Styron CALIBREâ„¢ 301-10 Polycarbonate Resin
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | Styron |
| Trade Name | CALIBRE™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styron CALIBREâ„¢ 301-10 Polycarbonate Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Overview: CALIBREâ„¢ 300-10 polycarbonate resins offer exceptional impact resistance, heat distortion resistance and optical clarity as well as high melt strength for blow molding and sheet applications. The CALIBREâ„¢ 300-10 series products are available in 4 additive packages: CALIBREâ„¢ 300: No mold release or UV Stabilizer. CALIBREâ„¢ 301: Mold release. CALIBREâ„¢ 302: UV stabilizer. CALIBREâ„¢ 303: Mold release and UV stabilizer.Applications:AppliancesStorage media housingsBusiness equipment Electrical components Lighting Transportation Houseware Recreation Packaging applications Govt. and Industry Standards:CSAUnderwriters Laboratory (UL) Information provided by Styron
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ISO 1183/B |
| Water Absorption | 0.32 % @Temperature 23.0 °C |
0.32 % @Temperature 73.4 °F |
Equilibrium, 50% RH; ISO 62 |
| 0.15 % @Temperature 23.0 °C, Time 86400 sec |
0.15 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ISO 294-4 |
| Melt Flow | 10 g/10 min @Load 1.20 kg, Temperature 300 °C |
10 g/10 min @Load 2.65 lb, Temperature 572 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 73 | 73 | ASTM D785 |
| Hardness, Rockwell R | 118 | 118 | ASTM D785 |
| Tensile Strength at Break | 71.0 MPa | 10300 psi | ISO 527-2/50 |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | ISO 527-2/50 |
| Elongation at Break | 150 % | 150 % | ISO 527-2/50 |
| Elongation at Yield | 6.0 % | 6.0 % | ISO 527-2/50 |
| Tensile Modulus | 2.30 GPa | 334 ksi | ISO 527-2/50 |
| Flexural Strength | 97.0 MPa | 14100 psi | 2.0 mm/min; ISO 178 |
| Flexural Modulus | 2.40 GPa | 348 ksi | 2.0 mm/min; ISO 178 |
| Izod Impact, Unnotched (ISO) | 90.0 kJ/m² @Temperature 23.0 °C |
42.8 ft-lb/in² @Temperature 73.4 °F |
ISO 180/A |
| Charpy Impact, Notched | 1.30 J/cm² @Temperature -30.0 °C |
6.19 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 3.50 J/cm² @Temperature 12.0 °C |
16.7 ft-lb/in² @Temperature 53.6 °F |
ISO 179/1eA | |
| Abrasion | 45 | 45 | [%] Taber; ISO 9352 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 70.0 µm/m-°C | 38.9 µin/in-°F | ISO 11359-2 |
| Hot Ball Pressure Test | 125 °C | 257 °F | IEC 60335-1 |
| Deflection Temperature at 0.46 MPa (66 psi) | 144 °C | 291 °F | Annealed; ISO 75-2/B |
| Deflection Temperature at 1.8 MPa (264 psi) | 125 °C | 257 °F | Unannealed; ISO 75-2/A |
| 141 °C | 286 °F | Annealed; ISO 75-2/A | |
| Vicat Softening Point | 149 °C | 300 °F | ISO 306/B50 |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0626 in |
|
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
||
| Oxygen Index | 26 % | 26 % | ISO 4289-2 |
| Glow Wire Test | 875 °C @Thickness 2.00 mm |
1610 °F @Thickness 0.0787 in |
IEC 60695-2-12 |
| 875 °C @Thickness 3.00 mm |
1610 °F @Thickness 0.118 in |
IEC 60695-2-12 | |
| 900 °C @Thickness 1.00 mm |
1650 °F @Thickness 0.0394 in |
IEC 60695-2-12 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Refractive Index | 1.586 | 1.586 | ASTM D542; ISO 489 |
| Haze | 1.0 % | 1.0 % | ASTM D1003 |
| Transmission, Visible | 89 % | 89 % | ASTM D1003 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Dielectric Constant | 3.0 @Frequency 60.0 Hz |
3.0 @Frequency 60.0 Hz |
IEC 60250 |
| 3.0 @Frequency 1.00e+6 Hz |
3.0 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| 3.0 @Frequency 100 Hz |
3.0 @Frequency 100 Hz |
IEC 60250 | |
| Dielectric Strength | 17.0 kV/mm | 432 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.0010 @Frequency 50.0 Hz |
0.0010 @Frequency 50.0 Hz |
ASTM D150 |
| 0.0020 @Frequency 1.00e+6 Hz |
0.0020 @Frequency 1.00e+6 Hz |
ASTM D150 | |
| Comparative Tracking Index | 250 V @Thickness 2.00 mm |
250 V @Thickness 0.0787 in |
Solution A; IEC 60112 |
| Hot Wire Ignition, HWI | 775 sec @Thickness 2.00 mm |
775 sec @Thickness 0.0787 in |
IEC 60695-2-13 |
| 775 sec @Thickness 3.00 mm |
775 sec @Thickness 0.118 in |
IEC 60695-2-13 | |
| 800 sec @Thickness 1.00 mm |
800 sec @Thickness 0.0394 in |
IEC 60695-2-13 |
Users viewing this material also viewed the following:
- PolyOne Edgetek® PS-15GF-25MN/000 Polybutylene Terephthalate (PBT), Glass/Mineral Filled (discontinued **)<
- PolyOne Edgetek® AS-20GF/000 Acrylonitrile Butadiene Styrene (ABS)
- Albis Plastics Cellulose Acetate Butyrate B932 (UV Inhibitor Added), 4% Plasticizer (discontinued **)
- A. Schulman POLYFORT™ FPP 1200X High Flow, Calcium Carbonate Fortified Homopolymer Polypropylene
- Hexcel® HexForce™ 1597 Fiber Glass Fabric
- Tra-Con Tra-Bond 716K02 Thixotropic Adhesive
- Chevron Phillips Marlex® HHM TR-418Q MDPE Hexene Copolymer
- Tra-Con Tra-Bond 2130 Medium Viscosity Epoxy Adhesive
- Gromax Evasin EV-3201V Ethylene-Vinyl Alcohol Copolymer
Copyright © lookpolymers.com All Rights Reserved