- Quadrant EPP Duratron® U2100 OEI Extruded 10% Glass Reinforced Polyetherimide
Quadrant EPP Duratron® U2100 OEI Extruded 10% Glass Reinforced Polyetherimide
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) , Polyetherimide (PEI), 20% Glass Fiber |
| Manufacturer | Quadrant Engineering Plastics Products |
| Trade Name | Duratron® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Quadrant EPP Duratron® U2100 OEI Extruded 10% Glass Reinforced Polyetherimide.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.34 g/cc @Temperature 22.8 °C |
1.34 g/cc @Temperature 73.0 °F |
ASTM D792 |
| Water Absorption | 0.20 % | 0.20 % | IMMERSION; 24HRS.; ASTM D570 2 |
| Water Absorption at Saturation | 1.0 % | 1.0 % | ASTM D570 2 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 131 MPa @Temperature 22.8 °C |
19000 psi @Temperature 73.0 °F |
ASTM D638 |
| Elongation at Break | 5.0 % | 5.0 % | ASTM D638 |
| Tensile Modulus | 4.14 GPa @Temperature 22.8 °C |
600 ksi @Temperature 73.0 °F |
ASTM D638 |
| Flexural Strength | 176 MPa @Temperature 22.8 °C |
25500 psi @Temperature 73.0 °F |
ASTM D790 |
| Compressive Strength | 179 MPa @Strain 10.0 %, Temperature 22.8 °C |
26000 psi @Strain 10.0 %, Temperature 73.0 °F |
ASTM D695 |
| Compressive Modulus | 2.76 GPa @Temperature 22.8 °C |
400 ksi @Temperature 73.0 °F |
ASTM D695 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Glass Transition Temp, Tg | 210 °C | 410 °F | ASTM D3418 |
Users viewing this material also viewed the following:
- Overview of materials for Acrylonitrile Butadiene Styrene (ABS), Extruded
- A. Schulman POLYBATCH™ White 8350 AP Concentrate Based In LDPE
- DSM Akulon® K224-LGM35 (Cond.) 15% Glass Reinforced, 25% Mineral Reinforced Nylon 6 (North America)
- EMS-Griltech Griltex® D 1500A Copolyamide Hotmelt Adhesive (Technical Applications)
- BASF Ultramid® A3X3G5 BK 23187 25% Glass Filled PA66 FR (Conditioned)
- BASF Ultrason S 2010 G4 20% Glass Filled PSU
- Arkema Group Rilsan® ASR 30 Nylon 12, 30% Carbon Fiber Filled (Dry)
- Bulk Molding Compounds BMC 1100 Corelyn Glass Fiber Reinforced Polyester Compound
- Haynes Hastelloy® C-2000® Bar, Annealed at 2100°F (1149°C)
Copyright © lookpolymers.com All Rights Reserved