Grade |
| Manufacturer | Iran Petrochemical Commercial Co. (PCC) |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Iran Petrochemical (PCC) EX 3 – 100S HM CRP 100 N High Density Polyethylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
EX3-100S is a high density polyethylene with 1-Butene as co monomer. It is natural, outstanding ESCR, high impact strength, outstanding hydrostatic strength for PE 100 class.Applications: pipe extrusion PE 100 class, industrial and pressure pipe , gas pipe, drinking water pipe, relining , fittings.Information provided by Iran Petrochemical Commercial Co.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.948 g/cc | 0.0342 lb/in³ | ISO 1183 |
| Environmental Stress Crack Resistance | 400 hour @Pressure 4.00 MPa |
400 hour @Pressure 580 psi |
ISO CD 16770 |
| Melt Flow | 0.22 g/10 min @Load 5.00 kg, Temperature 190 °C |
0.22 g/10 min @Load 11.0 lb, Temperature 374 °F |
ISO 1133 |
| 6.2 g/10 min @Load 21.6 kg, Temperature 190 °C |
6.2 g/10 min @Load 47.6 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 62 | 62 | ISO 868 |
| Tensile Stress | 36.0 MPa | 5220 psi | at Break; ISO 527 |
| Tensile Strength, Yield | 23.0 MPa | 3340 psi | ISO 527 |
| Elongation at Break | >= 1000 % | >= 1000 % | ISO 527 |
| Elongation at Yield | 10 % | 10 % | ISO 527 |
| Tensile Modulus | 0.850 GPa | 123 ksi | ISO 527 |
| Charpy Impact, Notched | 2.50 J/cm² | 11.9 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Softening Point | 74.0 °C | 165 °F | ISO 306 |
| Brittleness Temperature | >= -80.0 °C | >= -112 °F | ASTM D746-72 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 190 - 220 °C | 374 - 428 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Flexural Creep Modulus (MPa) | 1050 | 4 point, 1 min; DIN 19537-2 |
Users viewing this material also viewed the following:
- Solvay Specialty Polymers Cogegum® AFR/765 Polyolefin, Unspecified (Unverified Data**)
- Kazanorgsintez Propylene
- LTL Color Compounds ColorRxâ„¢ PP2-1001A Antimicrobial Polypropylene Random Copolymer
- Borealis Borstar® HE3470-LS Black HDPE Compound for Pressure Pipes
- DSM Akulon® F223-D (Dry) Low/Medium Viscosity Nylon 6 (North America)
- Arkema Group Pebax® 6333 Polyether Block Amide (PEBA)
- Ascend Performance Materials Vydyne® 22HSP NT Nylon 66, Conditioned
- Parker Chomerics CHO-BOND 1053, Part B Silicone Rubber Mixture
- LG Chemical HF350U ABS, High Flow
- GEHR Plastics PPE Polyphenylene Ether (discontinued **)
Copyright © lookpolymers.com All Rights Reserved