- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 141 °C
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 141 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 141 °C | 286 °F | ASTM D648 |
| Performance Polymers IPS II PPL-A1050 PEKK (Polyetherketoneketone) Branched Standard Grade Amber pellets; neat resinInformation provided by Infinite Polymer System II. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 141 °C | 286 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP LUBRICOMP DFL23 PC LNP* Lubricomp* DFL23 is a compound based on Polycarbonate resin containing 15% Glass Fiber and 10% PTFE. Added features include: Internally Lubricated. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 141 °C | 286 °F | ASTM D 648 |
| MRC Polymers NAXELL™ PC110-20G General Purpose Polycarbonate, Medium Viscosity, 20% Glass Fiber • Available in natural and custom colors• Can be UV Stabilized• Internal and external lubricants can be addedInformation provided by MRC Polymers Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 141 °C @Thickness 3.20 mm |
286 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP STAT-KON DE002 PC LNP* STAT-KON* DE002 is a Polycarbonate base resin containing 10% Carbon Fiber. Added feature of this grade is: Electrically Conductive. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 141 °C @Thickness 3.20 mm |
286 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP STAT-KON DE004ER PC LNP* STAT-KON* DE004ER is a compound based on Polycarbonate resin containing 20% Carbon Fiber. Added featuresof this material include: Electrically Conductive, Easy Molding, Mold Release. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 141 °C @Thickness 3.20 mm |
286 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP STAT-KON DEL33EC PC (Asia Pacific) LNP STAT-KON* DEL33EC is a compound based on Polycarbonate resin containing Carbon Fiber, PTFE. Added features of this material include: Clean Compounding System. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 141 °C | 285 °F | unannealed, .125in; ASTM D648 |
| Star Plastics PCGF20 Molding Grade PC with 20% Glass Information provided by Star Plastics, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 141 °C | 285 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® PP CO GF15 CC 15% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 15% Filler by WeightFeatures: CopolymerInformation provided by TP Composites, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 141 °C @Thickness 3.20 mm |
286 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP DF002 PC LNP THERMOCOMP* DF002 is a compound based on Polycarbonate resin containing 10% Glass Fiber. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 141 °C @Thickness 6.40 mm |
286 °F @Thickness 0.252 in |
ASTM D648 |
| Samsung Cheil Industries Infino® CF-3200HF PC, Glass Filled High Impact Information provided by Samsung Cheil Industries. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 141 °C | 286 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics NORYL HNA033 PPE+HIPS Noryl* HNA033 resin is an unfilled modified polyphenylene ether resin designed to withstand several cycles in an autoclave. This resin is suitable for multiple conversion routes and is available in.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 141 °C | 286 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics NORYL HNA033 PPE+HIPS (Asia Pacific) Noryl* HNA033 resin is an unfilled modified polyphenylene ether resin designed to withstand several cycles in an autoclave. This resin is suitable for multiple conversion routes and is available in.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 141 °C | 285 °F | Unannealed; ASTM D648 |
| Techmer ES Electrablend® ABS SS16 FR BK 16% Stainless Steel Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Stainless Steel Fiber, 16% Filler by WeightFeatures: Electromagnetic Shielding (EMI)Appearance: BlackInformation provided by TP Composi.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 141 °C @Thickness 3.20 mm |
286 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP STAT-KON DE006ER PC (Asia Pacific) LNP STAT-KON* DE006ER is a compound based on Polycarbonate resin containing Carbon Fiber. Added features of this material include: Easy Molding. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 141 °C | 286 °F | annealed; ASTM D648 |
| Styron CALIBREâ„¢ 303-10 Polycarbonate Information provided by DowThis product line was spun off from Dow Chemical to Styron in 2010. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 141 °C | 286 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP THERMOCOMP MF006SU PP LNP* THERMOCOMP* MF006SU is a compound based on Polypropylene containing 30% lass Fiber. Characteristics of this grade are: Heat Stabilized, Chemically Coupled, UV Stabilized. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 141 °C | 285 °F | unannealed; ASTM D648 |
| Styron EMERGEâ„¢ 4701-13 Polycarbonate EMERGEâ„¢ PC 4701-13 advanced resin is formulated with 10% glass fiber and a proprietary flame retardant package. It provides good ignition resistance, rigidity, dimension stability and heat res.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 141 °C | 286 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 3063UV-3120 Black, UV Stabilized Modified Polypropylene DescriptionPolyfort® FPP 3063UV-3120 is a black, UV stabilized, 30% chemically coupled, glass reinforced, high impact resistance, modified polypropylene. Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 141 °C | 285 °F | Unannealed; ASTM D648 |
| Chase Plastics CP Pryme® PC320R Polycarbonate, Recycled Content Features: Good mold releaseRecycled contentForm: PelletsInformation provided by Chase Plastics. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 141 °C | 285 °F | ASTM D648 |
| Westlake Plastics Zelux® CN-SS Polycarbonate (conductive) CN-SS is filled with small non-sloughing stainless steel fibers. Has high flexural strength and good thermal stability to 275F. The CN-SS material has excellent impact strength. Information provid.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 141 °C | 286 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 3063UV-3120 Black, UV Stabilized Modified Polypropylene DescriptionPolyfort® FPP 3063UV-3120 is a black, UV stabilized, 30% chemically coupled, glass reinforced, high impact resistance, modified polypropylene. Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 141 °C | 286 °F | ISO 75-2/AF |
| Addiplast Addilene PMD 50272 Flame Retardant Polypropylene Flame retardant, high rigidityInformation provided by Addiplast. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 141 °C | 286 °F | |
| BASF Luranyl® KR 2403 G6 Polyphenylene Ether + Styrene-Butadiene Blend, 30% Glass Fiber Reinforced General-purpose grade with 30% glass fiber for parts requiring especially good resistance to heat deformation.Applications: parts for hot-water contact, pump housings, fan blades.Data was collected .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 141 °C | 286 °F | ASTM D648 |
| Ashley Polymers Ashlene® 1503WO BK Polycarbonate A rigid flame retardant polycarbonate, UV stabilized in black for applications requiring superior dimensional stability and overall toughness.Data provided by the manufacturer |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 141 - 175 °C | 286 - 347 °F | Average value: 164 °C Grade Count:3 |
| Overview of materials for PEKK, Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "PEKK, Unreinforced". Each property range of values reported is minimum and maximum values of appropriate.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 141 °C | 286 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP LUBRICOMP DFL329 PC LNP LUBRICOMP* DFL329 is a compound based on Polycarbonate resin containing 10% Glass Fiber, 15% PTFE. Added features of this material include: Flame Retardant, Internally Lubricated. |
|||