Industeel VIRGO 17.4PH 17Cr-4Ni-3Cu Precipitation Hardening Martensitic Stainless Steel (496°C - 4 hours + air cooled)
| Category | Metal , Ferrous Metal , Martensitic , Stainless Steel , Precipitation Hardening Stainless , T S10000 Series Stainless Steel |
| Manufacturer | Groupe Arcelor |
| Trade Name | VIRGO |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Industeel VIRGO 17.4PH 17Cr-4Ni-3Cu Precipitation Hardening Martensitic Stainless Steel (496°C - 4 hours + air cooled).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Alloy VIRGO 17.4 PH is a precipitation hardening martensitic stainless steel with Cu and Nb/Cb additions. The grade combines high strength, hardness (up to 300°C / 572°F) and corrosion resistance. Mechanical properties can be optimized with heat treatment. Very high yield strength up to 1100-1300 MPa can be achieved. The grade should not be used at temperatures above 300°C (572°F) or at very low temperatures. It has adequate resistance to atmospheric corrosion or in diluted acids or salts where its corrosion resistance is equivalent to CLC 18.9 (304) or SOLEIL B4 (430). If there are potential risks of stress corrosion cracking, higher aging temperatures must be selected over 550°C (1022°F), preferably 590°C(1094°F). The main applications are :mechanical componentsaerospaceoffshore industryfood industryInformation provided by manufacturer.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 7.80 g/cc | 0.282 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Brinell | 375 | 375 | Typical |
| Hardness, Rockwell C | 38 | 38 | Typical |
| Tensile Strength, Ultimate | >= 1170 MPa | >= 170000 psi | Minimum Guaranteed |
| 1310 MPa | 190000 psi | Typical | |
| Tensile Strength, Yield | >= 1070 MPa @Strain 0.200 % |
>= 155000 psi @Strain 0.200 % |
|
| 1207 MPa @Strain 0.200 % |
175100 psi @Strain 0.200 % |
Typical | |
| Elongation at Break | >= 8.0 % | >= 8.0 % | |
| 14 % | 14 % | Typical |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Carbon, C | 0.040 % | 0.040 % | |
| Chromium, Cr | 16.5 % | 16.5 % | |
| Copper, Cu | 3.3 % | 3.3 % | |
| Iron, Fe | 74.66 % | 74.66 % | As remainder |
| Manganese, Mn | 0.70 % | 0.70 % | |
| Nickel, Ni | 4.5 % | 4.5 % | |
| Niobium, Nb (Columbium, Cb) | 0.30 % | 0.30 % |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycoloy® C2100 PC+ABS (Asia Pacific)
- Iran Petrochemical (PCC) LL 18XF5 N Linear Low Density Polyethylene
- Sharadaa Ceramics Sharada RFC-80 Gel Bonded Castables
- Stir SpA CT 60 ATC (PVC)
- Shandong Dongyue Shenzhou New Material Co CHF115 Perfluorosulfonic Acid Ion-Exchange Resin (PFSA)
- A. Schulman POLYBATCH™ Green P30244/4 Concentrate Based In Copolymer PP
- Bulk Molding Compounds BMC 665 Mineral filled, 20% glass reinforced polyester molding compound
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 330ºF Cure Temperature
- Solvay Engineered Polymers DEXFLEX® 826HS TPO (discontinued **)
- Polyplastics Duracon® CH-15 Acetal Co-polymer (POM), Conductive, CF reinforced, Wear resistance
Copyright © lookpolymers.com All Rights Reserved