- SABIC Innovative Plastics LNP LUBRICOMP EFL36 PEI
SABIC Innovative Plastics LNP LUBRICOMP EFL36 PEI
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP EFL36 PEI.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP LUBRICOMP* EFL36 is a compound based on Polyetherimide resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Internally Lubricated.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.62 g/cc | 0.0585 lb/in³ | ASTM D792 |
| 1.62 g/cc | 0.0585 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.150 % | 0.150 % | 50% RH, 24 hrs; ASTM D570 |
| 0.220 % | 0.220 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Time 86400 sec |
0.0010 - 0.0030 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0021 - 0.0024 cm/cm @Time 86400 sec |
0.0021 - 0.0024 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0035 - 0.0047 cm/cm @Time 86400 sec |
0.0035 - 0.0047 in/in @Time 24.0 hour |
ISO 294 |
| 0.0040 - 0.0060 cm/cm @Time 86400 sec |
0.0040 - 0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 168 MPa | 24400 psi | ISO 527 |
| 175 MPa | 25400 psi | ASTM D638 | |
| Elongation at Break | 2.0 % | 2.0 % | ASTM D638 |
| 2.0 % | 2.0 % | ISO 527 | |
| Tensile Modulus | 11.18 GPa | 1622 ksi | 1 mm/min; ISO 527 |
| 12.68 GPa | 1839 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 248 MPa | 36000 psi | ISO 178 |
| 252 MPa | 36500 psi | ASTM D790 | |
| Flexural Modulus | 11.3 GPa | 1640 ksi | ASTM D790 |
| 11.39 GPa | 1652 ksi | ISO 178 | |
| Izod Impact, Notched | 1.22 J/cm | 2.29 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 7.10 J/cm | 13.3 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 13.0 kJ/m² | 6.19 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 46.0 kJ/m² | 21.9 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 10.0 J | 7.38 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.45 | 0.45 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.43 | 0.43 | ASTM D3702 Modified |
| K (wear) Factor | 70.5 x 10-8 mm³/N-M | 35.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 39.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
22.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 39.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
22.1 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 27.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
15.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 28.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
15.8 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 204 °C | 399 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 202 °C @Thickness 3.20 mm |
396 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Precision Polymer Engineering Q75B Polyurethane Rubber
- Nilit FRIANYL B63 HS-GV 5 Nylon 6 for injection molding, 5% glass fiber reinforced
- Kraton® FG1924 G (SEBS) Linear Block Copolymer
- SABIC Innovative Plastics LNP LUBRICOMP KL001 Acetal Copolymer
- Solvay ALKAMULS® SC 242 Surfactant
- Eastman Eastman Embrace Copolyester for Shrink Film
- ATG s.r.l. NBR Nitrile-Butadiene Rubber
- ACC QM 2125 QSI Quantum Silicones 25 Durometer Condensation Cure Moldmaking Material
- Goodfellow Chromium 70/Titanium 30 Alloy
Copyright © lookpolymers.com All Rights Reserved