Multibase Multi-Pro® 5002 CU Natural Polypropylene
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | Multibase |
| Trade Name | Multi-Pro® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Multibase Multi-Pro® 5002 CU Natural Polypropylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Forms:PelletsProcessing Methods:Injection MoldingFeatures:Gloss, LowInformation provided by Multibase
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.32 g/cc | 0.0477 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0070 - 0.0090 cm/cm | 0.0070 - 0.0090 in/in | ASTM D955 |
| Melt Flow | 2.25 g/10 min @Load 2.16 kg, Temperature 230 °C |
2.25 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 19.3 MPa | 2800 psi | ASTM D638 |
| Elongation at Break | 900 % | 900 % | ASTM D638 |
| Flexural Strength | 31.0 MPa | 4500 psi | ASTM D790 |
| Flexural Modulus | 2.38 GPa | 345 ksi | Method I (3 point load), Procedure B); ASTM D790 |
| Izod Impact, Notched | NB | NB | 73°F; ASTM D256 |
| Gardner Impact | 22.60 J | 16.67 ft-lb | ASTM D3029 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 120 °C | 248 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | Unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- LyondellBasell Hostacomâ„¢ TKS708D Thermoplastic Polyolefin Elastomer
- Solvay Specialty Polymers Torlon® 4275 Polyamide-imide (PAI)
- SABIC Innovative Plastics LNP THERMOCOMP JF004E PES (Asia Pacific)
- Ensinger Tecapeek® XP-100 Compression Molded PEEK Compound, Bearing Grade Material with 10% Graphite, 10% PTFE, and 10% Carbon Fiber
- ExxonMobil Santoprene® 9101-80E Thermoplastic Vulcanizate - Co-extrusion
- Hippe EP PC 301 Woven Polyester Cloth Reinforced Epoxy Resin - Sheet
- DuPont Teijin Films Mylar® ADS Polyester Film, 200 Gauge
- Von Roll Isola IMI E-Solder® 3083 Electrically Conductive Adhesive
- A. Schulman POLYBATCH™ Yellow 26787V Concentrate Based In LDPE
Copyright © lookpolymers.com All Rights Reserved