SABIC Innovative Plastics LNP THERMOCOMP 9X04488 POLYPHENYLENESULFONE (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyphenylsulfone (PPSU) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP 9X04488 POLYPHENYLENESULFONE (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* 9X04488 is a compound based on POLYPHENYLENESULFONE resin containing Mineral.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.31 g/cc | 0.0473 lb/in³ | ASTM D792 |
| 1.31 g/cc | 0.0473 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.300 % | 0.300 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0090 - 0.011 cm/cm @Time 86400 sec |
0.0090 - 0.011 in/in @Time 24.0 hour |
ISO 294 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.012 cm/cm @Time 86400 sec |
0.010 - 0.012 in/in @Time 24.0 hour |
ASTM D955 |
| 0.010 - 0.012 cm/cm @Time 86400 sec |
0.010 - 0.012 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 59.0 MPa | 8560 psi | ASTM D638 |
| Tensile Strength, Yield | 69.0 MPa | 10000 psi | ISO 527 |
| 74.0 MPa | 10700 psi | ASTM D638 | |
| Elongation at Break | 19.2 % | 19.2 % | ASTM D638 |
| Elongation at Yield | 7.7 % | 7.7 % | ISO 527 |
| 8.2 % | 8.2 % | ASTM D638 | |
| Tensile Modulus | 2.12 GPa | 307 ksi | 1 mm/min; ISO 527 |
| 2.28 GPa | 331 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 71.0 MPa | 10300 psi | ISO 178 |
| 96.0 MPa | 13900 psi | ASTM D790 | |
| Flexural Modulus | 2.09 GPa | 303 ksi | ISO 178 |
| 2.46 GPa | 357 ksi | ASTM D790 | |
| Izod Impact, Notched | 3.63 J/cm | 6.80 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 25.63 J/cm | 48.02 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 14.0 kJ/m² | 6.66 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | NB | NB | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 51.0 J | 37.6 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 59.0 J | 43.5 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 53.3 µm/m-°C @Temperature -40.0 - 40.0 °C |
29.6 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 54.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
30.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 52.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
29.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 52.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
29.1 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 195 °C | 383 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 200 °C @Thickness 3.20 mm |
392 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycoloy® CY100FC PC+ABS
- Saint-Gobain COHRlastic® CF4420 High Heat Reinforced Solid Rubber
- Lubrizol ESTANE® 5702F3 Ester Based Thermoplastic Polyurethane (European Grade)
- Wanhua Chemical Wanthane® WHT-2198 Polycaprolactone Based TPU
- Dow Corning SYL-OFF® 294 COATING
- ChevronTexaco Delo® SAE 85W-140 Gear Lubricant ESI®
- DuPont Performance Polymers Delrin® 100KM NC000 Acetal (POM) (Unverified Data**)
- BASF Ultramid® 82335G HS BK 102 50% Glass Filled PA6 (Dry)
- Bhansali Engineering Abstron AP-78 EP ABS Electro Plating Applications
- Sumitomo Bakelite North America RX® 647 Fiberglass Reinforced Phenolic
Copyright © lookpolymers.com All Rights Reserved