Toyobo GLAMIDE® TY-102ND Nylon/Elastomer
| Category | Polymer , Thermoplastic , Nylon |
| Manufacturer | Toyobo |
| Trade Name | GLAMIDE® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Toyobo GLAMIDE® TY-102ND Nylon/Elastomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing and a specific grade approved as UL94V-0 class is provided, and it exhibits excellent chemical resistance and oil resistance. Grade TY-102ND is a super tough, non-reinforced alloy of nylon and elastomer.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.09 g/cc | 1.09 g/cc | Absolute Drying; ASTM-D792 |
| Water Absorption | 1.0 % | 1.0 % | Absolute Drying; ASTM-D570 |
| Moisture Absorption at Equilibrium | 2.9 % | 2.9 % | Absolute Drying; ASTM-D570 |
| Linear Mold Shrinkage | 0.0070 - 0.010 cm/cm @Thickness 1.00 mm |
0.0070 - 0.010 in/in @Thickness 0.0394 in |
Absolute Drying |
| 0.015 - 0.020 cm/cm @Thickness 3.00 mm |
0.015 - 0.020 in/in @Thickness 0.118 in |
Absolute Drying |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 102 | 102 | Absolute Drying; ASTM-D785 |
| Tensile Strength, Ultimate | 15.0 MPa @Temperature 80.0 °C |
2180 psi @Temperature 176 °F |
Practical Use (Water Absorption 2.9%); ASTM-D638 |
| 21.0 MPa @Temperature 80.0 °C |
3050 psi @Temperature 176 °F |
Absolute Drying; ASTM-D638 | |
| 27.0 MPa @Temperature 23.0 °C |
3920 psi @Temperature 73.4 °F |
Practical Use (Water Absorption 2.9%); ASTM-D638 | |
| 50.0 MPa @Temperature 23.0 °C |
7250 psi @Temperature 73.4 °F |
Absolute Drying; ASTM-D638 | |
| 74.0 MPa @Temperature -40.0 °C |
10700 psi @Temperature -40.0 °F |
Practical Use (Water Absorption 2.9%); ASTM-D638 | |
| 85.0 MPa @Temperature -40.0 °C |
12300 psi @Temperature -40.0 °F |
Absolute Drying; ASTM-D638 | |
| Elongation at Break | >= 200 % | >= 200 % | ASTM-D638 |
| Flexural Strength | 17.0 MPa @Temperature 80.0 °C |
2470 psi @Temperature 176 °F |
Practical Use (Water Absorption 2.9%); ASTM-D790 |
| 27.0 MPa @Temperature 80.0 °C |
3920 psi @Temperature 176 °F |
Absolute Drying; ASTM-D790 | |
| 35.0 MPa @Temperature 23.0 °C |
5080 psi @Temperature 73.4 °F |
Practical Use (Water Absorption 2.9%); ASTM-D790 | |
| 75.0 MPa @Temperature 23.0 °C |
10900 psi @Temperature 73.4 °F |
Absolute Drying; ASTM-D790 | |
| 87.0 MPa @Temperature -40.0 °C |
12600 psi @Temperature -40.0 °F |
Practical Use (Water Absorption 2.9%); ASTM-D790 | |
| 94.0 MPa @Temperature -40.0 °C |
13600 psi @Temperature -40.0 °F |
Absolute Drying; ASTM-D790 | |
| Flexural Modulus | 0.200 GPa @Temperature 80.0 °C |
29.0 ksi @Temperature 176 °F |
Practical Use (Water Absorption 2.9%); ASTM-D790 |
| 0.600 GPa @Temperature 80.0 °C |
87.0 ksi @Temperature 176 °F |
Absolute Drying; ASTM-D790 | |
| 0.800 GPa @Temperature 23.0 °C |
116 ksi @Temperature 73.4 °F |
Practical Use (Water Absorption 2.9%); ASTM-D790 | |
| 2.00 GPa @Temperature 23.0 °C |
290 ksi @Temperature 73.4 °F |
Absolute Drying; ASTM-D790 | |
| 2.30 GPa @Temperature -40.0 °C |
334 ksi @Temperature -40.0 °F |
Practical Use (Water Absorption 2.9%); ASTM-D790 | |
| 2.70 GPa @Temperature -40.0 °C |
392 ksi @Temperature -40.0 °F |
Absolute Drying; ASTM-D790 | |
| Izod Impact, Notched | 1.50 J/cm @Temperature -40.0 °C |
2.81 ft-lb/in @Temperature -40.0 °F |
Absolute Drying; ASTM-D256 |
| 1.80 J/cm @Temperature -40.0 °C |
3.37 ft-lb/in @Temperature -40.0 °F |
Practical Use (Water Absorption 2.9%); ASTM-D256 | |
| 3.10 J/cm @Temperature 23.0 °C |
5.81 ft-lb/in @Temperature 73.4 °F |
Absolute Drying; ASTM-D256 | |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
Practical Use (Water Absorption 2.9%); ASTM-D256 | |
| Taber Abrasion, mg/1000 Cycles | 8.0 | 8.0 | CS-17, Absolute Drying; ASTM-D1044 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 87.0 µm/m-°C | 48.3 µin/in-°F | Absolute Drying; ASTM-D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 150 °C | 302 °F | Absolute Drying; ASTM-D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 58.0 °C | 136 °F | Absolute Drying; ASTM-D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+9 ohm-cm | 1.00e+9 ohm-cm | Practical Use (Water Absorption 2.9%); ASTM-D257 |
| 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | Absolute Drying; ASTM-D257 | |
| Dielectric Strength | 14.0 kV/mm @Thickness 2.00 mm |
356 kV/in @Thickness 0.0787 in |
Practical Use (Water Absorption 2.9%); ASTM-D149 |
| 18.0 kV/mm @Thickness 2.00 mm |
457 kV/in @Thickness 0.0787 in |
Absolute Drying; ASTM-D149 | |
| Arc Resistance | 108 sec | 108 sec | Practical Use (Water Absorption 2.9%); ASTM-D495 |
| 125 sec | 125 sec | Absolute Drying; ASTM-D495 | |
| Comparative Tracking Index | >= 600 V | >= 600 V | IEC Method |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 245 - 285 °C | 473 - 545 °F | |
| Mold Temperature | 50.0 - 80.0 °C | 122 - 176 °F | |
| Injection Pressure | 40.0 - 80.0 MPa | 5800 - 11600 psi |
Users viewing this material also viewed the following:
- MV Labs ND700 Nd(NO3)3·6H2O Neodymium nitrate hydrate
- Ineos ABS Lustran® 448
- Momentive Performance Materials Siloprenâ„¢ LSR 3386/40 Liquid Silicone Rubber - Self-Lubricating / Low Compression Set
- Shinil Chemical SHINSTRA PA-66 Devlop Structural Polymer Window Strip
- Taiwan PU Corporation TPUI-T64D Transparent Grade, Injection Molding Polyester Base TPU
- ChevronTexaco HDAX® ISO 100 NG Screw Compressor Oil
- DuPont Performance Polymers Crastin® PC164 NC010 Polybutylene Terephthalate (PBT) (Unverified Data**)
- Ashley Polymers Ashlene® E126WO PET Polyester, 30% Glass Reinforced
- Austin Novel Materials Texalan® 385A Polyester-based TPU
- Bhansali Engineering Abstron IM17A TT ABS Injection Molding Grade
Copyright © lookpolymers.com All Rights Reserved