Styrolution TerblendÂ® N NM-11 ABS/PA6 (Dry)

Category	Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS)/Nylon Blend , Nylon
Manufacturer	Styrolution
Trade Name	Terblend®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Styrolution TerblendÂ® N NM-11 ABS/PA6 (Dry).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Terblend N NM-11 is an ABS/PA6 blend combining very high impact strength, even at low temperatures, with an excellent processability and surface appearance.Information provided by STYROLUTION, which is a joint venture between BASF and INEOS.

Physical Properties	Metric	English	Comments
Density	1.07 g/cc	0.0387 lb/inÂ³	ISO 1183
Moisture Absorption at Equilibrium	1.3 %	1.3 %	23Â°C/50% R.H.; ISO 62
Melt Flow	18 g/10 min @Load 10.0 kg, Temperature 240 Â°C	18 g/10 min @Load 22.0 lb, Temperature 464 Â°F	ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	36.0 MPa	5220 psi	0.2 in/min; ASTM Test
Tensile Strength, Yield	43.0 MPa	6240 psi	50mm/min; ISO 527
	45.0 MPa	6530 psi	2 in/min; ASTM Test
	64.0 MPa @Temperature -40.0 Â°C	9280 psi @Temperature -40.0 Â°F	ISO Data
Elongation at Break	>= 50 %	>= 50 %	50mm/min, Nominal strain; ISO 527
	>= 50 %	>= 50 %	0.2 in/min; ASTM Test
Elongation at Yield	3.5 %	3.5 %	50mm/min; ISO 527
	4.8 % @Temperature -40.0 Â°C	4.8 % @Temperature -40.0 Â°F	ISO Data
Tensile Modulus	1.93 GPa	280 ksi	ASTM Test
	2.00 GPa	290 ksi	1mm/min; ISO 527
Flexural Strength	62.0 MPa	8990 psi	ASTM Test
Flexural Modulus	1.80 GPa	261 ksi	ISO Data
	1.80 GPa	261 ksi	ASTM Test
Izod Impact, Notched (ISO)	65.0 kJ/mÂ²	30.9 ft-lb/inÂ²	ISO Test
Charpy Impact Unnotched	NB	NB	ISO 179
	NB @Temperature -30.0 Â°C	NB @Temperature -22.0 Â°F	ISO 179
Charpy Impact, Notched	7.00 J/cmÂ²	33.3 ft-lb/inÂ²	ISO 179
	1.50 J/cmÂ² @Temperature -30.0 Â°C	7.14 ft-lb/inÂ² @Temperature -22.0 Â°F	ISO 179

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	100 Âµm/m-Â°C	55.6 Âµin/in-Â°F	ISO 11359
Deflection Temperature at 0.46 MPa (66 psi)	90.6 Â°C	195 Â°F	ASTM Test
	96.0 Â°C	205 Â°F	ISO 75
Deflection Temperature at 1.8 MPa (264 psi)	65.6 Â°C	150 Â°F	ASTM Test
	71.0 Â°C	160 Â°F	ISO 75
Vicat Softening Point	104 Â°C	219 Â°F	(50 Â°C/h / 50N) - B/50; ISO 306
Flammability, UL94	HB @Thickness 1.60 mm	HB @Thickness 0.0630 in
	HB @Thickness 3.20 mm	HB @Thickness 0.126 in

Electrical Properties	Metric	English	Comments
Volume Resistivity	>= 1.00e+13 ohm-cm	>= 1.00e+13 ohm-cm	IEC 60093
Surface Resistance	>= 1.00e+14 ohm	>= 1.00e+14 ohm	IEC 60093
Dielectric Constant	2.9 @Frequency 1.00e+6 Hz	2.9 @Frequency 1.00e+6 Hz	IEC 60250
	3.3 @Frequency 100 Hz	3.3 @Frequency 100 Hz	IEC 60250
Dielectric Strength	41.0 kV/mm	1040 kV/in	IEC 60243-1
Dissipation Factor	0.015 @Frequency 1.00e+6 Hz	0.015 @Frequency 1.00e+6 Hz	IEC 60250
Comparative Tracking Index	600 V	600 V	IEC 60112

Descriptive Properties	Value	Comments
Commercial Status	Active America
Primary Processing Technique	Injection Molding
UL.UL-C	Yes