- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 58.0 °C
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 58.0 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 58.0 °C | 136 °F | ISO 75, ASTM D648 |
| Nilit Nilitop BT FR C3 Unfilled, Flame Retardant PBT Description: Nilitop BT FR C3 is an unfilled, flame retardant PBT with halogens. The flame retardant does not contain PBB and PBDE, so it is compliant with the WEEE directive.Key characteristics: Go.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 58.0 °C | 136 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYfill PPH TS15010 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 58.0 °C | 136 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYfill PP EIP8020F Polypropylene/EPDM, Mineral Reinforced Information provided by Polykemi AB |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 58.0 °C @Thickness 6.40 mm |
136 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| LG Chemical Lupox® GP1000S PBT Description: Injection Molding, PBT, General PurposeApplication: Automotive (Connector)CAS No. 24968-12-5Information provided by LG Chemical |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 58.0 °C | 136 °F | 80*10*4mm, Cut; ISO 75-1&2 |
| SABIC Innovative Plastics SABIC PPCOMPOUND 9712 PP SABIC® PPcompound 9712 is a mineral filled, impact modified polypropylene TPO. This material combines high impact resistance, scratch resistance, and heat stability with interior automotive UV st.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 58.0 °C @Thickness 3.20 mm |
136 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP WL003 PBT LNP* LUBRICOMP* WL003 is a compound based on PBT resin containing 15% PTFE. Added feature of th is grade is: Wear Resistant. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 58.0 °C @Thickness 3.20 mm |
136 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRILOY RX05497 PA 66 LNP LUBRILOY* RX05497 is a compound based on Nylon 66 resin containing Proprietary Lubricant. Added feature of this material is: Wear Resistant. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 58.0 °C @Thickness 3.20 mm |
136 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRILOY RX05497 PA 66 (Asia Pacific) LNP LUBRILOY* RX05497 is a compound based on Nylon 66 resin containing Proprietary Lubricant. Added features of this material include: Internally Lubricated. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 58.0 °C | 136 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| SABIC Innovative Plastics Valox® HX312C PBT (Europe-Africa-Middle East) Unreinforced PBT with release. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI), food contact compliant. EtO and stea.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 58.0 °C | 136 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP STAT-KON MD000AP PP LNP* STAT-KON* MD000AP is a compound based on Polypropylene containing Carbon Powder. Added features of this grade include: Electrically Conductive, Exceptional Processing. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 58.0 °C | 136 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP Thermocomp MX05038 PP (Europe-Africa-Middle East) Polypropylene compound, containing miniral. Added features include High ImpactThis data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 58.0 °C | 136 °F | Unannealed; ISO 75 |
| Styron INSPIREâ„¢ TF1500 ESU Polypropylene Talc filled, high impact PP compound. INSPIREâ„¢ TF1500 ESU has been developed for aesthetic automotive applications, with good scratch resistance and UV light stabilization.Information provided.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 58.0 °C | 136 °F | ISO 75 |
| Unipetrol PP MONSTEN® GB 506 Polypropylene Impact Copolymer Applications include injection molding and thermoforming. Basic stabilization. Impact copolymer.Information provided by Unipetrol RPA |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 58.0 °C | 136 °F | ISO 75 |
| Unipetrol PP MONSTEN® NB 112 Polypropylene Homopolymer Applications include injection molding and fibers. Basic and anti-gasfading stabilization. Homopolymer.Information provided by Unipetrol RPA |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 58.0 °C | 136 °F | ISO 75 |
| Unipetrol PP MONSTEN® TB 002 Polypropylene Homopolymer Applications include injection molding, extrusion, tapes, and thermoforming. Basic stabilization. Homopolymer.Information provided by Unipetrol RPA |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 58.0 °C | 136 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 1697HU High Flow Fortified Polypropylene DescriptionPolyfort® FPP 1697HU is a high flow fortified polypropylene with high temperature dimensioned stability. It is stabilized for UV exposure and available in matched automotive color.Infor.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 58.0 °C | 136 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 1697HU High Flow Fortified Polypropylene DescriptionPolyfort® FPP 1697HU is a high flow fortified polypropylene with high temperature dimensioned stability. It is stabilized for UV exposure and available in matched automotive color.Infor.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 58.0 °C | 136 °F | 120°C per hour; ISO 75-2 |
| Total PPH 10012 Polypropylene, Homopolymer ATOFINA Polypropylene PPH 10012 is a nucleated and antistatic homopolymer polypropylene obtained by controlled rheology.ApplicationPPH 10012 is intended for high speed injection molding of household.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 58.0 °C | 136 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 1697HU High Flow Fortified Polypropylene DescriptionPolyfort® FPP 1697HU is a high flow fortified polypropylene with high temperature dimensioned stability. It is stabilized for UV exposure and available in matched automotive color.Infor.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 58.0 °C | 136 °F | 120°C/hr; ASTM D 648 |
| Cossa Polimeri ESTAPROP K 1280 T8 Polypropylene, 40% Mineral Filled PP copolymer 40% mineral fillerExcellent physical and mechanical characteristics, good surface appearanceInformation provided by Cossa Polimeri S.r.l. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 58.0 °C | 136 °F | ISO 75-2/AF |
| Addiplast Addilene J 120 M10 Polypropylene Copolymer Low fluidity for extrusion or injectionInformation provided by Addiplast. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 58.0 °C | 136 °F | |
| BASF Novolen® 1102 G Polypropylene Data was collected by ISO methods and provided by BASF. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 58.0 °C | 136 °F | |
| Arkema Group Appryl® CZN 0525 Polypropylene, 25% Talc Filled Compound of a PP copolymer modified with EPR and 25% talc. This grade has been specially developed for interior trim applications, that required an excellent impact test associated with a high modul.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 58.0 °C | 136 °F | ISO 75-2/AF |
| Addiplast Addilene PMD 50306 Polypropylene Copolymer Mineral reinforced, improved scratch resistanceInformation provided by Addiplast. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 58.0 °C | 136 °F | Unannealed; ISO 75-2/A |
| Ascend Performance Materials Vydyne® 41H BK03 Nylon 66, Impact Modified, DAM Vydyne® 41H BK03 is a general-purpose, impact-modified PA66 resin. Available in black, it is heat-stabilized for improved resistance to elevated temperatures. The heat stabilization package for Vyd.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 58.0 °C | 136 °F | Unannealed; ISO 75-2/A |
| Ascend Performance Materials Vydyne® 41H Nylon 66, Impact Modified, DAM Vydyne® 41H is a general-purpose, impact-modified PA66 resin. Available in natural, it is heat-stabilized for improved resistance to elevated temperatures. The heat stabilization package for Vydyne.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 58.0 °C | 136 °F | Unannealed; ISO 75-2/A |
| Ascend Performance Materials Vydyne® 41 NT Nylon 66, Impact Modified, DAM Vydyne® 41 NT is general-purpose, impact-modified PA66 resin. Available in natural, it is recognized for all the processing and property advantages inherent to PA66 with the addition of improved im.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 58.0 °C | 136 °F | ASTM D648 |
| Albis Plastics Cellulose Acetate Butyrate B9004 (Odor Mask Added), 20% Plasticizer
(discontinued **) Amorphous Cellulose Acetate Butyrate (CAB)Characteristics: Dimensional Stability, Weatherability and Low Temp Impact StrengthApplications: Pens, Ski Goggles, Auto Trim, Skylights, Tool Handles and T.. |
|||
Copyright © lookpolymers.com All Rights Reserved