- Acrylonitrile Butadiene Styrene (ABS), Transparent, Molded
- Styrolution Terlux® 2802 TR Q434 Transparent MABS
Styrolution Terlux® 2802 TR Q434 Transparent MABS
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Transparent, Molded |
| Manufacturer | Styrolution |
| Trade Name | Terlux® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styrolution Terlux® 2802 TR Q434 Transparent MABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Terlux® 2802 TR Q434 is a new grade with enhanced toughness.Information provided by STYROLUTION, which is a joint venture between BASF and INEOS
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.08 g/cc | 0.0390 lb/in³ | ISO 1183 |
| Water Absorption | 0.70 % | 0.70 % | ISO 62 |
| Moisture Absorption at Equilibrium | 0.35 % | 0.35 % | 23°C/50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | |
| Melt Flow | 2.16 g/10 min @Load 10.0 kg, Temperature 220 °C |
2.16 g/10 min @Load 22.0 lb, Temperature 428 °F |
ISO 1133 |
| 18.36 g/10 min @Load 21.6 kg, Temperature 220 °C |
18.36 g/10 min @Load 47.6 lb, Temperature 428 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 84 | 84 | ISO 2039-2 |
| Ball Indentation Hardness | 70.0 MPa @Load 36.5 kg, Time 30.0 sec |
10200 psi @Load 80.5 lb, Time 0.00833 hour |
ISO 2039-1 |
| Tensile Strength, Yield | 48.0 MPa | 6960 psi | 50mm/min; ISO 527-1/-2 |
| Elongation at Break | 12 % | 12 % | Nominal; ISO 527-1/-2 |
| Elongation at Yield | 4.0 % | 4.0 % | 50mm/min; ISO 527-1/-2 |
| Tensile Modulus | 2.00 GPa | 290 ksi | ISO 527-1/-2 |
| Charpy Impact Unnotched | 12.0 J/cm² @Temperature -30.0 °C |
57.1 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| 18.0 J/cm² @Temperature 23.0 °C |
85.7 ft-lb/in² @Temperature 73.4 °F |
ISO 179 | |
| Charpy Impact, Notched | 0.200 J/cm² @Temperature -30.0 °C |
0.952 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| 1.00 J/cm² @Temperature 23.0 °C |
4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 80.0 - 110 µm/m-°C @Temperature 23.0 - 80.0 °C |
44.4 - 61.1 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-1/-2 |
| Maximum Service Temperature, Air | 75.0 °C | 167 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 94.0 °C | 201 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C | 194 °F | ISO 75 |
| Vicat Softening Point | 93.0 °C | 199 °F | VST/B/50; ISO 306 |
| 105 °C | 221 °F | VST/A/50; ISO 306 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Refractive Index | 1.54 | 1.54 | ISO 489 |
| Transmission, Visible | 90 % | 90 % | transparent; thickness not quantified |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | IEC 60093 |
| Dielectric Constant | 2.8 @Frequency 1.00e+6 Hz |
2.8 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 2.9 @Frequency 100 Hz |
2.9 @Frequency 100 Hz |
IEC 60250 | |
| Dielectric Strength | 34.0 kV/mm | 864 kV/in | K20/P50; IEC 60243-1 |
| Dissipation Factor | 0.014 @Frequency 1.00e+6 Hz |
0.014 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 0.016 @Frequency 100 Hz |
0.016 @Frequency 100 Hz |
IEC 60250 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 230 - 260 °C | 446 - 500 °F | Injection Molding |
| Mold Temperature | 50.0 - 80.0 °C | 122 - 176 °F | Injection Molding |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Transparent | |
| Commercial Status | Europe |
Users viewing this material also viewed the following:
- Ravago Manufacturing Americas Hybrid S470H Acrylonitrile Butadiene Styrene + PC Alloy
- Arlon R36798T017 0.017" (0.432 mm) Uncured Silicone Rubber with Laminated Tefzel® Substrate (discontinue
- Indium Corp. 99.9% InI3 Indium Triiodide
- SABIC Innovative Plastics Ultem 1010FV PEI (Asia Pacific)
- SABIC Innovative Plastics Valox® 312 PBT
- SABIC Innovative Plastics LNP Thermocomp RFZ349 PA 66 (Asia Pacific)
- SABIC Innovative Plastics LNP Thermocomp R1000HI620 PA 66 (Europe-Africa-Middle East)
- ExxonMobil Mobil Glygoyle 320
- Wellman Wellamid® GS40-60 42L-NBK1 40% Glass Sphere Reinforced Nylon 6
- Bapolene® 4012 Polypropylene, Extrusion Grade
Copyright © lookpolymers.com All Rights Reserved