SABIC Innovative Plastics Cycolac® EX39 ABS
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Cycolac® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Cycolac® EX39 ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Highest impact extrusion ABS for sheet and blow molding applications.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.03 g/cc | 1.03 g/cc | ASTM D792 |
| Viscosity | 1.52e+6 cP | 1.52e+6 cP | Melt Viscosity, 240°C, 100 sec-1; ASTM D3825 |
| Linear Mold Shrinkage, Flow | 0.0070 - 0.0090 cm/cm @Thickness 3.20 mm |
0.0070 - 0.0090 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Index of Compound | 4.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
4.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 28.0 MPa | 4060 psi | Type I, 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 35.0 MPa | 5080 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 108 % | 108 % | Type I, 5 mm/min; ASTM D638 |
| Elongation at Yield | 3.5 % | 3.5 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 1.68 GPa | 244 ksi | 5 mm/min; ASTM D638 |
| Flexural Yield Strength | 57.0 MPa | 8270 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 1.90 GPa | 276 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 4.64 J/cm | 8.69 ft-lb/in | ASTM D256 |
| 3.20 J/cm @Temperature -30.0 °C |
5.99 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Dart Drop, Total Energy | 39.0 J @Temperature 23.0 °C |
28.8 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 101 µm/m-°C @Temperature -40.0 - 40.0 °C |
56.1 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 117 µm/m-°C @Temperature -40.0 - 40.0 °C |
65.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 °C @Thickness 3.20 mm |
196 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 77.0 °C @Thickness 3.20 mm |
171 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Vicat Softening Point | 95.0 °C | 203 °F | Rate B/50; ASTM D1525 |
| UL RTI, Electrical | 60.0 °C | 140 °F | UL 746B |
| UL RTI, Mechanical with Impact | 60.0 °C | 140 °F | UL 746B |
| UL RTI, Mechanical without Impact | 60.0 °C | 140 °F | UL 746B |
| Flammability, UL94 | HB @Thickness 1.52 mm |
HB @Thickness 0.0598 in |
UL 94 |
Users viewing this material also viewed the following:
- LG Chemical Lupox® GP2300G PBT+GF30%
- Mi-Tech Metals CW70E 68 Tungsten/32 Copper PM Metal Composite
- Haysite HCR-125 Corrosion Resistant Vinyl Ester/Glass Sheet
- Solvay Specialty Polymers Solef® 11010 Polyvinylidene Fluoride (PVDF)
- Special Metals INCONEL® 601GC® Nickel Superalloy
- Chase Plastics CP Pryme® N100L (COND, 50% RH) Nylon 6, Internally Lubricated
- Zeon Chemicals Zetpol® 3310 Hydrogenated Nitrile Elastomomer
- CoorsTek PlasmaPure-UC™ 99.9% Alumina
- 3M XR8123 Double Coated Paper Tapes
- Ascend Performance Materials Vydyne® 50BWFS Nylon 66, General Purpose
Copyright © lookpolymers.com All Rights Reserved