Samsung Cheil Industries Infino® NH-1037 PC/ABS, Unreinforced FR
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Infino® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Infino® NH-1037 PC/ABS, Unreinforced FR.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.19 g/cc | 1.19 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 19 g/10 min @Load 10.0 kg, Temperature 220 °C |
19 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength at Break | 70.6 MPa | 10200 psi | 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 65.7 MPa | 9530 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 109 % | 109 % | 50 mm/min; ASTM D638 |
| Tensile Modulus | 2.35 GPa | 341 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 98.1 MPa | 14200 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 2.65 GPa | 384 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 1.86 J/cm @Thickness 6.35 mm |
3.49 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| 5.88 J/cm @Thickness 3.17 mm |
11.0 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 108 °C @Thickness 6.40 mm |
226 °F @Thickness 0.252 in |
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C @Thickness 6.40 mm |
212 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 112 °C | 234 °F | B/50; ISO R306 |
| 114 °C | 237 °F | B/120; ISO R306 | |
| Flammability, UL94 | V-0 @Thickness >=1.50 mm |
V-0 @Thickness >=0.0591 in |
Users viewing this material also viewed the following:
- Pyrotek TS-107 Thermoset Electrical Insulation Product (Nema Grade: G-7)
- Magyar Aluminum ALOLT 59AF Aluminum Hydroxide
- H.C. Starck Amperit® 151.065 Tantalum (Ta)
- Karina 851D48/1-A-IS-LMP Black PVC Compound
- SABIC Innovative Plastics LNP STAT-KON RE007 PA 66
- DuPont Teijin Films Melinex® 339 Polyester Film, 300 Gauge
- Aclo Accutech Polypropylene Copolymer CP0437M20CL Mica Reinforced Coupled
- BASF Diisopropanolamine 90% Solution
- BASF Neopolen® P 9035 0.04 g/cc Core density; Expanded Polypropylene (Europe)
Copyright © lookpolymers.com All Rights Reserved