Oxford Polymers 20GF 20% Glass Fiber Filled Polycarbonate for Injection Molding
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 20% Glass Filled |
| Manufacturer | Oxford Polymers |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Oxford Polymers 20GF 20% Glass Fiber Filled Polycarbonate for Injection Molding.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
20% Glass Fiber Filled Polycarbonate for Injection MoldingInformation provided by Oxford Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.35 g/cc | 1.35 g/cc | ASTM D792 |
| Filler Content | 20 % | 20 % | |
| Linear Mold Shrinkage | 0.0025 cm/cm | 0.0025 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 110 MPa | 16000 psi | ASTM D638 |
| Elongation at Break | 5.0 % | 5.0 % | ASTM D638 |
| Tensile Modulus | 5.93 GPa | 860 ksi | ASTM D638 |
| Flexural Strength | 131 MPa | 19000 psi | ASTM D790 |
| Flexural Modulus | 5.52 GPa | 800 ksi | ASTM D790 |
| Compressive Strength | 110 MPa | 16000 psi | ASTM D695 |
| Izod Impact, Notched | 1.12 J/cm @Temperature 23.0 °C |
2.10 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 149 °C | 300 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 146 °C | 295 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 293 °C | 560 °F | |
| Back Pressure | 103 MPa | 15000 psi | Mold pressure |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® EXL1493T PC Copolymer
- Techmer ES HiFill® PA6 GF10 TL10 10% Glass Filled
- Samyang Trirex® PC-3025U 12 MFI UV Stabilized Clear Polycarbonate
- SABIC Innovative Plastics LNP THERMOTUF PX06417 PA 6
- A. Schulman SCHULADUR® A GF15 15% Glass Fiber Reinforced PBT
- Eurotec® Tecopet® PT70 GR15 NL100 MB PET, 15% glass fiber reinforced, impact modified, heat stabilized, natural
- Buckeye Polymers BP RPP 1012 C Polypropylene, 10% Mineral Filled
- Arlon R33468A030 0.0305" (0.775 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- Samyang Triel® 5650 Thermoplastics Polyetherester Elastomer, General Extrusion
Copyright © lookpolymers.com All Rights Reserved