Polyram RamOfin PPH308G6 Polypropylene, 30% Glass Fiber, Impact Modified
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Glass Reinforced, Impact Modified |
| Manufacturer | Polyram |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram RamOfin PPH308G6 Polypropylene, 30% Glass Fiber, Impact Modified.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
30% Glass fiber reinforced, heat stabilized, impact modified polypropylene for injection molding applications.Information provided by Polyram.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.11 g/cc | 0.0401 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0010 - 0.0040 cm/cm | 0.0010 - 0.0040 in/in | ISO 2577 |
| Melt Flow | 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
4.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 115 | 115 | |
| Tensile Strength, Yield | 95.0 MPa | 13800 psi | ISO 527 |
| Elongation at Break | 5.0 % | 5.0 % | ISO 527 |
| Tensile Modulus | 6.00 GPa | 870 ksi | ISO 527 |
| Flexural Strength | 115 MPa | 16700 psi | ISO 178 |
| Flexural Modulus | 5.90 GPa | 856 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 14.0 kJ/m² | 6.66 ft-lb/in² | ISO 180 |
| Charpy Impact Unnotched | 7.50 J/cm² | 35.7 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 165 °C | 329 °F | ISO 11357 |
| Maximum Service Temperature, Air | 110 °C | 230 °F | Continuous use |
| 140 °C | 284 °F | Short peaks operation | |
| Deflection Temperature at 0.46 MPa (66 psi) | 153 °C | 307 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 145 °C | 293 °F | ISO 75 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
|
| Flame Spread | 40 mm/min | 1.6 in/min | FMVSS302 |
Users viewing this material also viewed the following:
- PolyOne Edgetek® LCP-30CF/000 Liquid Crystal Polymer - 30% Carbon Fiber (discontinued **)
- Indium Corp. 1072 VOC-Free Wave Solder Flux Containing Rosin
- Lehmann & Voss LUVOCOM® 1/GF/30/TF/15/BK Polyamide 66, with glass fiber and PTFE
- A. Schulman POLYBLAK™ 4676 Black Color Concentrate, 50% Carbon Black Based In LLDPE
- Dow Corning 735 OIL RESISTANT SEALANT
- Clariant Renol 612-01L Nylon 612, Lubricated
- Braskem CP 204 Injection Molding Polypropylene
- Asia International Enterprise (Hong Kong) 60C4 Nylon 66
- Solvay TECHNYL® 1021ST PA6, Conditioned
- LyondellBasell Astryn 7523C Polypropylene Copolymer
Copyright © lookpolymers.com All Rights Reserved