Arlon 680-R3839R 0.084" (2.13 mm) Cured Silicone Coating with Silica-based Substrate

Category	Polymer , Thermoset , Silicone
Manufacturer	Arlon
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Arlon 680-R3839R 0.084" (2.13 mm) Cured Silicone Coating with Silica-based Substrate.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Design/Construction:Side 1: Cured Silicone Coating Substrate: Silica-basedSide 2: Cured Silicone Coating Rubber Application Advantages:Extremely low thermal conductivityThermally stableBondable to silicone rubber2-3 times thinner than competing silicone foamFlexible and light weight Energy savingsRecommended process method for particle free applications: Vacuum Bag Cure Cycle: 15 minutes @ 250°F under 15 psi-Oversized uncured silicone rubber to seal the exposed edgesProduct Use: Thermal insulationAppearance: Red silicone rubber on black fabricThis data represents typical values for the production material. The data should not be used to write, or in place of, material specifications.Information provided by Arlon, Silicone Technologies Division

Physical Properties	Metric	English	Comments
Thickness	50.8 microns	2.00 mil	Side 1; Arlon SQA-TMS-003
	50.8 microns	2.00 mil	Side 2; Arlon SQA-TMS-003
	2030 microns	80.0 mil	Substrate; Arlon SQA-TMS-003
	2130 microns	84.0 mil	Overall; Arlon SQA-TMS-003

Mechanical Properties	Metric	English	Comments
Peel Strength	>= 0.175 kN/m	>= 1.00 pli	to Arlon 51270R015, Bond Strength; Arlon SQA -TMS-011

Thermal Properties	Metric	English	Comments
Thermal Conductivity	0.0600 W/m-K @Temperature 200 °C	0.416 BTU-in/hr-ft²-°F @Temperature 392 °F	Arlon SQA-TMS-022
Maximum Service Temperature, Air	121 °C	250 °F
Minimum Service Temperature, Air	-7.61 °C	18.3 °F

Processing Properties	Metric	English	Comments
Cure Time	15.0 min @Pressure 0.103 MPa, Temperature 121 °C	0.250 hour @Pressure 15.0 psi, Temperature 250 °F	Recommended Cure Cycle
Shelf Life	60.0 Month @Temperature 21.1 °C	60.0 Month @Temperature 70.0 °F	From date of manufacture

Descriptive Properties	Value	Comments
Color	Red
Total Product Weight (oz/yd2)	16.7	Arlon SQA-TMS-025
Uncoated Fabric Break Strength	18 lb/in	Wrap Direction, Arlon SQA-TMS-026