Teknor Apex Chemlon® 282 Nylon 6, Non-halogenated

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced, Flame Retardant
Manufacturer Teknor Apex Company
Trade Name Chemlon®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Teknor Apex Chemlon® 282 Nylon 6, Non-halogenated.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Features: Flame Retardant; General Purpose; Halogen-free; U.L. 94 V-O at 0.63 mm; ColorableProcessing Method: Injection Molding Forms: Pellets Additive: Flame RetardantInformation Provided by Teknor Apex
Physical Properties Metric English Comments
Specific Gravity 1.18 g/cc
1.18 g/cc
ASTM D792
Linear Mold Shrinkage 0.0090 - 0.0147 cm/cm
0.0090 - 0.0147 in/in
ASTM D955
Melt Flow 13.0 g/10 min

@Load 5.00 kg,
Temperature 235 °C
 13.0 g/10 min

@Load 11.0 lb,
Temperature 455 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 120
120
ASTM D785
Tensile Strength 72.4 MPa
10500 psi
ASTM D638
Elongation at Break 6.0 %
6.0 %
ASTM D638
Elongation at Yield 6.0 %
6.0 %
ASTM D638
Flexural Strength 96.5 MPa
14000 psi
ASTM D790
Flexural Modulus 3.14 GPa
455 ksi
ASTM D790
Izod Impact, Notched 0.534 J/cm

@Temperature 22.8 °C
 1.00 ft-lb/in

@Temperature 73.0 °F
 ASTM D256
Thermal Properties Metric English Comments
Melting Point 216 °C
420 °F
DSC
Deflection Temperature at 1.8 MPa (264 psi) 79.4 °C
175 °F
Unannealed; ASTM D648
UL RTI, Electrical 130 °C

@Thickness 0.810 mm
 266 °F

@Thickness 0.0319 in
 UL 746
130 °C

@Thickness 1.50 mm
 266 °F

@Thickness 0.0590 in
 UL 746
130 °C

@Thickness 3.00 mm
 266 °F

@Thickness 0.118 in
 UL 746
UL RTI, Mechanical with Impact 105 °C

@Thickness 0.810 mm
 221 °F

@Thickness 0.0319 in
 UL 746
105 °C

@Thickness 1.50 mm
 221 °F

@Thickness 0.0590 in
 UL 746
105 °C

@Thickness 3.00 mm
 221 °F

@Thickness 0.118 in
 UL 746
UL RTI, Mechanical without Impact 120 °C

@Thickness 0.810 mm
 248 °F

@Thickness 0.0319 in
 UL 746
120 °C

@Thickness 1.50 mm
 248 °F

@Thickness 0.0590 in
 UL 746
120 °C

@Thickness 3.00 mm
 248 °F

@Thickness 0.118 in
 UL 746
Flammability, UL94 V-0

@Thickness 0.630 mm
 V-0

@Thickness 0.0248 in
Oxygen Index 32 %
32 %
ASTM D2863
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
ASTM D257
Dielectric Strength 15.0 kV/mm

@Thickness 3.00 mm
 380 kV/in

@Thickness 0.118 in
 ASTM D149
Comparative Tracking Index 600 V
600 V
UL 746
Processing Properties Metric English Comments
Rear Barrel Temperature 218 - 235 °C
425 - 455 °F
Middle Barrel Temperature 229 - 252 °C
445 - 485 °F
Front Barrel Temperature 241 - 260 °C
465 - 500 °F
Nozzle Temperature 241 - 260 °C
465 - 500 °F
Melt Temperature 241 - 260 °C
465 - 500 °F
Processing Temperature
Drying Temperature 79.4 °C
175 °F
Descriptive Properties Value Comments
Suggested Moisture, max 0.2
Suggested Regrind, max 25
Users viewing this material also viewed the following: