Styrolution PS 156F GPPS
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Heat Resistant Grade |
| Manufacturer | Styrolution |
| Trade Name | PS |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styrolution PS 156F GPPS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Styrolution PS 156F is a general purpose polystyrene grade with excellent flow properties, high heat resistance and is zinc stearate free.Free of internal lubricantsHigh heat resistanceExcellent flow propertiesInformation provided by Styrolution
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | <= 0.10 % @Temperature 23.0 °C |
<= 0.10 % @Temperature 73.4 °F |
50% RH; ISO 62 |
| Water Absorption at Saturation | <= 0.10 % @Temperature 23.0 °C |
<= 0.10 % @Temperature 73.4 °F |
ISO 62 |
| Linear Mold Shrinkage | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | ISO 294-4 |
| Melt Flow | 28 g/10 min @Load 5.00 kg, Temperature 200 °C |
28 g/10 min @Load 11.0 lb, Temperature 392 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 150 MPa | 21800 psi | ISO 2039-1 |
| Tensile Strength, Yield | 40.0 MPa | 5800 psi | ISO 527 |
| Elongation at Break | 1.5 % | 1.5 % | ISO 527 |
| Tensile Modulus | 3.20 GPa | 464 ksi | ISO 527 |
| Flexural Strength | 50.0 MPa | 7250 psi | ISO 178 |
| Charpy Impact Unnotched | 0.500 J/cm² | 2.38 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 80.0 µm/m-°C | 44.4 µin/in-°F | ISO 11359 |
| Thermal Conductivity | 0.160 W/m-K | 1.11 BTU-in/hr-ft²-°F | DIN 52612-1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C | 194 °F | ISO 75 |
| Vicat Softening Point | 101 °C @Load 5.10 kg |
214 °F @Load 11.2 lb |
120°C/h; ASTM D 1525 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+18 ohm-cm | >= 1.00e+18 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+13 ohm | >= 1.00e+13 ohm | IEC 60093 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 180 - 280 °C | 356 - 536 °F | ISO 294 |
Users viewing this material also viewed the following:
- MV Labs IR470 [(C6H5O3P]2Ir(CO)Cl Carbonylchlorobis(triphenylphosphine) iridium(I)
- Polymax® Maxelast® P3850H TPE, PP Overmold or Standalone use
- Braskem BS 002J HDPE Blow Molding Polyethylene (discontinued **)
- LG Chemical LUTENE XL8080UC PE Compound
- Sharadaa Ceramics REFCAST LC95 Low Cement Castables
- Polyram PlusTek PA7800G33 Nylon 6.6 for Injection Molding, 33% Glass Fiber Reinforced, Heat Stabilized, Impact Modified
- Polyplastics Duranex® 3200 Polybutylene Terephthalate (PBT), Standard, 20% GF filled
- BIW ASTM Class 2D2 Silicone Foam
- Silberline Sparkle Silvet® 880-20-E
Copyright © lookpolymers.com All Rights Reserved