Styrolution PS 495N HIPS
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Impact Modified |
| Manufacturer | Styrolution |
| Trade Name | PS |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styrolution PS 495N HIPS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Styrolution PS 495N is an impact resistant polystyrene with a good balance of toughness, high flow, heat resistance and high gloss.High flowGood balance of toughness and heat resistanceUL 94 HBInformation provided by Styrolution
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | <= 0.10 % @Temperature 23.0 °C |
<= 0.10 % @Temperature 73.4 °F |
50% RH; ISO 62 |
| Water Absorption at Saturation | <= 0.10 % @Temperature 23.0 °C |
<= 0.10 % @Temperature 73.4 °F |
ISO 62 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ISO 294-4 |
| Melt Flow | 9.5 g/10 min @Load 5.00 kg, Temperature 200 °C |
9.5 g/10 min @Load 11.0 lb, Temperature 392 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 74.0 MPa | 10700 psi | ISO 2039-1 |
| Tensile Strength, Yield | 26.0 MPa | 3770 psi | ISO 527 |
| Elongation at Break | 40 % | 40 % | ISO 527 |
| Elongation at Yield | 1.5 % | 1.5 % | ISO 527 |
| Tensile Modulus | 2.00 GPa | 290 ksi | ISO 527 |
| Flexural Strength | 40.0 MPa | 5800 psi | ISO 178 |
| Flexural Modulus | 2.10 GPa | 305 ksi | ISO 178 |
| Charpy Impact Unnotched | 1.70 J/cm² | 8.09 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 80.0 µm/m-°C | 44.4 µin/in-°F | ISO 11359 |
| Thermal Conductivity | 0.170 W/m-K | 1.18 BTU-in/hr-ft²-°F | DIN 52612-1 |
| Deflection Temperature at 0.46 MPa (66 psi) | 89.0 °C | 192 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | ISO 75 |
| Vicat Softening Point | 89.0 °C @Load 5.10 kg |
192 °F @Load 11.2 lb |
120°C/h; ASTM D 1525 |
| 98.0 °C @Load 1.02 kg |
208 °F @Load 2.25 lb |
50°C/h; ISO 306 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+18 ohm-cm | >= 1.00e+18 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+13 ohm | >= 1.00e+13 ohm | IEC 60093 |
| Dielectric Constant | 2.5 @Frequency 100 Hz |
2.5 @Frequency 100 Hz |
IEC 60250 |
| Dissipation Factor | 0.00040 @Frequency 100 Hz |
0.00040 @Frequency 100 Hz |
IEC 60250 |
| 0.00040 @Frequency 1.00e+6 Hz |
0.00040 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 180 - 260 °C | 356 - 500 °F | ISO 294 |
| Injection Velocity | 200 mm/sec | 7.87 in/sec | ISO 294 |
Users viewing this material also viewed the following:
- Plastcom SLOVALEN PC 51 C 40 LS/1M Polypropylene reinforced with mineral filler, UV stabilized
- Cheng Yu Plastic PP225 Flame Retardant Polypropylene, Medium Impact
- Ensinger Tecatron® XP-83 Compression Molded PPS Compound, Filled with 10% PTFE, 10% Graphite and 15% Carbon Fiber
- Bapolene® PP5062 Polypropylene, Injection Grade
- Akzo Nobel Expancel® 930 DU 120 Dry unexpanded microspheres
- 3M FM012 Indoor UL Recognized Clear Polyester Overlaminate Label Product
- 3M FM065 Indoor UL Recognized Brite Silver Polyester Label Products
- 3M FM502 Bright Silver Polyester Label Product
- Axiall 8740 Moldings & Extrusions Flexible PVC
Copyright © lookpolymers.com All Rights Reserved